Crackle paint for spray-coating glass and use thereof

A technology for crack paint and glass, applied in the coating and other directions, can solve the problems of difficult to apply glass surface, difficult to adhere to glass surface, not good enough, etc., to achieve the effect of simple construction, beautiful cracks, increased consistency and adhesion

Inactive Publication Date: 2014-10-15
陈湛玲
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But in the prior art, crackle paint is mainly used on ceramic surface, is difficult to be applied to glass surface, and its reason mainly is that existing crackle paint is difficult to adhere on glass surface, and the effect of generating crackle is not good enough either.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Crackle paint for spray-coating glass and use thereof
  • Crackle paint for spray-coating glass and use thereof
  • Crackle paint for spray-coating glass and use thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] The crackle paint that is used for glass spraying consists of the following components by weight percentage:

[0027]

[0028] Among them, the role of nitrocellulose is to provide proper adhesion and film performance for cracked paint.

[0029] The role of calcium carbonate is to promote cracking of the paint film.

[0030] The function of fumed silica is to prevent the precipitation of fillers and pigments.

[0031] The functions of butyl acetate and xylene are to dissolve nitrocellulose, help the pigment to disperse, facilitate film formation and adjust the drying speed.

[0032] Polysiloxane-polyether copolymers are used as defoamers.

[0033] Aminosilane coupling agents are used as adhesion promoters.

[0034] The role of zinc stearate is to improve cracking performance.

[0035] The present invention also provides a method for preparing the crack paint used for glass spraying, comprising the following steps: stirring the nitrocellulose in a mixer at a low sp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses crackle paint for spray-coating glass and a use thereof. The crackle paint comprises nitrocotton, a pigment, a filling material, fumed silica, butyl acetate, a polysiloxane-polyether copolymer, an aminosilane coupling agent, xylene and zine stearate according to a weight percentage. Through adjustment of a component ratio and a construction technology, crackle paint denseness and adhesion are improved so that the crackle paint can well adhere to the glass surface. The crackle paint can be used simply and can produce beautiful cracks.

Description

technical field [0001] The invention relates to the field of decorative paints, in particular to a crack paint used for glass spraying, a preparation method and a construction method thereof. Background technique [0002] Crackle paint can produce beautiful and varied crackles on the surface of decorations, which is of great ornamental value. But in the prior art, crackle paint is mainly used in ceramic surface, is difficult to be applied to glass surface, and its reason mainly is that existing crackle paint is difficult to adhere on glass surface, and the effect of generating crackle is also not good enough. Contents of the invention [0003] The object of the present invention is to overcome above-mentioned defective of prior art, provide the crack paint that is used for glass spraying. To achieve the above object, the present invention adopts the following technical solutions: [0004] The crackle paint that is used for glass spraying is characterized in that, by weig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D101/18C09D5/28C03C17/00
Inventor 陈湛玲
Owner 陈湛玲