Composition for optical materials

一种光学材料、组合物的技术，应用在光学、光学元件、仪器等方向，能够解决聚合不均匀等问题，达到抑制聚合不均匀的效果

Active Publication Date: 2015-08-19
MITSUBISHI GAS CHEM CO INC
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the polymerization curing of compositions containing these compounds sometimes leads to the occurrence of non-uniform polymerization called streaks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition for optical materials

Examples

Experimental program
Comparison scheme
Effect test

specific example

[0058]Preferable examples of the ultraviolet absorber include benzotriazole compounds. Specific examples of particularly preferred compounds include: 2-(2-hydroxy-5-methylphenyl)-2H-benzotriazole, 5-chloro-2-(3,5-di-tert-butyl-2-hydroxy Phenyl)-2H-benzotriazole, 2-(3-tert-butyl-2-hydroxy-5-methylphenyl)-5-chloro-2H-benzotriazole, 2-(3,5- Di-tert-amyl-2-hydroxyphenyl)-2H-benzotriazole, 2-(3,5-di-tert-butyl-2-hydroxyphenyl)-2H-benzotriazole, 2-(2- Hydroxy-4-octyloxyphenyl)-2H-benzotriazole and 2-(2-hydroxy-5-tert-octylphenyl)-2H-benzotriazole. Preferable examples of the bluing agent include anthraquinone compounds.

[0059] In addition, when the composition for optical materials of the present invention is difficult to take out from the mold, known external and / or internal mold release agents may be used or added to improve the mold release properties of the resulting cured material. Examples of the release agent include: nonionic fluorine-based surfactants, nonionic silicon-...

Embodiment 1

[0082] The curing was performed by polymerization method A using a polymerization catalyst comprising 99.6% by mass of dibutyltin dichloride and 0.4% by mass of monobutyltin trichloride. The observed results were rated as excellent streak suppression. The evaluated results are shown in Table 1.

Embodiment 2 to 4

[0084] Curing was performed by the polymerization method shown in Table 1 using a polymerization catalyst containing 99.6% by mass of dibutyltin dichloride and 0.4% by mass of monobutyltin trichloride. The evaluated results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
aperture sizeaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a composition for an optical material, which is capable of suppressing occurrence of polymerization unevenness called striae, in particular, striae to be caused in high-powered lenses with sharp curves, and more specifically relates to a composition for an optical material including: a polymerization catalyst having a mass ratio of dibutyltin dichloride to monobutyltin trichloride of 97.0 / 3.0 to 100.0 / 0.0; a polythiol compound; and a polyiso(thio)cyanate compound.

Description

technical field [0001] The present invention relates to compositions and the like for optical materials, and more particularly to optical materials suitable for use as optical materials (such as plastic lenses, prisms, optical fibers, information recording substrates, and optical filters) and particularly suitable for use as plastic lenses With composition etc. Specifically, the present invention relates to an optical material having good optical properties and prepared from a polyurethane-based resin by polymerization of a polymerizable composition comprising a polythiol compound and a polyiso(thio)cyanate compound. The response is obtained. Background technique [0002] Optical materials made of resin are lightweight and less prone to damage than optical materials made of inorganic materials, and can be dyed. Therefore, it has been rapidly applied to various optical materials such as spectacle lenses and camera lenses in recent years. [0003] Higher performance is requ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/24G02B1/04
CPCC08G18/3876C08G75/00C08G18/242G02B1/04C08L75/04C08L81/00C08G18/24C08G18/52C08L75/00
Inventor 竹村纮平堀越裕
Owner MITSUBISHI GAS CHEM CO INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com