Bamboo-wood bottom plate for container and manufacture method thereof

A manufacturing method and container technology, which are applied in the directions of wood layered products, chemical instruments and methods, packaging, etc., can solve the problems of poor floor stability, easy to open layers, and it is difficult to meet the waterproof requirements of container bottom plates.

Inactive Publication Date: 2012-04-04
广州市国田集装箱配件有限公司
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The bamboo-wood composite board produced by this solution can basically meet the load-bearing requirements of the container bottom plate in terms of bending strength, but because it is difficult to solve the problem of overgluing the bamboo chips, the produced floor has poor stability and is easy to split. It is difficult to meet the waterproof requirements of the container floor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo-wood bottom plate for container and manufacture method thereof
  • Bamboo-wood bottom plate for container and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: A method for making the bamboo and wood floor of a container. First, the bamboo is broken into bamboo filaments, and then the bamboo filaments are carbonized into carbonized bamboo filaments at a temperature of 200 degrees and in an environment of 2 atmospheres of pressure and high humidity. ; The carbonized bamboo silk is woven into a bamboo silk veneer, wherein the thickness of the bamboo silk veneer is 2.5 millimeters, and a plurality of bamboo silk veneers are glued to form a multi-layer bamboo silk veneer layer; wherein the wood veneer is made of fast-growing Composed of wood, multiple wood veneers are glued to form multi-layer wood veneer layers; multi-layer bamboo silk veneer layers and multi-layer wood veneer layers are combined to form corresponding blanks, and the blanks are pre-prepared. Press waste to repair, after high temperature and high pressure hot pressing, it becomes a bamboo and wood glued floor, so that the bamboo and wood floor of the ...

Embodiment 2

[0023] Embodiment 2: A kind of manufacturing method of container bamboo floor, first break bamboo into bamboo silk, then carbonize bamboo silk under the temperature of 150 degrees, 1.87 atmospheric pressure and high humidity environment to become carbonized bamboo silk ; The carbonized bamboo silk is woven into a bamboo silk veneer, wherein the thickness of the bamboo silk veneer is 3 millimeters, and a plurality of bamboo silk veneers are glued to form a multi-layer bamboo silk veneer layer; wherein the wood veneer is made of fast-growing Composed of wood, multiple wood veneers are glued to form multi-layer wood veneer layers; multi-layer bamboo silk veneer layers and multi-layer wood veneer layers are combined to form corresponding blanks, and the blanks are pre-prepared. Press waste to repair, after high temperature and high pressure hot pressing, it becomes a bamboo and wood glued floor, so that the bamboo and wood floor of the container is produced.

Embodiment 3

[0024] Embodiment 3: A kind of manufacturing method of container bamboo and wood bottom plate, first break bamboo into bamboo silk, then carbonize bamboo silk under the temperature of 230 degrees, 3 atmospheres of pressure and high humidity environment to become carbonized bamboo silk ; The carbonized bamboo silk is woven into a bamboo silk veneer, wherein the thickness of the bamboo silk veneer is 4 millimeters, and a plurality of bamboo silk veneers are glued to form a multi-layer bamboo silk veneer layer; wherein the wood veneer is made of fast-growing Composed of wood, multiple wood veneers are glued to form multi-layer wood veneer layers; multi-layer bamboo silk veneer layers and multi-layer wood veneer layers are combined to form corresponding blanks, and the blanks are pre-prepared. Press waste to repair, after high temperature and high pressure hot pressing, it becomes a bamboo and wood glued floor, so that the bamboo and wood floor of the container is produced.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a bamboo-wood bottom plate for a container, which relates to the technical field of the aspect of the bottom plate for the container and is characterized in that the bamboo-wood bottom plate for the container is in a nineteen-layer-plate structure, wherein the first layer and the nineteenth layer are cloned surface bottom layers, the second layer to the sixth layer are single-wood-plate layers, the fourteenth layer to the eighteenth layer are single-wood-plate layers, and the seventh layer to the thirteenth layer are single-carbonization bamboo-filament-wood-plate layers. The bamboo-wood bottom plate for the container has the advantages of good waterproof and anti-corrosion performance and good stability.

Description

technical field [0001] The invention relates to the technical field of the bottom plate of the container. Background technique [0002] The Chinese utility model patent number is: 03205404.1 discloses a container bottom plate, which is formed by overlapping and hot-pressing an odd number of multi-layer wooden veneers, including an upper surface plate, a lower surface plate, and a core plate. The upper and lower surface plates each include three or four veneer, the wood grain directions of the veneers of each layer comprising the upper surface plate, the lower surface plate and the core plate are symmetrically arranged on both sides of the veneer in the center layer of the core plate, and the upper and lower surface plates are both When including three layers of veneers along the grain, the core board includes a structure in which one veneer with transverse grains overlaps with five consecutive veneers along the grain; when the upper and lower surface boards both include four...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B65D90/02B32B21/13B32B21/14B27M3/00
CPCY02W90/10
Inventor 陈志航
Owner 广州市国田集装箱配件有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com