Technique for preparing echelon interpenetration polymer network damping material

A technology of interpenetrating polymers and damping materials, which is applied in the field of preparation technology of graded interpenetrating polymer network damping materials, can solve the problems that gradient interpenetrating polymer networks are difficult to realize industrialization, and achieve the purpose of broadening the effective damping temperature range, Easy to operate, increase the effect of energy consumption

Inactive Publication Date: 2008-08-13
HEILONGJIANG UNIV
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, this method of preparing gradient interpenetrating polymer networks is difficult to achieve industrialization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of preparation technology of graded interpenetrating polymer network damping material, it is finished through the following steps: first, the molar ratio of acetic anhydride by acetyl group and epoxy acrylate hydroxyl group in vinyl ester resin is 1: 1 ratio drop Add it to epoxy acrylate, the reaction temperature is 50°C, and the reaction time is 0.75 hours to prepare hydroxyl-sealed epoxy acrylate, and mix it with butyl methacrylate at a mass ratio of 2:1 to prepare modified vinyl ester resin; then, polyurethane and modified vinyl ester resin were solidified at room temperature by synchronous interpenetration process to prepare a single-layer polyurethane / modified vinyl ester resin interpenetrating polymer network damping material, and when the time interval between the two layers was 5 hours, respectively Injection molding is prepared into a graded polyurethane / modified vinyl ester resin interpenetrating polymer network damping material with three layers and a c...

Embodiment 2

[0017] A preparation process for a graded interpenetrating polymer network damping material, which is completed through the following steps: first, drop acetyl chloride in a ratio of 1.1:1 to the molar ratio of acetyl group to epoxy acrylate hydroxyl group in vinyl ester resin Add it to epoxy acrylate, the reaction temperature is 35°C, and the reaction time is 4 hours to prepare a hydroxyl group, and mix it with butyl methacrylate in a mass ratio of 2:1 to prepare a modified vinyl ester resin; then , Polyurethane and modified vinyl ester resin were solidified at room temperature through a synchronous interpenetrating process to prepare a single-layer polyurethane / modified vinyl ester resin interpenetrating polymer network damping material, which was injected separately when the time interval between the two layers was 5 hours. The number of layers is 3 layers, and the composition ratio of each layer is 6:4, 7:3, 8:2 graded polyurethane / modified vinyl ester resin interpenetratin...

Embodiment 3

[0019] A kind of preparation technology of graded interpenetrating polymer network damping material, it is finished through the following steps: first, the mol ratio of acetic anhydride or acetyl chloride is 1: 1 according to the molar ratio of acetyl group and epoxy acrylate hydroxyl group in vinyl ester resin Or 1.1:1 ratio is added dropwise in the epoxy acrylate, the reaction temperature is 50 ℃ or 35 ℃, and the reaction time is 0.75 hours or 4 hours, prepares hydroxyl-blocking epoxy acrylate and it and butyl methacrylate according to A mass ratio of 2:1 is mixed to prepare a modified vinyl ester resin; then, the polyurethane and the modified vinyl ester resin are cured at room temperature by a synchronous interpenetrating process to prepare a single-layer graded polyurethane / modified vinyl ester resin interpenetrating polymer The network damping material is injected separately when the time interval between the two layers is 7 hours, and prepared into a graded polyurethane / ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Preparation of gradient interpenetrating polymer networks damping material with wide temperature range, high damping, which can be used to reduce vibration and noise. The invention comprises firstly adding acetic anhydride or acetyl chloride into epoxy acrylate drop by drop according to a mole ratio of acetyl and epoxy acrylic hydroxyl 1:1-1.1:1, with reaction temperature from room temperature to 50 DEG C., and reaction time 0.75-4 hours, preparing hydroxy epoxy acrylate, mixing it with butyl methacrylate with a mass ratio of 2:1 to prepare modified vinyl ester resin; then solididying polyurethane and modified vinyl ester resin through simultaneous interpenetrating process to prepare single layer polyurethane / modified vinyl ester resin interpenetrating polymer networks damping material, molding at the two layer respectively with a time interval of 5-7 hours, so gradient interpenetrating polymer networks damping material of polyurethane / modified vinyl ester resin with a composition ratio of 5:5 - 8:2 is prepared.

Description

Technical field: [0001] The invention relates to a preparation process of a wide temperature range, high damping graded interpenetrating polymer network damping material. Background technique: [0002] Damping material refers to a class of materials that can lose energy during the process of undergoing vibration deformation. It can effectively reduce vibration and noise without changing the original design and structure of the equipment, especially has special effects on the control of broadband random vibration and noise, and is especially suitable for frame-based vibration and noise reduction. . High-performance damping materials require that the effective damping temperature range of the material (the temperature range where the damping factor tanδ>0.3) is 60°C to 80°C. In order to achieve effective vibration and noise reduction effects, it is necessary to start from two aspects at the same time. On the one hand, from the perspective of material design, the effective...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G81/02
Inventor秦川丽白续铎姜海健谭强
OwnerHEILONGJIANG UNIV