Valve controlled lead acid accumulator positive lead paste
A technology of lead-acid battery and positive electrode paste, which is applied in the direction of lead-acid battery electrodes, lead-acid batteries, battery electrodes, etc., which can solve the problems of easy injury to personnel, uneven lead paste, and short battery cycle life, so as to avoid personnel injury , prolong the life of deep cycle and prolong the service life of equipment
Inactive Publication Date: 2006-11-22
ZHEJIANG NARADA POWER SOURCE CO LTD
View PDF0 Cites 4 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0006] The invention mainly solves the problem of short cycle life of batteries with traditional lead paste formulations, and at the same time solves the problems of corrosive equipment, easily injured personnel and uneven lead paste caused by adding sulfuric acid to the traditional lead paste formula. Therefore, the valve of the present invention is provided. Positive lead paste for lead-acid batteries
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0030] Wherein the short fiber is polyacrylonitrile material.
[0031] The preparation process of lead paste:
[0032] 1. Add the short fiber into the water and stir to disperse the short fiber evenly;
[0033] 2. Add lead powder and stir to make it even.
[0034] The role of each component:
[0035] 1. Lead powder is used as the positive electrode active material to give the battery capacity;
[0036] 2. The short fibers are used as the skeleton for the bonding of active substances.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
![No PUM](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
This invention relates to a value controlled lead acid battery positive lead paste prolonging the working life of batteries and devices since it can avoid corrosion to the devices, harm to human bodies or non-uniform mixing which is composed of the components in following weigh percentage taking its weight as the primary standard: short fiber: 0.08-0.5%, water: 5-20% and lead powder for rest.
Description
technical field [0001] The invention relates to a lead-acid accumulator pole plate, especially a lead paste layer on a positive pole plate. Background technique [0002] Valve-regulated lead-acid batteries have been widely used in the fields of backup power, energy storage and power supply. However, the fatal problem of lead-acid batteries at present is mainly the short cycle life of the batteries. The positive active material is the key to restricting this problem. The earliest positive active material used two lead plates as electrodes for repeated charge and discharge, and the lead plates were transformed during the charge and discharge process. It can be said that the positive active material at that time was pure lead. Later, people in the industry used active materials to cover the grid to make battery plates, such as Faure using Pb 3 o 4 As the active material, the lead paste is applied to the lead sheet to make a pole plate. The U.S. patent "...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/14H01M4/62H01M4/56H01M4/38H01M10/06
CPCH01M4/14H01M4/56H01M4/627H01M10/121Y02E60/10
Inventor 包有富王瑜
Owner ZHEJIANG NARADA POWER SOURCE CO LTD
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap