Stainless steel alloy material

An alloy material and stainless steel technology, applied in the field of stainless steel alloy materials, can solve the problems of non-corrosion and wear resistance, and achieve the effects of high resistance to cold and heat fatigue, low processing cost, and good oxidation resistance.

Inactive Publication Date: 2013-01-16
WUXI HONGCHANG HARDWARE MFG
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the long-term use of conventional stainless steel materials, there are still disadvantages of non-wear resistance and corrosion resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The stainless steel alloy material is prepared from the following components in parts by weight:

[0016] C: 0.05 parts, Cr: 10 parts, Mo: 3 parts, Ni: 5 parts, Cu: 0.1 parts, Si: 0.2 parts, Mn: 0.3 parts, B: 0.1 parts, Ti: 0.1 parts, Al: 0.1 parts, N: 0.01 parts, S: 0.01 parts, Fe: 80-100 parts.

[0017] The above ingredients can be finished by conventional smelting technology.

[0018] After the stainless steel alloy material prepared in this embodiment is made into a cutter, compared with a common cutter, the results are as follows:

[0019] .

Embodiment 2

[0021] The stainless steel alloy material is prepared from the following components in parts by weight:

[0022] C: 0.10 parts, Cr: 20 parts, Mo: 5 parts, Ni: 7 parts, Cu: 0.5 parts, Si: 0.8 parts, Mn: 0.6 parts, B: 0.5 parts, Ti: 0.8 parts, Al: 0.3 parts, N: 0.05 parts, S: 0.05 parts, Fe: 100 parts.

Embodiment 3

[0024] The stainless steel alloy material is prepared from the following components in parts by weight:

[0025] C: 0.06 parts, Cr: 12 parts, Mo: 4 parts, Ni: 6 parts, Cu: 0.2 parts, Si: 0.4 parts, Mn: 0.4 parts, B: 0.2 parts, Ti: 0.4 parts, Al: 0.2 parts, N: 0.02 parts, S: 0.03 parts, Fe: 80 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides stainless steel alloy material. The stainless steel alloy material comprises, by weight, 0.05-0.10 part of C, 10-20 parts of Cr, 3-5 parts of Mo, 5-7 parts of Ni, 0.1-0.5 part of Cu, 0.2-0.8 part of Si, 0.3-0.6 part of Mn, 0.1-0.5 part of B, 0.1-0.8 part of Ti, 0.1-0.3 part of Al, 0.01-0.05 part of N, 0.01-0.05 part of S, and 80-100 parts of Fe. The stainless steel alloy material has the advantages of corrosion resistance, wear resistance, less easiness in passivation.

Description

technical field [0001] The invention relates to the field of alloy materials, in particular to a stainless steel alloy material. Background technique [0002] Stainless Steel (Stainless Steel) refers to steel resistant to weak corrosive media such as air, steam, water, and chemically corrosive media such as acid, alkali, and salt. It is also called stainless acid-resistant steel. In practical applications, the steel resistant to weak corrosion medium is often called stainless steel, and the steel resistant to chemical medium corrosion is called acid-resistant steel. Due to the difference in chemical composition between the two, the former is not necessarily resistant to chemical media corrosion, while the latter is generally stainless. The corrosion resistance of stainless steel depends on the alloying elements contained in the steel. The basic alloying elements of stainless steel include nickel, molybdenum, titanium, niobium, copper, nitrogen, etc., to meet the requiremen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/54C22C38/60
Inventor 浦永建
Owner WUXI HONGCHANG HARDWARE MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com