Preparation method for cobalt carbonate material with dense structure and globoid shape

A sphere-like, cobalt carbonate technology, applied in cobalt carbonate and other directions, can solve the problems of poor uniformity, cluttered morphology, and loose microstructure of cobalt carbonate materials, and achieve the effect of better structure, uniform particle size, and easy control of process parameters.

Active Publication Date: 2014-05-21
NORTHWEST RES INST OF MINING & METALLURGY INST
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a method for preparing a cobalt carbonate material with a compact structure and a spheroidal appearance, so as to solve the problems of loose microstructure, disordered appearance and poor uniformity of the cobalt carbonate material prepared by conventional production methods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for cobalt carbonate material with dense structure and globoid shape
  • Preparation method for cobalt carbonate material with dense structure and globoid shape
  • Preparation method for cobalt carbonate material with dense structure and globoid shape

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Put the filtered cobalt chloride solution with a cobalt concentration of 1.0 mol / L and a pH value of 4.75 into the reactor;

[0024] Under stirring conditions, the heating step Solution, control the temperature of the solution system at 55°C, and keep the temperature of the system relatively stable;

[0025] Spray the pre-filtered ammonium bicarbonate solution with a concentration of 1.8 mol / L to the step at a constant speed of 800L / h in the system;

[0026] control step The pH value of the medium solution system is 7.5 as the end point of the system reaction, that is, the addition of the ammonium bicarbonate solution is terminated;

[0027] will step The obtained solid-liquid system was aged for 20 minutes, filtered and washed repeatedly to obtain the desired material.

[0028] The spherical shape structure and particle size distribution of the material obtained in embodiment 1 are as follows: figure 1 and figure 2 , the physical index "particle s...

Embodiment 2

[0030] Put the filtered cobalt chloride solution with a cobalt concentration of 1.5 mol / L and a pH value of 4.80 into the reactor;

[0031] Under stirring conditions, the heating step Solution, control the temperature of the solution system at 63°C, and keep the temperature of the system relatively stable;

[0032] Spray the pre-filtered ammonium bicarbonate solution with a concentration of 2.0 mol / L to the step at a constant speed of 588L / h in the system;

[0033] control step The pH value of the middle solution system is 7.2 as the end point of the system reaction, that is, the addition of the ammonium bicarbonate solution is terminated;

[0034] will step The obtained solid-liquid system was aged for 30 minutes, filtered and washed repeatedly to obtain the desired material.

[0035] The spheroid morphology and particle size distribution of the material obtained in embodiment 2 are as follows: image 3 and Figure 4 , the physical index "particle size an...

Embodiment 3

[0037] Put the filtered cobalt chloride solution with a cobalt concentration of 1.6 mol / L and a pH value of 5.09 into the reactor;

[0038] Under stirring conditions, the heating step Solution, control the temperature of the solution system at 60°C, and keep the temperature of the system relatively stable;

[0039] Spray the pre-filtered ammonium bicarbonate solution with a concentration of 1.86 mol / L to the step at a constant speed of 280L / h in the system;

[0040] control step The pH value of the middle solution system is 7.2 as the end point of the system reaction, that is, the addition of the ammonium bicarbonate solution is terminated;

[0041] will step The obtained solid-liquid system was aged for 30 minutes, filtered and washed repeatedly to obtain the desired material.

[0042] The spheroid morphology and particle size distribution of the material obtained in embodiment 3 are as follows: Figure 5 and Figure 6 , the physical index "particle size ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a cobalt carbonate material with a dense structure and a globoid shape, and aims to solve the problem that the cobalt carbonate material prepared by the conventional method has a loose microstructure, a clutter shape and poor uniformity. The preparation method comprises the following steps: putting a cobalt chloride solution meeting requirements of system temperature, pH value and cobalt concentration in a reaction kettle, and keeping relatively constancy; adding an ammonium bicarbonate solution uniformly into a cobalt solution system according to a certain flow, with a defined pH value as a reaction terminal parameter of a control system; and after aging for a certain time, filtering and repeatedly washing to obtain the required cobalt carbonate material. The cobalt carbonate material has the characteristics of globoid shape, uniform particle size, dense structure and better particle size distribution; the specific cobalt carbonate material is prepared by using standard conventional equipment; process parameters are easy to control; the operation is simple; and the cobalt carbonate material is suitable for large-scale production.

Description

technical field [0001] The invention belongs to the field of new energy and new materials, and relates to a method for preparing a cobalt carbonate material with characteristic requirements on microscopic appearance and physical properties. The cobalt carbonate obtained by the preparation method can be used to produce battery materials, hard alloys, electronic materials, etc. Precursor material for cobalt oxide products. Background technique [0002] With the vigorous development of the electronics and communication industries, the demand for lithium-ion secondary batteries for various household appliances, mobile phones, and notebook computers has doubled. Cobalt tetroxide, as an important raw material for lithium cobalt oxide materials for lithium batteries, has also achieved rapid progress in its production technology. . The appearance of cobalt oxide (especially cobalt tetroxide) is gray-black or black powder. It is an important transition metal oxide and is usually us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G51/06
Inventor 吉鸿安朱来东王同敏
Owner NORTHWEST RES INST OF MINING & METALLURGY INST