Superfine crystal particle hot-rolling steel plate with thick specification and production thereof

A technology of ultra-fine grain and hot-rolled steel plates, applied in metal rolling and other directions, can solve the problems of difficult process control, high price of alloy elements, high price, etc., and achieve the effect of good comprehensive performance, good cold bending performance and low cost

Inactive Publication Date: 2005-05-11
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF0 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the relatively high price of alloying elements, the price

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0009] Example 1:

[0010] Q235 plain carbon steel is smelted by a converter, and the weight percentage of the chemical composition of the steel includes: C: 0.13%, Si: 0.22%, Mn: 0.52%, P: 0.018%, S: 0.010%. The steel is cast into 200×(800~1200)×5500mm continuous casting slabs by conventional continuous casting methods, and the slabs are sent to the 1450mm hot continuous rolling mill for rolling. The heating, rolling and cooling are controlled in the whole process. The rolling process control is as follows:

[0011] a. Control the heating temperature of the continuous casting slab to 1180℃; b. The slab is rough-rolled at 970℃, and the rough rolling adopts six-pass rolling; c. The thickness of the intermediate slab after rough rolling is 31mm; d. Hot-rolled finish rolling The inlet temperature is 890℃; e. The finishing rolling adopts six stands for rolling; f. The cooling water is put into the three sets of stands; g. The exit temperature of the hot rolling finishing rolling is 81...

Example Embodiment

[0013] Example 2:

[0014] Q235 carbon steel is smelted by a converter, and the weight percentage of the chemical composition of the steel includes: C: 0.15%, Si: 0.25%, Mn: 0.61%, P: 0.015%, S: 0.008%. The steel is cast into 200×(800~1200)×5500mm continuous casting slabs by conventional continuous casting methods, and the slabs are sent to the 1450mm hot continuous rolling mill for rolling. The heating, rolling and cooling are controlled in the whole process. The rolling process control is as follows:

[0015] a. Control the heating temperature of the continuous casting slab to 1200℃; b. The slab is rough-rolled at 980℃; c. The thickness of the intermediate slab after rough rolling is 34.5mm; d. The hot-rolling finish-rolling entrance temperature is 910℃; e , Finish rolling adopts five stands for rolling; f. Put cooling water between the four sets of stands; g. The exit temperature of the hot rolling finishing rolling is 830℃; h, the coiling temperature is 520℃.

[0016] The thic...

Example Embodiment

[0017] Example 3:

[0018] Q235 plain carbon steel is smelted by a converter, and the weight percentage of the chemical composition of the steel includes: C: 0.17%, Si: 0.25%, Mn: 0.68%, P: 0.015%, S: 0.009%. The steel is cast into 200×(800~1200)×5500mm continuous casting slabs by conventional continuous casting methods, and the slabs are sent to the 1450mm hot continuous rolling mill for rolling, and the whole process of heating, rolling and cooling is controlled. The hot rolling process control is as follows:

[0019] a. Control the heating temperature of the continuous casting slab to 1200℃; b. The slab is rough-rolled at 980℃; c. The thickness of the intermediate slab after rough rolling is 35.5mm; d. The hot-rolling finish-rolling entrance temperature is 920℃; e , Finish rolling adopts five stands for rolling; f. Put cooling water between the four sets of stands; g. The exit temperature of hot rolling finishing rolling is 830℃; h, the coiling temperature is 500℃.

[0020] The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention was involved in the preparation method of thick hot rolled steel plate with ultra-fine grain. The alloy consist of 0.13-0.18%C, 0.12-0.30% Si, 0.50-0.70%Mn, is less than or equal to 0.020% P and is less than or equal to 0.015%S. The technology included the following steps: a) the heating-up temperature of continuous cast ingot was 1150-1200deg.C. b) The temperature of coarse crushing was 950-1000deg.C. c) The thickness of intermediate ingot after coarse crushing was 30-35mm. d) Inlet temperature of fine rolling was 880-920deg.C. e) Five or six groups frameworks were used in the rolling process of fine rolling. f) Three or four groups cooling water were input among the frameworks. g) Outlet temperature of fine rolling was 800-830deg.C. h) The reel temperature was 500-560deg.C. Chemical constitution of the hot rolling steel plate was simple and the cost was low. Ultra-fine grain hot rolling steel plate with 6.5-8.0mm thick was formed by controlling heating, coarse rolling and cooling. The steel plate had fine strength of extension, yield strength, extensibility and cold bending performance.

Description

technical field [0001] The invention relates to a steel plate and its production process, in particular to a thick gauge hot-rolled steel plate with ultrafine grains and its production process. Background technique [0002] For Q235 plain carbon steel, on the traditional hot rolling mill, the conventional rolling process is used for rolling, that is: the heating temperature is 1250°C, the rough rolling temperature is 970°C, the finish rolling entrance temperature is 950°C ~ 1000°C, and the exit temperature is 1000°C. The temperature is 850°C-920°C, the coiling temperature is 670°C-700°C, the mechanical properties of the produced steel plate are: yield strength ReL: 235MPa-300MPa, tensile strength Rm: 375MPa-500MPa. For a hot-rolled steel plate with a thicker thickness (eg, 6.5 mm to 8.0 mm in thickness), it is more difficult to increase the strength of the steel plate by using the conventional rolling process described above. In addition, in order to improve the strength of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21B1/22B21B1/46C21D8/02C22C38/04
Inventor 宋立秋左军佘广夫程兴德刘勇刘建华
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap