Plastic-based composite material with permanent magnetism function and preparation method thereof

A composite material and plastic-based technology, which is applied in the field of plastic-based composite materials and its preparation, can solve the problems of the maximum magnetic energy area and unsatisfactory mechanical properties of composite magnetic plastics, and achieve the effect of good mechanical properties and large magnetic energy area

Inactive Publication Date: 2011-10-05
GUANGDONG HIGH & NEW ENG PLASTICS
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, magnetic plastics can be divided into two types: structural type and composite type. The structural type refers to the polymer itself with magnetic function, while the composite type refers to the permanent magnetic material formed by processing and co

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] A method for preparing a plastic-based composite material with permanent magnet function, comprising the following steps:

[0018] 1) Put the plastic matrix, compatibilizer, lubricant, and NdFeB surface-treated with a coupling agent in a mixer and mix for 2-3 minutes;

[0019] 2) Extrude the raw materials obtained in step 1) in a co-rotating twin-screw extruder, and the screw length-to-diameter ratio of the extruder is 1:30-40;

[0020] 3) Mix the material obtained in step 2) with ferrous metaferrate and antioxidant in a mixer for 2-3 minutes;

[0021] 4) The material obtained in step 3) is extruded in a co-rotating twin-screw extruder, and the length-to-diameter ratio of the screw of the extruder is 1:30-40.

Embodiment 1

[0026] A formula composition of a plastic-based composite material with permanent magnet function is shown in Table 1:

[0027] Table 1: Formulation composition of a plastic matrix composite with permanent magnet function

[0028] raw material

Embodiment 2

[0030] A formula composition of a plastic-based composite material with permanent magnet function is shown in Table 2:

[0031] Table 2: Formulation composition of a plastic matrix composite with permanent magnet function

[0032] raw material

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a plastic-based composite material with a permanent magnetism function which comprises the following raw materials by weight: 40-80 parts of plastic substances, 10-40 parts of ferroferric oxides, 10-20 parts of neodymium iron boron surface-treated by a coupling agent, 5-10 parts of compatilizers, 0.5-1 parts of lubricants, and 0.5-1 parts of antioxidants. The plastic-basedcomposite material with a permanent magnetism function prepared by the invention has good mechanical properties, and a large maximal magnetic energy area.

Description

technical field [0001] The invention relates to a plastic-based composite material with permanent magnet function and a preparation method thereof. Background technique [0002] As a new type of functional material, magnetic plastic is widely used in many fields such as electronics, electricity, instrumentation, communication, etc. due to its inherent characteristics. Due to the low density and high impact strength of magnetic plastic, it can be cut, cut, drilled, welded , lamination, and embossing patterns will not break when used, and can be directly injection molded. At the same time, it can be processed into products with high dimensional accuracy, thin walls, and complex shapes. Products with inserts can be formed to realize the miniaturization of electromagnetic equipment. , light weight, precision and high performance. Therefore, in some new fields, sintered magnets are gradually being replaced by magnetic plastics. At the same time, magnetic plastics consume less en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/06C08L67/02C08L51/06C08K13/06C08K3/24C08K3/38
Inventor 曾斌
Owner GUANGDONG HIGH & NEW ENG PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap