Erosion-resistant fused zirconium corundum brick for glass furnace and preparation method thereof

A glass kiln and zirconium corundum brick technology, applied in the field of refractory materials, can solve the problems of difficult industrialization, hindering material movement, and extremely high equipment requirements, and achieve a reasonable internal crystal phase structure, prolong service life, and high corrosion resistance. Effect

Active Publication Date: 2022-03-01
江苏徐耐新材料科技股份有限公司
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process can effectively improve the uniformity of the material liquid components and avoid material streaks. However, in the melting process, the raw material needs to be heated by microwave before entering the furnace body, and the detection temperature of microwave heating is the surface temperature of the material, and there are some high-temperature places inside. There may be a liquid phase, and components with low melting points are easy to liquefy, and the liquid phase agglomeration hinders the movement of materials, and may also adhere to equipment, making production extremely demanding on equipment, making it difficult to implement industrialization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Erosion-resistant fused zirconium corundum brick for glass furnace and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] An erosion-resistant fused zirconia corundum brick for a glass furnace, comprising the following components in mass percentage: 43.0% zircon sand, 51.0% alumina powder, 1.4% soda ash, 3.8% zirconia, 0.2% rare earth, andalusite powder 0.2%, hydroxypropyl methylcellulose 0.4%.

[0033] Its preparation method steps are as follows:

[0034]S1: Use computer 3D modeling sub-drawings to issue product mold drawings. The model workshop uses a foam cutting machine to make models according to the drawings, and the sand mold workshop makes sand molds through model sanding; sand molds use self-hardening sand technology to make reasonable blank processing. The casting workshop puts the sand mold into a special insulation box, fills it with hollow silicon-aluminum ball insulation material, and then uses a vibrator to vibrate the insulation material and wait for casting;

[0035] S2: After mixing zircon sand, alumina powder, zirconia, soda ash, and hydroxypropyl methylcellulose throug...

Embodiment 2

[0044] An erosion-resistant fused zirconia corundum brick for a glass furnace, comprising the following components in mass percentage: 41.0% zircon sand, 48% alumina powder, 2.0% soda ash, 5.9% zirconia, 0.7% rare earth, andalusite powder 0.8%, hydroxypropyl methylcellulose 1.6%.

[0045] Its preparation method steps are as follows:

[0046] S1: Use computer 3D modeling sub-drawings to issue product mold drawings. The model workshop uses a foam cutting machine to make models according to the drawings, and the sand mold workshop makes sand molds through model sanding; sand molds use self-hardening sand technology to make reasonable blank processing. The casting workshop puts the sand mold into a special insulation box, fills it with hollow silicon-aluminum ball insulation material, and then uses a vibrator to vibrate the insulation material and wait for casting;

[0047] S2: After mixing zircon sand, alumina powder, zirconia, soda ash, and hydroxypropyl methylcellulose through...

Embodiment 3

[0056] An erosion-resistant fused zirconia corundum brick for a glass furnace, which consists of the following components in mass percentage: 41.9% zircon sand, 49.4% alumina powder, 2.0% soda ash, 4.6% zirconia, 0.4% rare earth, andalusite Powder 0.6%, hydroxypropyl methylcellulose 1.1%.

[0057] Its preparation method steps are as follows:

[0058] S1: Use computer 3D modeling sub-drawings to issue product mold drawings. The model workshop uses a foam cutting machine to make models according to the drawings, and the sand mold workshop makes sand molds through model sanding; sand molds use self-hardening sand technology to make reasonable blank processing. The casting workshop puts the sand mold into a special insulation box, fills it with hollow silicon-aluminum ball insulation material, and then uses a vibrator to vibrate the insulation material and wait for casting;

[0059] S2: After mixing zircon sand, alumina powder, zirconia, soda ash, and hydroxypropyl methylcellulos...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
porosityaaaaaaaaaa
Login to view more

Abstract

The object of the present invention is to provide an erosion-resistant fused zirconia corundum brick for glass furnaces and a preparation method thereof. The fused zirconia corundum brick provided by the present invention includes the following components in mass percentage: zircon sand 41.0-43.0%, Alumina powder 48.0‑51.0%, soda ash 1.4‑2.0%, zirconia 3.80‑5.90%, rare earth 0.2‑0.7%, andalusite powder 0.2‑0.8%, hydroxypropyl methylcellulose 0.4‑1.6%. By improving product formula and process technology, the 33% # The content of silicon and sodium in fused zirconia corundum bricks can reduce the content of glass phase in the product, optimize the crystal phase structure of the product, improve the corrosion resistance of the product in the use of glass furnaces, significantly prolong the service life and reduce the precipitation of glass phase In contrast, to a certain extent, the pollution of the product to the glass liquid in the glass furnace is reduced, and the service life of the glass furnace and the quality of glass products are significantly improved.

Description

technical field [0001] The invention belongs to the technical field of refractory materials, and in particular relates to an erosion-resistant fused zirconia corundum brick for a glass kiln and a preparation method thereof. Background technique [0002] Fused zirconia corundum bricks are mainly used in glass furnaces. They have good resistance to glass liquid erosion, rapid cooling and rapid heating, and high thermal load performance. They are used in various important parts of melting furnaces. The excellent corrosion and erosion resistance of the bricks is due to their mineral composition and microstructure. However, with the upgrading of glass enterprises, the quality requirements for fused zirconia corundum bricks are more stringent, and the quality defects of fused zirconia corundum bricks will directly affect the quality of glass products and the service life of glass furnaces. [0003] Existing 33 # Fused zirconia corundum bricks are mainly used in the pool wall of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66C04B35/10C03B5/43
CPCC04B35/66C04B35/10C03B5/43C04B2235/3248C04B2235/3201C04B2235/3244C04B2235/3224C04B2235/3463C04B2235/656C04B2235/6567C04B2235/66C04B2235/77
Inventor 张雪沈超群
Owner 江苏徐耐新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap