Anticorrosion and mildew-resistant Song brocade fabric and its manufacturing method

Abstract

Disclosed are an anticorrosion and mildew-resistant Song brocade fabric and its manufacturing method. The manufacturing method comprises the following steps of: preparing a surface treatment fluid for spray by the use of a polyacrylic acid film forming emulsion and an antiseptic; spraying the surface treatment fluid on the surface of a pair of compression rollers to make them absorb a certain amount of the surface treatment fluid; allowing a Song brocade fabric which is required to be processed to pass through the compression rollers in the state of open width and at constant speed; and making the surface treatment fluid part on the compression rollers transfer onto the front and back sides of the Song brocade fabric under a certain extruding force until the total permeation degree of the surface treatment fluid on the Song brocade fabric finally reaches 1 / 4-3 / 4 of the thickness of the fabric. After being dried, the Song brocade fabric processed by the method has obvious anticorrosion and mildew-resistant effects, and maintains its original softness and permeability.

Description

technical field

[0001] The invention relates to an antibacterial mulberry silk satin and a manufacturing method thereof. The real silk satin is suitable for various artworks and decoration purposes. Background technique

[0002] Song Brocade is one of the "Three Famous Brocades" in China, and it got its name from the Song Dynasty. Song brocade is made of mulberry silk, which is mainly used for non-clothing decorative products, such as painting and calligraphy mounting and decoration materials. Song brocade has been included in the first batch of national intangible cultural heritage list, and has been included in the world intangible cultural heritage. Although Song brocade has high artistic value, since silk itself is prone to mildew in humid environment and moderate temperature, severe mildew not only affects its appearance, but also accelerates fiber decay. Song brocade products, especially Song brocade works of art cannot be cleaned by conventional washing methods, so ...

Examples

Embodiment 1

[0009] The polyacrylic acid film-forming resin emulsion with a solid content of 30% is diluted with water into a surface treatment solution with a concentration of 10%, and then 3% FM2598 antibacterial agent (in terms of surface treatment solution weight) is added therein. The antibacterial agent is provided by Jiangsu Silk Science provided by the Institute. The surface treatment liquid prepared in the above-mentioned manner is evenly sprayed onto the surface of the extrusion roller through the upper and lower sprayers, so that the felt layer on the surface of the extrusion roller absorbs a certain amount of surface treatment liquid. 100% mulberry silk Song brocade fabric passes through the extrusion film at a running speed of 10m / min, applying an extrusion force of 2kg, the total penetration of the surface treatment liquid on the front and back of the fabric is about 3 / 4, and the fabric is subjected to a mildew test after drying .

Embodiment 2

[0011] The polyacrylic acid film-forming resin emulsion with a solid content of 40% is diluted with water into a surface treatment solution with a concentration of 10%, and then 5% FM2598 antibacterial agent (in terms of surface treatment solution weight) is added thereto. The antibacterial agent is provided by Jiangsu Silk Science provided by the Institute. The surface treatment liquid prepared in the above-mentioned manner is evenly sprayed onto the surface of the extrusion roller through the upper and lower sprayers, so that the felt layer on the surface of the extrusion roller absorbs a certain amount of surface treatment liquid. 100% mulberry silk Song brocade fabric passes through the extrusion film at a running speed of 20m / min, applying an extrusion force of 3kg, the total penetration of the surface treatment liquid on the front and back of the fabric is about 1 / 2, and the fabric is subjected to a mildew test after drying .

[0012] Anti-fungal mildew test method is a...

technical field

[0001] The invention relates to an antibacterial mulberry silk satin and a manufacturing method thereof. The real silk satin is suitable for various artworks and decoration purposes. Background technique

[0002] Song Brocade is one of the "Three Famous Brocades" in China, and it got its name from the Song Dynasty. Song brocade is made of mulberry silk, which is mainly used for non-clothing decorative products, such as painting and calligraphy mounting and decoration materials. Song brocade has been included in the first batch of national intangible cultural heritage list, and has been included in the world intangible cultural heritage. Although Song brocade has high artistic value, since silk itself is prone to mildew in humid environment and moderate temperature, severe mildew not only affects its appearance, but also accelerates fiber decay. Song brocade products, especially Song brocade works of art cannot be cleaned by conventional washing methods, so ...

Examples

Embodiment 1

[0009] The polyacrylic acid film-forming resin emulsion with a solid content of 30% is diluted with water into a surface treatment solution with a concentration of 10%, and then 3% FM2598 antibacterial agent (in terms of surface treatment solution weight) is added therein. The antibacterial agent is provided by Jiangsu Silk Science provided by the Institute. The surface treatment liquid prepared in the above-mentioned manner is evenly sprayed onto the surface of the extrusion roller through the upper and lower sprayers, so that the felt layer on the surface of the extrusion roller absorbs a certain amount of surface treatment liquid. 100% mulberry silk Song brocade fabric passes through the extrusion film at a running speed of 10m / min, applying an extrusion force of 2kg, the total penetration of the surface treatment liquid on the front and back of the fabric is about 3 / 4, and the fabric is subjected to a mildew test after drying .

Embodiment 2

[0011] The polyacrylic acid film-forming resin emulsion with a solid content of 40% is diluted with water into a surface treatment solution with a concentration of 10%, and then 5% FM2598 antibacterial agent (in terms of surface treatment solution weight) is added thereto. The antibacterial agent is provided by Jiangsu Silk Science provided by the Institute. The surface treatment liquid prepared in the above-mentioned manner is evenly sprayed onto the surface of the extrusion roller through the upper and lower sprayers, so that the felt layer on the surface of the extrusion roller absorbs a certain amount of surface treatment liquid. 100% mulberry silk Song brocade fabric passes through the extrusion film at a running speed of 20m / min, applying an extrusion force of 3kg, the total penetration of the surface treatment liquid on the front and back of the fabric is about 1 / 2, and the fabric is subjected to a mildew test after drying .

[0012] Anti-fungal mildew test method is a...