Heat insulation material and method for preparing heat insulation shell from same

A technology of thermal insulation and pigment, applied in the direction of coating, can solve the problems of poor thermal insulation effect, fragile, poor appearance of thermal insulation materials, etc., and achieve the effect of improving thermal insulation effect

Inactive Publication Date: 2011-01-26
王锐
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the disadvantages of the prior art that the thermal insulation material is not easy to form, the thermal insulation effect is not good in the case of a small volume, it is fragile when forming, and the thermal insulation material has a poor appearance, and provides an easy-to-form, Thermal insulation material that can still ensure good thermal insulation effect and beautiful appearance in the case of small volume

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat insulation material and method for preparing heat insulation shell from same
  • Heat insulation material and method for preparing heat insulation shell from same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 257.71 grams of glass fiber, 257.87 grams of water, 6.45 grams of methyl cellulose, 22.03 grams of vinyl acetate and ethylene copolymer, 44.05 grams of bentonite, 85.9 grams of vermiculite, 28.63 grams of foaming agent, and 257.71 grams of thermosetting amino resin.

[0024] Preparation method: Add the above components into a mixer and mix and stir for later use.

Embodiment 2

[0026] 257.71 grams of glass fiber, 257.87 grams of water, 6.45 grams of methyl cellulose, 22.03 grams of vinyl acetate and ethylene copolymer, 44.05 grams of bentonite, 85.9 grams of vermiculite, 28.63 grams of foaming agent, and 257.71 grams of thermosetting amino resin.

[0027] Preparation method: Add the above components into a mixer and mix and stir for later use.

[0028] Embodiment one:

[0029] 257.71 grams of glass fiber, 257.87 grams of water, 6.45 grams of methyl cellulose, 22.03 grams of vinyl acetate and ethylene copolymer, 44.05 grams of bentonite, 85.9 grams of vermiculite, 28.63 grams of foaming agent, and 257.71 grams of thermosetting amino resin.

[0030] Preparation method: Add the above components into a mixer and mix and stir for later use.

[0031] Embodiment two:

[0032] 257.71 grams of glass fiber, 258.87 grams of water, 5.45 grams of methyl cellulose, 25.03 grams of vinyl acetate and ethylene copolymer, 41.05 grams of bentonite, 85.9 grams of vermi...

Embodiment 3

[0035] 237.71 grams of glass fiber, 257.87 grams of water, 6.45 grams of methyl cellulose, 22.03 grams of vinyl acetate and ethylene copolymer, 44.05 grams of bentonite, 105.9 grams of vermiculite, 28.63 grams of foaming agent, and 257.71 grams of thermosetting amino resin.

[0036] Preparation method: Add the above components into a mixer and mix and stir for later use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a heat insulation material, comprising 25-40% of glass fiber, 20-35% of methylcellulose solution, 3-10% of mixture of vinyl acetate and ethylene copolymer, 5-10% of bentonite, 3-10% of vermiculite, 1-5% of foaming agent and 25-35% of thermosetting amino resin. The invention further discloses a method for preparing a heat insulation shell from the heat insulation material, which comprises the following steps of: adding the materials into a blender mixer to be uniformly blended and stirred, then adding into a high-speed cutting machine to obtain a sludge object, adding the sludge object into a mold, which is heated to 180-280 DEG C, according to the weight of each style of product, pressure casting, keeping pressure for 2-3m to obtain the heat insulation shell. The heat insulation shell has the advantages of good energy-saving effect, easy formation and attractive appearance.

Description

technical field [0001] The invention belongs to the technical field of heat insulation materials, in particular to a heat insulation material used for household appliances and a method for preparing a heat insulation shell using the material. Background technique [0002] With the deterioration of the human living environment and the warming of the temperature, many countries have incorporated energy conservation and emission reduction into the national strategy, and the refinement of environmentally friendly products has gradually become a trend. At present, in the field of heat insulation materials, it has become the direction for enterprises to enhance their competitiveness by improving the heat insulation effect, reducing costs, and improving the convenience of use to increase the added value of products. In the prior art, there is a method of using air to improve the heat insulation effect, but because the existence of air reduces the compression resistance and flexibil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L61/20C08L61/28C08L23/08C08L31/04C08L1/26C08K7/14C08K3/34C08J9/04B29C45/00
Inventor 王锐
Owner 王锐
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com