Heat resistant magnesium alloy

A magnesium alloy, heat-resistant technology, applied in the field of magnesium alloys, can solve the problems of high temperature resistance, high working temperature, unsuitable components to work, etc., and achieve the effect of improving high temperature resistance, good fluidity and die casting, and excellent mechanical properties.

Inactive Publication Date: 2012-08-01
JIANGHAN UNIVERSITY
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the process of realizing the present invention, the inventor has found that the prior art has at least the following problems: some parts on the automobile, such as: gearbox case, engine case cover, etc., have higher operating temperature, and there are also lightweight parts. need
But the above-mentioned MgAlZn series magnesium alloy is due to the β phase in the alloy structure as Mg 17 Al 12 Mainly, Mg

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat resistant magnesium alloy
  • Heat resistant magnesium alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Prepare the heat-resistant magnesium alloy according to the steps described in the above-mentioned process one, and the casting is cast by metal mold, and the weight percentage of the magnesium alloy is composed of Al 25%, Zn 3.5%, Mn 2.2%, Y 16%, Nb 4%, Zr 2 %, the rest is Mg.

[0030] Heat treatment of castings (T4 solid solution treatment process): the castings are heated up to 400°C in a box-type resistance furnace and kept for 12 hours. After the castings are released from the furnace, they are water quenched at a water temperature of 80°C.

[0031] See Table 1 for the properties of the magnesium alloy castings provided in this example.

Embodiment 2

[0033] Prepare the heat-resistant magnesium alloy according to the steps described in the above-mentioned process two, the casting adopts semi-solid casting, and the weight percentage of the magnesium alloy is composed of Al 10%, Zn 1%, Mn 0.6%, Gd 2%, Nb 1%, Zr 0.9 %, the rest is Mg.

[0034]Heat treatment of castings (T4 solid solution treatment process): the castings are heated up to 400°C in a box-type resistance furnace and kept for 12 hours. After the castings are released from the furnace, they are water quenched at a water temperature of 80°C.

[0035] See Table 1 for the properties of the magnesium alloy castings provided in this example.

Embodiment 3

[0037] Prepare the heat-resistant magnesium alloy according to the steps described in the above-mentioned process 1. The casting adopts high-pressure die-casting, and the weight percentage of the heat-resistant magnesium alloy is composed of Al 1.5%, Zn 0.1%, Mn 0.1%, Sm 0.0002%, Nb 0.0002%, Zr 0.001% , and the rest are Mg.

[0038] See Table 1 for the properties of the magnesium alloy castings provided in this example.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a heat resistant magnesium alloy and belongs to the magnesium alloy field. The magnesium alloy is composed of Mg, Al, Zn, Mn, rare earths, Nb and Zr, and comprises, by weight, 1.5 to 25 percents of Al, 0.1 to 3.5 percents of Zn, 0.1 to 2.2 percents of Mn, 0.0002 to 16 percents of rear earths, 0.0002 to 4 percents of Nb, 0.001 to 2 percents of Zr, and the balance Mg. According to the magnesium alloy, the structure of Beta phase is changed by adding rare earth elements and the Nb element into the magnesium alloy; and grains are refined and the alloy liquid is purified by adding the Zr element, so that the heat resistant performance of the magnesium alloy is improved, and the heat resistant magnesium alloy which has good mechanical properties, machinability, mobility and die-casting properties and is suitable for casting in particular to die-casting is obtained.

Description

technical field [0001] The invention relates to a magnesium alloy, in particular to a MgAlZn heat-resistant magnesium alloy suitable for casting, especially die-casting. Background technique [0002] With the development of science and technology, vehicles represented by automobiles need to further develop new products with higher fuel efficiency by reducing the weight of the body. In the automobile manufacturing industry, magnesium alloy, as a new type of lightweight metal material, is used by automobile manufacturers to replace traditional cast iron in order to achieve the purpose of reducing the weight of the vehicle body. [0003] At present, the grades of domestic MgAlZn series die-casting magnesium alloys are YM302, YM303, YM304, YM305; the grades of MgAlZn series die-casting magnesium alloys of the American standard ASTM B are AZ91A, AZ91B, AZ91D; the grades of MgAlZn series die-casting magnesium alloys of the Japanese standard JIS H are MDC1B, MDC1D; European standa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C23/02C22C1/03
Inventor 冯俊
Owner JIANGHAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap