Method for preparing fire-proof paint of trees during growth period

Abstract

The invention provides a preparation method of a fireproof coating for growth period tree. Ammonium polyphosphate 20, melamine 9, pentaerythritol 6, chlorinated paraffin 5, titanium dioxide 5, talcum powder 4, ethyl cellulose 0.6 solution and tap water 20 are mixed, dispersed and stirred for 60 minutes by a high-speed stirrer. The dispersed slurry is ground by a grinder, mixed with a water-based acrylic resin 30, stirred, filtered and tested. The invention has the following advantages that the invention does not influence normal growth of trees, prevents fire and protects forest resources when the woods catch fire.

Description

technical field [0001] The invention relates to a method for preparing a fireproof coating for trees during growth. Background technique [0002] At present, there are many varieties of fireproof coatings for wood structures, which are applied to building structures. However, it has not been found to be used for fire prevention of trees while they are growing. Contents of the invention [0003] The object of the present invention is to overcome above-mentioned defective, a kind of preparation method that is used for the fireproof coating of trees during growing period is provided. [0004] The technical scheme of the present invention is: a kind of preparation method that is used for the fireproof coating of trees during growing period, it is characterized in that: prepare according to following proportion by weight: polyphosphate amine 10-30, melamine 5-15, pentaerythritol 3-9 , paraffin wax 3-9, titanium dioxide / red iron oxide 3-10, talc powder 2-8, carboxyethyl cellul...

AI Technical Summary

Problems solved by technology

but not found to be used for fire protection of trees while they are growing