A heat treatment process for low-alloy structural steel and low-carbon structural steel

A technology of structural steel and low alloy, applied in the field of heat treatment of iron and steel materials, can solve problems such as not meeting the requirements of use, and achieve the effects of improving toughness, refining grain size, and large elastic-plastic deformation delay interval

Active Publication Date: 2016-08-10
CHENGDU XINZHU ROAD & BRIDGE MASCH CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, low-alloy structural steel without special treatment process cannot meet the requirements of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A heat treatment process for low-alloy structural steel and low-carbon structural steel
  • A heat treatment process for low-alloy structural steel and low-carbon structural steel
  • A heat treatment process for low-alloy structural steel and low-carbon structural steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Taking the low-alloy structural steel Q345B sample as an example, the composition (weight%) of the sample is: 0.18%C, 0.45%Si, 1.65%Mn, 0.03%P, 0.03%S, 0.01%N, 0.15%V , 0.25%Cr, 0.45%Ni, 0.20%Cu. The sample diameter d is 10mm, and the original gauge length Lo is 50mm.

[0031] After preparing the sample, set the process parameters of the heating furnace and tempering furnace: the normalizing temperature is 910°C, and the holding time is 90 minutes; the tempering temperature is 480°C, and the holding time is 120 minutes.

[0032] Then put the samples into the material frame, the samples are evenly arranged and the intervals are neat, put the material frame into the heating furnace, make sure the material frame is reliable, close the furnace door, call out the microcomputer process program, press "Start", the process will start automatically , and turn on the temperature recorder at the same time; after the heating and heat preservation program is over, close the normali...

Embodiment 2

[0041] Taking the low-carbon structural steel Q235 sample as an example, the composition (weight %) of the sample is: 0.20%C, 0.32%Si, 1.38%Mn, 0.043%P, 0.04%S, 0.006%N, 0.25%Cr , 0.28%Ni, 0.25%Cu. The sample diameter d is 10mm, and the original gauge length Lo is 50mm.

[0042] After preparing the sample, set the process parameters of the heating furnace and tempering furnace: the normalizing temperature is 920°C, and the holding time is 90 minutes; the tempering temperature is 650°C, and the holding time is 120 minutes.

[0043] Then put the samples into the material frame, the samples are evenly arranged and the intervals are neat, put the material frame into the normalizing furnace, make sure the material frame is reliable, close the furnace door, call out the microcomputer process program, press "Start", the process will start automatically , and turn on the temperature recorder at the same time; after the heating and heat preservation program is over, close the normaliz...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
yield ratioaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of heat treatment of iron and steel materials, and in particular relates to a heat treatment process of low-alloy structural steel and low-carbon structural steel. The process includes the following steps: put the material into the heating furnace, raise the temperature to 880°C-950°C with the furnace, normalize and keep it for 60-120 minutes; Cold, after air cooling, the temperature is controlled at 300°C-600°C; put the air-cooled material into the tempering furnace for tempering treatment, the tempering temperature is controlled at 450°C-650°C, keep warm for 120-180 minutes, and air-cool to room temperature. This process improves the toughness of low-alloy structural steel and low-carbon structural steel, refines the grain size, makes the yield (displacement) section of the material steel more than 2mm, and increases the yield strength by 15-20%, which can be used for bridge insulation Vibration materials or suitable for places that require high toughness of materials.

Description

technical field [0001] The invention belongs to the technical field of heat treatment of iron and steel materials, and in particular relates to a heat treatment process of low-alloy structural steel and low-carbon structural steel. Background technique [0002] The seismic isolation of bridges and buildings has become the main content of modern seismic isolation design, and the selection and treatment of seismic isolation materials have become the most core content. In particular, large bridges require large displacement changes and high requirements for shock absorption and isolation, and the requirements for shock absorption and isolation are extremely special. At present, some countries in the world have carried out systematic research on shock-absorbing and isolating materials, and have also achieved some results. However, most of them are used in the shock absorption and isolation of buildings, and the shock absorption effect is not obvious. The shock-absorbing and is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C21D1/00C21D6/00
Inventor 向阳邹贻军刘海量杨刚尧宗友
Owner CHENGDU XINZHU ROAD & BRIDGE MASCH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap