Deposition device for densification of prefabricated body and charging structure

Abstract

The invention relates to the technical field of chemical vapor infiltration of carbon-carbon composite materials, and discloses a deposition device for densification of a preform and a charging structure. A flow limiting channel is formed between the preform to be densified and the side wall of an inner flow limiting cylinder, and an overflowing opening is formed in the top of the preform to be densified; and a flow limiting path which sequentially leads to the flow limiting channel, the overflowing opening and the furnace cavity outlet from the furnace cavity inlet is formed in the furnace cavity. In the deposition process, the temperature of a thermal field in a furnace chamber is gradually reduced from outside to inside, the deposition speed is increased exponentially along with temperature increase, carbon source gas permeates from the inner surface to the outer side with the high temperature for deposition densification, the temperature in the prefabricated body to be densified is continuously increased, and the deposition surface is continuously pushed inwards during deposition; and the whole to-be-densified prefabricated body is completely deposited, so that the surface crusting of the to-be-densified prefabricated body is avoided, and the densification density of the to-be-densified prefabricated body is uniform. In addition, through the flow limiting path, the carbon source gas activity space can be effectively compressed, the active group collision probability is increased, and therefore the deposition efficiency is greatly improved.

Description

technical field

[0001] The invention generally relates to the technical field of chemical vapor infiltration of carbon-carbon composite materials, and in particular relates to a deposition device and a furnace loading structure for densification of preforms. Background technique

[0002] Carbon-carbon composite materials, that is, composite materials composed of carbon fiber reinforced carbon matrix, not only have good structural properties such as high specific strength, but also have excellent functional properties such as heat resistance, thermal insulation, adsorption, superconductivity, wear resistance, etc. At present, the preparation of carbon-carbon composite materials at home and abroad generally adopts the chemical vapor infiltration process (CVI). The pyrolytic carbon is obtained by deposition, so that the carbon fiber preform is continuously densified, and finally a carbon-carbon product with the desired density is obtained. Although this process can avoid damag...

Images