Transparent film-forming coating liquid and substrate with transparent film

A technology of coating liquid and film, which is applied in the direction of coating, conductive coating, anti-reflection coating, etc., and can solve the problems of unevenness and other problems

Active Publication Date: 2014-03-26
JGC CATALYSTS & CHEM LTD
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] However, in Patent Documents 4 and 5, as in Patent Document 2, the object is to exist unevenly, so the properties targeted by the present invention cannot necessarily be exhibited, and there are also problems on substrates such as plastics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent film-forming coating liquid and substrate with transparent film
  • Transparent film-forming coating liquid and substrate with transparent film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0170] [Example 1] Preparation of Surface-treated Silica Microparticles (A-1) Dispersion

[0171] Silica-alumina sol (manufactured by Nikke Catalyst Chemicals Co., Ltd.: USBB-120, average particle size 25nm, SiO 2 ·Al 2 o 3 Concentration 20% by weight, Al in solid content 2 o 3 Content 27% by weight) 3680g of pure water was added to 120g, the temperature was raised to 95°C, and SiO was added while maintaining the temperature. 2 Concentration is 15% by weight of sodium silicate aqueous solution 2100g and Al 2 o 3 Concentration is 2100g of sodium aluminate aqueous solution 5% by weight, obtains SiO 2 ·Al 2 o 3 Composite oxide microparticles (1-1) (average particle diameter: 43 nm) dispersion. Al at this time 2 o 3 / SiO 2 The molar ratio was 0.2. The pH of the reaction liquid at this time was 12.0.

[0172] Added with SiO 2 The concentration is 15% by weight of sodium silicate aqueous solution 8800g and Al 2 o 3 Concentration is 5% by weight sodium aluminate aq...

Embodiment 2

[0222] Preparation of Coating Solution (2) for Transparent Film Formation

[0223] A mixed alcohol of methanol, ethanol and isopropanol (Nippon Alcohol Trading Co. Produced by the company: Solmix AP-11) 76.76 g, PGME 13.24 g, 4.10 g of a dispersion of surface-treated chain-shaped conductive metal oxide particles (B-1) prepared in the same manner as in Example 1 with a solid content concentration of 20.5% by weight , 1.44 g of pentaerythritol triacrylate (manufactured by Kyoeisha Chemical Co., Ltd.: ライトアクリレートPE-3A, resin concentration 100% by weight) and 0.95 g of a photoinitiator (manufactured by Ciba Seika Co., Ltd.: イルガキュュア184), fully mixed, A coating liquid (2) for forming a transparent film having a solid content concentration of 3% by weight was prepared.

[0224] Preparation of substrate (2) with transparent film

[0225] In Example 1, except having used the coating liquid (2) for transparent film formation, the base material (2) with a transparent film was prepare...

Embodiment 3

[0226] [Example 3] Preparation of Coating Solution (3) for Transparent Film Formation

[0227] A mixed alcohol of methanol, ethanol and isopropanol (Nippon Alcohol Trading Co. Produced by the company: Solmix AP-11) 76.76 g, PGME 13.24 g, 1.76 g of a dispersion of surface-treated chain-shaped conductive metal oxide particles (B-1) prepared in the same manner as in Example 1 with a solid content concentration of 20% by weight , 1.44 g of pentaerythritol triacrylate (manufactured by Kyoeisha Chemical Co., Ltd.: ライトアクリレートPE-3A, resin concentration 100% by weight) and 0.95 g of a photoinitiator (manufactured by Ciba Seika Co., Ltd.: イルガキュュア184), fully mixed, A coating liquid (3) for forming a transparent film having a solid content concentration of 3% by weight was prepared.

[0228] Preparation of substrate (3) with transparent film

[0229] In Example 1, except having used the coating liquid (3) for transparent film formation, the base material (3) with a transparent film w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a transparent film-forming coating liquid for forming a transparent film having a refractive index reducing from a lower layer to a top layer, excellent light transmittance and transparency and anti-static and anti-reflection performances. The transparent film-forming coating liquid is composed of surface-treated silica type particles (A), surface-treated chain conductive metal oxide particles (B), a matrix-forming component and a solvent. An average particles size (DA) of the surface-treated silica type particles (A) is within 10-200 nm; the surface-treated chain conductive metal oxide particles (B) is formed by connecting 2-30 metal oxide particles with an average particles size (DA) being within 5-20 nm into a chain; and the metal oxide particles are chain conductive particles with a volume resistance value being 10<-2>-10<0> ohms.cm. A concentration of the surface-treated silica type particles (A) is within a range of 0.05-35 wt.% in terms of solids; a concentration of the surface-treated chain conductive metal oxide particles (B) is within a range of 0.025-25 wt.% in terms of solids; a concentration of the matrix-forming component is within a range of 0.1-42.5 wt.% in terms of the solids; and a concentration of total solids is within a range of 0.5-50 wt.%.

Description

technical field [0001] The present invention relates to a coating liquid for forming a transparent film for forming a transparent film comprising a chain-shaped conductive metal oxide particle component with a high refractive index and a substrate with a transparent film by applying once. A coating liquid containing silica-based particle components with a low rate has at least antistatic performance and antireflection performance. Especially in the transparent film, the content of the conductive component gradually decreases from the lower layer to the upper layer of the transparent film. On the one hand, the content of low refractive index components gradually decreases from the upper layer to the lower layer of the transparent film. As a result, the refractive index gradually decreases from the lower layer to the upper layer, and the light transmittance and transparency are excellent, and it has antistatic and antireflection properties. Background technique [0002] Conven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D7/12B32B27/18C09C1/00C09C1/28C09C3/12C09D5/24C09D201/00G02B1/10G02B1/11G02B1/111G02B1/16
CPCC08K3/22C08K3/36C08K9/06C08K2201/001C09D5/006C09D5/24C09D7/62C09D7/67C09D7/68C09D7/70
Inventor 箱嶋夕子松田政幸村口良
Owner JGC CATALYSTS & CHEM LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com