Spinneret plate, profiled filament processed by utilizing same and preparation method thereof

A spinneret and fiber technology, applied in the field of special-shaped fibers and their preparation, achieves the effects of novel shape, good gloss effect and low cost

Active Publication Date: 2010-08-11
CHINESE TEXTILE ACAD
View PDF24 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In addition, related patents include US6673450B2, US6939608, US3673053, US5108838, US52081

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spinneret plate, profiled filament processed by utilizing same and preparation method thereof
  • Spinneret plate, profiled filament processed by utilizing same and preparation method thereof
  • Spinneret plate, profiled filament processed by utilizing same and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0072]The spinneret hole size used was the data shown in Table 1a. The melt direct spinning equipment is used, the raw material is PET, the spinning process parameters are shown in Table 1b, and the properties of the fibers are shown in Table 1c. Both the spinneret hole and the spinning process have adopted the conditions in the invention, and the fiber shape and performance have reached the conditions in the invention.

[0073] Table 1a. Spinning hole size of Example 1

[0074] project

parameter

The angle between the waist and height of A or B or C

15°

bc line

Connecting two straight lines

[0075] The spinning process parameter of table 1b. embodiment 1

[0076] condition

parameter

Spinning temperature °C

292

Spinning speed m / min

2850

Number of spinneret holes

96

blowing method

Outer ring blowing

[0077] Table 1c. Properties of Fibers of Example 1

[0078] ...

Embodiment 2

[0080] The spinneret hole size used is the data shown in Table 2a. The melt direct spinning equipment is used, the raw material is PET, the spinning process parameters are shown in Table 2b, and the properties of the fibers are shown in Table 2c. Both the spinneret hole and the spinning process have adopted the conditions in the invention, and the fiber shape and performance have reached the conditions in the invention.

[0081] Table 2a. Spinning hole size of Example 2

[0082] project

[0083] Table 2b. The spinning process parameters of Example 2

[0084] condition

[0085] Table 2c. Properties of Example 2 fibers

[0086] index

[0087] index

Embodiment 3

[0089] The spinneret hole size used is the data shown in Table 3a. The melt direct spinning equipment is used, the raw material is PET, the spinning process parameters are shown in Table 3b, and the properties of the fibers are shown in Table 3c. Both the spinneret hole and the spinning process have adopted the conditions in the invention, and the fiber shape and performance have reached the conditions in the invention.

[0090] Table 3a. Spinning hole size of Example 3

[0091] project

parameter

The angle between the waist and height of A or B or C

25°

bc line

Connecting two arcs

[0092] The spinning process parameter of table 3b. embodiment 3

[0093] condition

parameter

Spinning temperature °C

284

Spinning speed m / min

2860

Number of spinneret holes

72

blowing method

Outer ring blowing

[0094] Table 3c. Properties of Example 3 fibers

[0095] index

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a spinneret plate, a profiled filament processed by utilizing the same and a preparation method thereof. The spinneret orifices of the spinneret plate are trilobal, are symmetrical around the x,y and z shafts which mutually form the included angle of 120 degrees and are connected by the bottom edges of the minimum circumscribed isosceles triangles A, B and C of trefoil to form an equilateral triangle D; the included angle of the side and the height of A, B or C is 5-25 degrees; the contour line bc line of the trilobal is selected from two or a plurality of and two sections of or a plurality of sections of straight lines and quadratic curves and is formed by connecting in the minimum circumscribed isosceles triangle; and the contour lines ab line and the cd line of the trilobal are smoothly transiting curves. The spinneret plate can be used on a fusant direct spinning device with an on-line adding function, and fiber has the characteristic of high gloss by utilizing the phenomenon that the spinneret plate and the profiled filament prepared by the corresponding spinning process have better mirror reflection effect.

Description

technical field [0001] The invention relates to textile technology, which is a fiber manufacturing technology and its products, specifically, a spinneret, special-shaped fibers processed by the spinneret and a preparation method thereof. Background technique [0002] Due to the flat surface, the special-shaped cross-section fiber has a better gloss effect than the non-flat surface fiber, and is welcomed by functional fabrics, and the added value of the fiber is higher. The excellent properties of fine denier and micro-denier fibers are also the driving force behind the increasing pursuit of fine denier for various functional fibers, such as anti-ultraviolet, antibacterial, and antistatic fibers. It can be seen that the combination of special-shaped cross-section, fine denier and functionalization will undoubtedly increase the overall value of the fiber, and has a broad market demand. However, this has high requirements on spinning equipment and technology, as well as high r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01D5/253D01D5/08D01D5/12
Inventor 李健李鑫
Owner CHINESE TEXTILE ACAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap