Reinforced osseous porcelain and process for producing same

A technology for strengthening porcelain and bone, applied in the field of bone-enhancing porcelain and its production technology, can solve the problems of high flexural strength, low flexural strength, and high cost, and achieve the effects of improving flexural strength and saving energy.

Inactive Publication Date: 2006-09-27
潮州市波士发陶瓷制作有限公司
View PDF0 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the bone china on the market has good light transmittance, but its flexural strength is low, and because the support point of the blank is lowered under high temperature and load, it is easy to soften and deform, so a second firing process (that is, a high temperatu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reinforced osseous porcelain and process for producing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A bone-reinforced porcelain comprising the following components (% by weight): Longyan washed mud 47.0, Hunan feldspar 14.0, Guizhou clay 6.5, α-alumina powder 22.5, and synthetic bone powder 10.0.

[0021] Described Longyan washing mud is following component (by weight %): SiO 2 60.00, Al 2 o 3 27.50 Fe 2 o 3 0.40, TiO 2 0.04, CaO 0.11, MgO 0.29, K 2 O 4.80, Na 2 O 0.33, IL 7.00.

[0022] Described Guizhou clay is following composition (by weight %): SiO 2 45.79, Al 2 o 3 38.79 Fe 2 o 3 0.17, TiO 2 0.06, CaO 0.46, MgO 0.02, K 2 O 0.02, Na 2 O 0.02, IL 14.00.

[0023] The particle size of the α-alumina powder is 3 μm.

[0024] The production technology of bone reinforced porcelain of the present invention is the following steps:

[0025] Billet and green body production: put Longyan mud washing, Hunan feldspar, Guizhou clay, α-alumina powder and synthetic bone powder into the ball mill according to the proportion, add water ball mill, sieve, iron ...

Embodiment 2

[0031] A bone-reinforced porcelain, comprising the following components (% by weight): 45% of Longyan washing mud, 15% of Hunan feldspar, 8% of Guizhou clay, 24% of α-alumina powder, and 8% of synthetic bone powder.

[0032] Described Longyan washing mud is following component (by weight %): SiO 2 56.00, Al 2 o 3 28.00, Fe 2 o 3 0.30, TiO 2 0.03, CaO 0.15, MgO 0.33, K 2 O 5.40, Na 2 O 0.36, IL 8.00.

[0033] Described Guizhou clay is following composition (by weight %): SiO 2 50.00, Al 2 o 3 35.00, Fe 2 o 3 0.14, TiO 2 0.05, CaO 0.40, MgO 0.01, K 2 O 0.03, Na 2 O 0.03, IL 14.50.

[0034] The particle size of the α-alumina powder is 4 μm.

[0035] The production technology of bone reinforced porcelain of the present invention is the following steps:

[0036] Billet and green body production: put Longyan mud washing, Hunan feldspar, Guizhou clay, α-alumina powder and synthetic bone powder into the ball mill according to the above ratio, add water to ball m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Flexural strengthaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a sclerotin intensification ceramic and manufacturing technique, which comprises the following elements: dragon rock wash mud, Hunan feldspar, Guizhou clay, alpha-alumina powder and synthetic bone meal. The manufacturing technique comprises the following steps: blanking; making blank body; preparing frit; making magentify step. The sclerotin intensification ceramic realizes the primary firing, which reduces the energy and improves the transverse strength.

Description

technical field [0001] The invention relates to a reinforced porcelain and its production process, in particular to a bone reinforced porcelain and its production process. Background technique [0002] At present, the bone china on the market has good light transmittance, but its flexural strength is low, and because the support point of the blank is lowered under high temperature and load, and it is easy to soften and deform, a second firing process must be adopted (that is, a high temperature biscuit firing process). , a low-temperature glaze firing), high energy consumption and high cost; and high-silicon reinforced porcelain, high-alumina reinforced porcelain, magnesium reinforced porcelain, etc., have high flexural strength, but poor light transmission. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies in the prior art and provide a bone-reinforced porcelain and its production process. The produced product not only...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/14C04B35/622
Inventor 吴波利柯为郁
Owner 潮州市波士发陶瓷制作有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap