Molten steel dephosphorizing agent and molten steel dephosphorizing method

The technology of a molten steel dephosphorization agent and a water dephosphorization agent is applied in the field of molten steel dephosphorization agent, which can solve the problems of low dephosphorization rate and the like, and achieve the effect of improving the dephosphorization rate.

Active Publication Date: 2014-09-17
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to overcome the defect that the dephosphorization rate is low when the molten steel is dephosphorized by the existing method, and to provide a new molten steel dephosphorization agent and to use the molten steel dephosphorization agent under a specific argon blowing intensity. The method of carrying out dephosphorization of molten steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] This embodiment is used to illustrate the molten steel dephosphorization agent and the method for molten steel dephosphorization provided by the present invention.

[0037] In a factory with a 210t converter and a steel tapping capacity of 210t, the measured oxygen activity in molten steel is 900ppm, and the phosphorus content in molten steel is 0.025% by weight. During the tapping process of the converter, add the molten steel dephosphorization agent 7kg / t steel along with the steel flow. The molten steel dephosphorization agent contains lime and sodium carbonate, and the content of lime is 82.5% by weight, and the content of sodium carbonate is 17.5% by weight. Move the molten steel after adding the molten steel dephosphorization agent to the LF furnace for dephosphorization. In the LF process, turn on the electric heating process to control the temperature of the molten steel at 1550°C to melt slag, and the intensity of argon blowing is 100Nm 3 / h·ton of molten stee...

Embodiment 2

[0039] This embodiment is used to illustrate the molten steel dephosphorization agent and the method for molten steel dephosphorization provided by the present invention.

[0040] In a factory with a 210t converter and a steel tapping capacity of 210t, the measured oxygen activity in molten steel is 800ppm, and the phosphorus content in molten steel is 0.020% by weight. During the tapping process of the converter, 8kg / t of molten steel dephosphorization agent is added along with the steel flow. The molten steel dephosphorization agent contains lime and sodium carbonate, and the content of lime is 81% by weight, and the content of sodium carbonate is 19% by weight. Move the molten steel after adding the molten steel dephosphorization agent to the LF furnace for dephosphorization. In the LF process, turn on the electric heating process to control the temperature of the molten steel at 1580°C to melt slag, and the intensity of argon blowing is 120Nm 3 / h·ton of molten steel, the...

Embodiment 3

[0042] This embodiment is used to illustrate the molten steel dephosphorization agent and the method for molten steel dephosphorization provided by the present invention.

[0043] In a factory with a 210t converter and a steel tapping capacity of 210t, the measured oxygen activity in molten steel is 1000ppm, and the phosphorus content in molten steel is 0.022% by weight. During the tapping process of the converter, add molten steel dephosphorization agent 6kg / t steel along with the steel flow. The molten steel dephosphorization agent contains lime and sodium carbonate, and the content of lime is 85% by weight, and the content of sodium carbonate is 15% by weight. Move the molten steel after adding the molten steel dephosphorization agent to the LF furnace for dephosphorization. In the LF process, turn on the electric heating process to control the temperature of the molten steel at 1570°C to melt slag, and the intensity of argon blowing is 80Nm 3 / h·ton of molten steel, the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a molten steel dephosphorizing agent and a molten steel dephosphorizing method. The molten steel dephosphorizing method comprises the steps of enabling molten steel to be dephosphorized to be in contact with the molten steel dephosphorizing agent and transferring a contact product to an LF to dephosphorize in the steel tapping process of a converter, and slagging off after the dephosphorization operation is finished, wherein the molten steel dephosphorizing agent contains lime and sodium salt, the particle size of lime is smaller than 30mm, the particle sizes of at least 80wt% of particles in lime range from 5mm to 20mm, and argon blowing strength in the LF is at least 60Nm<3> / h.ton of molten steel. When the molten steel dephosphorizing agent provided by the invention is used for dephosphorizing under the specific argon blowing strength, the content of phosphorus in molten steel can be remarkably reduced, the dephosphorizing rate of molten steel can be increased, and therefore, the molten steel dephosphorizing agent has extremely wide industrial application prospect.

Description

technical field [0001] The invention relates to a molten steel dephosphorization agent and a method for using the molten steel dephosphorization agent to dephosphorize molten steel. Background technique [0002] Harmful impurities such as phosphorus and sulfur in steel are directly related to the performance of steel, and the presence of phosphorus in steel will reduce the plasticity of steel. When the phosphorus content in the steel is high, the steel is prone to "cold brittleness". In metallurgical production, the plasticity and toughness of the steel will be improved by reducing the phosphorus content in the steel, which can greatly improve the mechanical properties of the steel. . [0003] With the development of the economy, modern society has increasingly higher requirements on the performance of steel materials, which means that the control of impurity content in steel is becoming more and more strict. It is an important task for iron and steel enterprises to strive...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C21C7/064
Inventor 梁新腾曾建华李扬洲龚洪君杨森祥杨晓东喻林陈均何为陈路
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP