High-strength bainite steel rail and production method thereof

A production method and bainite technology, applied in furnaces, heat treatment equipment, heat treatment furnaces, etc., can solve problems such as cracks, wear to the limit, peeling off blocks, etc., and achieve excellent mechanical properties, good strength and toughness matching, and low alloy content Effect

Active Publication Date: 2014-10-08
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP +1
View PDF5 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, pearlitic rails also have certain deficiencies, such as low contact fatigue strength at the same strength level, and the rail head is prone to peeling off pieces, cracks, nuclear damage and other damages under the reciprocating stress of the wheels, which is not conducive to the development of railway longevity , especially in recent years, with the continuous increase of railway traffic density and vehicle axle load, the service environment of rails has become more and more harsh, and some road sections, especially curved parts, have been in servi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength bainite steel rail and production method thereof
  • High-strength bainite steel rail and production method thereof
  • High-strength bainite steel rail and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] In the following, a high-strength bainitic steel rail and its production method in the present invention will be described in detail with reference to examples.

[0027] The embodiment and comparative example of the present invention select the chemical composition of six groups of bainite rails in Table 1 and Table 2 respectively. Wherein, the comparative example is the chemical composition of the bainite rail in the prior art.

[0028] Table 1 Chemical composition of six groups of examples

[0029]

[0030] Continued Table 1

[0031]

[0032] Table 2 Chemical composition of comparative examples

[0033]

[0034] The steel slabs containing the components described in the examples and comparative examples were all rolled into 60kg / m rails, and the corresponding serial numbers adopted the same accelerated cooling start and finish cooling temperatures within the error range as shown in Table 3.

[0035] Six groups of embodiments and comparative examples proces...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a steel rail material and in particular relates to a high-strength bainite steel rail and a production method thereof, which solve the technical problems. The production method comprises the following steps: heating steel containing 0.15wt%-0.30wt% of C, 1.00wt%-1.80wt% of Si, 1.50wt%-2.50wt% of Mn, 0.20wt%-0.60wt% of Cr, 0.05wt%-0.10wt% of Mo and the balance of Fe, rolling the heated steel into a steel rail with needed section, utilizing waste heat of the steel rail, performing accelerated cooling on the rail head of the steel rail at a cooling speed of 3.0-6.0 DEG C/s when naturally cooling the tread surface of the rail head to 450-500 DEG C, stopping accelerated cooling when cooling the center of the tread surface of the rail head to 220-300 DEG C, and performing air-cooling to room temperature to obtain complex phase steel with carbide-free bainite, a small quantity of martensite and a small quantity of residual austenite. The steel is excellent in wear resistance and applicable to heavy haul railway.

Description

technical field [0001] The invention relates to a rail material, in particular to a high-strength bainite rail and a production method thereof. Background technique [0002] The rapid development of railway technology puts forward higher requirements for the service performance of rails. At present, my country's railway rails are mainly pearlite series carbon rails with a carbon content of 0.60% to 0.85%, microalloyed rails and high-strength heat-treated rails, and a small amount of bainite rails are also used. Pearlitic steel rail has the characteristics of simple production process, low production cost, stable structure and performance. However, pearlitic rails also have certain deficiencies, such as low contact fatigue strength at the same strength level, and the rail head is prone to peeling off pieces, cracks, nuclear damage and other damages under the reciprocating stress of the wheels, which is not conducive to the development of railway longevity , especially in re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/38C22C38/34C22C38/22C21D9/04
Inventor 韩振宇邹明郭华汪渊李大东邓勇王春建袁俊
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products