High temperature dye leveler for polyester fibers

A high-temperature leveling agent and polyester fiber technology, applied in dyeing, textiles and papermaking, etc., can solve the problems of unsatisfactory dyeing effect of polyester fiber fabrics, achieve good leveling effect, uniform color of fabrics, and improve bulkiness The effect of softness

Inactive Publication Date: 2014-04-23
CHANGSHU MIAOQUAN SHENGDA AUX FACTORY
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing high-temperature leveling agents are not ideal for dyeing polyester fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A high-temperature leveling agent for polyester fibers, made from the following raw materials:

[0022] 2 parts polyglyceryl monostearate,

[0023] 0.2 parts of zinc acetate,

[0024] 1 part dodecyltrimethylammonium chloride,

[0025] 80 parts leveling agent,

[0026] 0.1 part magnesium acetate,

[0027] 12 parts polyamide,

[0028] 0.3 parts calcium acetate,

[0029] 5 parts polyethylene glycol,

[0030] 0.2 parts tin acetate,

[0031] 4.5 parts ethylene glycol,

[0032] 3 parts dimethyl terephthalate,

[0033] 1 part hydroxypropyl methylcellulose.

Embodiment 2

[0035] A high-temperature leveling agent for polyester fibers, made from the following raw materials:

[0036] 1 part polyglyceryl monostearate,

[0037] 0.2 parts of zinc acetate,

[0038] 1 part dodecyltrimethylammonium chloride,

[0039] 80 parts leveling agent,

[0040] 0.1 part magnesium acetate,

[0041] 12 parts polyamide,

[0042] 0.3 parts calcium acetate,

[0043] 5 parts polyethylene glycol,

[0044] 0.2 parts tin acetate,

[0045] 4.5 parts ethylene glycol,

[0046] 3 parts dimethyl terephthalate,

[0047] 1 part hydroxypropyl methylcellulose.

Embodiment 3

[0049] A high-temperature leveling agent for polyester fibers, made from the following raw materials:

[0050] 1.2 parts polyglyceryl monostearate,

[0051] 0.2 parts of zinc acetate,

[0052] 1 part dodecyltrimethylammonium chloride,

[0053] 80 parts leveling agent,

[0054] 0.1 part magnesium acetate,

[0055] 12 parts polyamide,

[0056] 0.3 parts calcium acetate,

[0057] 5 parts polyethylene glycol,

[0058] 0.2 parts tin acetate,

[0059] 4.5 parts ethylene glycol,

[0060] 3 parts dimethyl terephthalate,

[0061] 1 part hydroxypropyl methylcellulose.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high temperature dye leveler for polyester fibers, which is composed of the following raw materials in parts by weight: 1 to 2 parts of polyglycerol monostearate, 0.2 part of zinc acetate, 1 part of dodecyl trimethyl ammonium chloride, 80 parts of dye leveler, 0.1 part of magnesium acetate, 12 parts of polyamide, 0.3 part of calcium acetate, 5 parts of polyethylene glycol, 0.2 part of tin acetate, 4.5 parts of glycol, 3 parts of dimethyl terephthalate, and 1 part of carboxyl propyl methyl cellulose. The high temperature dye leveler is used for polyester fibers, enables the fabric made of the dyed polyester fibers to have a more uniform and brighter color and luster, has a very good dye leveling effect, and moreover can improve the fluffy and soft touch-feel, anti static performance, smoothness, and hydrophilicity of polyester fibers.

Description

technical field [0001] The invention relates to a high-temperature leveling agent for polyester fibers. Background technique [0002] The existing high-temperature leveling agents are not ideal for dyeing polyester fabrics. Contents of the invention [0003] The purpose of the present invention is to provide a high-temperature leveling agent for polyester fibers, which not only makes the fabric color of polyester fibers dyed more uniform and bright, has good leveling effect, but also can improve the color and luster of polyester fibers. Fluffy and soft, antistatic, smooth and hydrophilic. [0004] In order to achieve the above object, the technical solution of the present invention is to design a high-temperature leveling agent for polyester fibers, which is made of the following raw materials: [0005] 1~2 parts of polyglycerol monostearate, [0006] 0.2 parts of zinc acetate, [0007] 1 part dodecyltrimethylammonium chloride, [0008] 80 parts leveling agent, [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06P1/613D06P1/653D06P1/66D06P1/52D06P1/651D06P1/50D06P3/52
Inventor 严佳
Owner CHANGSHU MIAOQUAN SHENGDA AUX FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap