Multicomponent fiber blended fabric and preparation thereof

A multi-component fiber and blended fabric technology, applied in the fields of dyeing and finishing, and textile, can solve the problems of fiber weaving characteristics, coloring conditions are quite different, industrial production is limited, and level dyeing is poor, etc., and achieves excellent physical indicators. , the effect of maintaining good performance

Inactive Publication Date: 2008-10-01
SHANDONG WOYUAN NEWFASHIONED FABRIC
View PDF0 Cites 45 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because although its performance is much better than that of fabrics with two or three fiber combinations, due to the variety of fibers, the weaving characteristics and coloring conditions of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multicomponent fiber blended fabric and preparation thereof
  • Multicomponent fiber blended fabric and preparation thereof
  • Multicomponent fiber blended fabric and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0167] According to embodiment 1 technique, spinning raw material is:

[0168] Tencel 12% 38mm×1.5D

[0169] Ramie 12% 50mm×8D

[0170] Bamboo fiber 12% 38mm×1.5D

[0171] Polyester staple fiber 63.3% 48mm×0.8D

[0172] Conductive fiber 0.7% 38mm×3D

[0173] Fabric performance and index

[0174] 1. The fabric has good shape retention and stable size

[0175] Washing size change rate (shrinkage rate): radial: -0.6%; weft: -0.5%.

[0176] 2. Excellent and long-lasting antistatic performance

[0177] (1) Surface charge density: initial, 0.60μC / m 2 ; After 50 washes, 0.68μC / m 2 .

[0178] (2) Electrostatic half-life: initial, 0.3S; after washing 50 times, 0.3S.

[0179] 3. Good anti-pilling effect

[0180] Anti-pilling level 4.

[0181] 4. Good stiffness

[0182] Bending length: warp direction, 1.7cm; weft direction, 1.6cm.

[0183] 5. Excellent elastic performance

[0184] Crease recovery angle: initial, 310 degrees; after 15 washes, 265 degrees.

[0185] 6. High ...

Embodiment 3

[0193] According to embodiment 1 technique, spinning raw material is:

[0194] Tencel A100 18% 38mm×1.5D

[0195] Ramie 8% 50mm×8D

[0196] Bamboo Fiber 8.5% 38mm×1.5D

[0197] Polyester staple fiber 65% 48mm×0.8D

[0198] Conductive fiber 0.5% 38mm×3D

[0199] Fabric performance and index

[0200] 1. The fabric has good shape retention and stable size

[0201] Washing size change rate (shrinkage rate): radial: -0.8%; weft: -0.7%.

[0202] 2. Excellent and long-lasting antistatic performance

[0203] (1) Surface charge density: initial, 0.76μC / m 2 ;After 50 washes, 0.81μC / m 2 .

[0204] (2) Electrostatic half-life: Initially, 0.3S; after washing 50 times, 0.5S.

[0205] 3. Good anti-pilling effect

[0206] Anti-pilling level 4.

[0207] 4. Good stiffness

[0208] Bending length: radial, 1.8cm; weft, 1.7cm.

[0209] 5. Excellent elastic performance

[0210] Crease recovery angle: initial, 295 degrees; after 15 washes, 255 degrees.

[0211] 6. High color fastness...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Air flowaaaaaaaaaa
Moisture permeabilityaaaaaaaaaa
Air flowaaaaaaaaaa
Login to view more

Abstract

A multi-component fiber blended facing material is disclosed, whose weight proportion of spinning raw material is (the chaine is same with the weft yarn) 11-20% of tencel, 8-12% of ramee, 8-12% of bamboo fibre, 60-65% of terylene short fiber and 0.5-0.7% of conductive fibre. The invention implementing reasonable collocation and assembly of tencel, terylene, bamboo fibre, ramee and conductive fibre, which not only useds the large brute force and sticking dynam characteristic of terylene, but also full utilizes the superior characteristic and favorable wear behavior of tencel, bamboo fibre and ramee, thereby implementing ascendency complementary and inferior position elimination of various fibres, and meanwhile the conductive fibre has better and longer electrostatic resistance effect in the fibre blended yarns. The facing material has superior characteristics of moisture absorption, ventilating, electrostatic resistance, sticking, sliding, embonpoint hand feeling, good drapability, flokkit and pilling resistance, good model keeping performance, antimicrobial, etc. The invention has reasonable technique, resolve difficult problem of spinning and dyeing, and establish hardness foundation for the amenity and high-grade of the chemical fabrics facing material.

Description

technical field [0001] The invention relates to the field of textile, dyeing and finishing, in particular to a multi-component clothing fabric made of polyester as the main raw material, blended with tencel, bamboo fiber, hemp fiber and conductive fiber and its preparation technology. Background technique [0002] At present, fabrics composed of differentiated fibers mainly composed of polyester and viscose fibers and cotton, wool, silk, and hemp fibers are more and more favored by clothing manufacturers and consumers because of the combination of different advantages of various fibers. Gradually lead the "trend" of popular fabrics. But there are more or less defects in various aspects in this type of conventional combined fabric. [0003] Because usually, this type of conventional fabric is a combination of two to three fibers, such as "polyester / tencel", "polyester / bamboo fiber" and "polyester / linen" combination fabrics. Fabric defects are manifested in: "Polyester / Tence...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/00D03D47/18D03D47/30D02G3/04D06B7/00D06M13/188D06M16/00D06P3/872D03D15/208D03D15/217D03D15/225D03D15/283D03D15/41D03D15/47D03D15/533
Inventor 杨军武光信刘文和
Owner SHANDONG WOYUAN NEWFASHIONED FABRIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap