Manufacturing process of stator

A manufacturing process and stator technology, which is applied in the manufacture of stator/rotor bodies, etc., can solve the problems of difficult manufacturing methods, unstable product quality, and extremely high metallographic requirements, so as to achieve the integrity of metal fibers, make up for defects, and improve strength indicators Effect

Inactive Publication Date: 2010-01-20
镇江中虎弹簧有限公司
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional processing methods have defects such as low efficiency, excessive energy consumption, excessive investment in equipment, and unstable product quality.
The stator is a kind of transmission mechanism, which has high requirements on the wear resistance of the internal teeth, and at the same time has extremely high requirements on the metallurgy of the product (grain size grade is 6), which is difficult to achieve by traditional manufacturing methods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing process of stator

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The present invention will be described in further detail below in conjunction with the accompanying drawings and specific embodiments.

[0026] The process route of the present invention is: blanking → annealing → billet making → lubrication → hole extrusion → tooth extrusion

[0027] (1) Cutting: Use CNC band sawing machine for cutting, verticality ≤ 0.3

[0028] (2) Annealing: Use well-type vacuum annealing furnace to evacuate and fill with nitrogen to protect annealing. After annealing, the single side of oxidative decarburization is ≤0.1, and the material hardness after annealing is HB113-120

[0029] 20CrMnTi spheroidizing annealing process:

[0030] like figure 1 , Requirements: 1. Heating rate <150°C / h, cooling rate <50°C / h;

[0031] 2. Pre-vacuumize, fill with nitrogen after each pumping, and the pressure is ≥0.01Mpa;

[0032] 3. The annealed metallographic structure is F+P ball, and the grade is 4-6

[0033] (3) Blank making: C6130 ordinary lathe is used ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a manufacturing process of a stator, which comprises the following steps: (1) blanking: adopting a numerical control band sawing machine to carry out blanking with a verticality being smaller than or equal to 0.3; (2) annealing: adopting a well type vacuum annealing furnace to vacuumize and fill nitrogen for protection and annealing with an oxidation and decarbonization jersey knit being smaller than or equal to 0.1 and material hardness HB of 113-120 after the annealing; (3) blank preparing: adopting an ordinary C6130 lathe to prepare a blank by controlling a height error within 0.3; (4) lubrication process; (5) hole extruding: adopting an ordinary 4000KN oil press to extrude with extruding force P of 280T, an extruding hole diameter phi of 39+ / -0.05 and an extruding depth of 70+ / -0.5mm by reserving 5-6mm at the bottom of the hole after extruding with hole wall roughness of 1.6; and (6) gear extruding: adopting a 4000KN oil press to extrude with the extruding force P of 300T, gear accuracy of + / -0.03 and an extruding depth of 80+ / -0.5mm.

Description

technical field [0001] The invention relates to a new manufacturing process of a stator, which is used in the field of hydraulic transmission and belongs to the technical field of hydraulic motors. Background technique [0002] There are many types of stators currently on the market, and they are widely used in hydraulic motors and steering gears, but they are basically processed by traditional manufacturing techniques. Traditional processing methods have defects such as low efficiency, excessive energy consumption, excessive equipment investment and unstable product quality. The stator is a kind of transmission mechanism, which has high requirements on the wear resistance of the internal teeth, and at the same time has extremely high requirements on the metallurgy of the product (grain size grade is 6), which is difficult to achieve by traditional manufacturing methods. Contents of the invention [0003] 1. Technical problems to be solved: [0004] Aiming at the above d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H02K15/02
Inventor 孟昭达
Owner 镇江中虎弹簧有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap