A kind of duplex stainless steel forging molding process

A duplex stainless steel, forging forming technology, applied in the field of forging, can solve the problems of crack propagation, high hardness and easy cracking, easy cracking, etc.

Active Publication Date: 2016-05-25
WUXI PAIKE HEAVY CASTING & FORGING
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the above-mentioned existing problems, the applicant has made researches and improvements, and provides a duplex stainless steel forging forming process, which effectively solves the problems of easy cracking of duplex stainless steel before forging, during forging, crack propagation and high hardness after forging. cracking problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of duplex stainless steel forging molding process
  • A kind of duplex stainless steel forging molding process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A duplex stainless steel forging forming process, comprising the following steps:

[0021] The first step: inspect and cut the duplex stainless steel raw materials to obtain a 2.5t square steel ingot with a riser.

[0022] Step 2: Put the steel ingot into a furnace at 450°C to heat and keep it warm for 4 hours, then use 6.5 hours to raise the temperature of the steel ingot at 450°C to 1050°C at a rate of 100°C / h, and keep it warm for 4 hours;

[0023] Step 3: Take 2.5 hours to raise the temperature of the steel ingot at 1050°C to 1250°C at a rate of 100°C / h, and keep it warm for 3.5 hours.

[0024] Step 4: Upsetting the steel ingot vertically, pause for 2s every time the upper anvil of the press is pressed down by 35mm, round the upper anvil of the press once every time it is pressed down by 150mm, and then continue upsetting to the required size Φ810*290 (diameter*height).

[0025] Step 5: Put the steel ingot obtained from the forging step in the fourth step into the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a duplex stainless steel forging and molding process. The heating time and heat preservation time are improved before forging, so that separation of a brittle precipitated phase of the duplex stainless steel is avoided, and trace elements in the alloy are homogenized. In the forging process, the rolling reduction of a forging machine is controlled, so that the stress of the duplex stainless steel is timely released at a high temperature. In addition, rounding once is performed when rolling down once by 100-150mm is performed in the upsetting process, so that the bulging condition occurring in the forging process is effectively eliminated. Therefore, the stress tensioned by the outer circle of the duplex stainless steel is pressure stress, and cracks are difficultly caused.

Description

Technical field [0001] The present invention relates to a forging method, and in particular to a forging process of duplex stainless steel (F53). Background technique [0002] Duplex Stainless Steel (DSS) refers to stainless steel with ferrite and austenite each accounting for about 50%. Generally, the content of the smaller phase needs to be at least 30%. In the case of low C content, the Cr content is 18%~28% and the Ni content is 3%~10%. Compared with austenitic stainless steel, duplex stainless steel has high strength and significantly improved resistance to intergranular corrosion and chloride stress corrosion. Duplex stainless steel has excellent pitting corrosion resistance and is also a nickel-saving stainless steel. Its main feature is that the yield strength can reach 400-550MPa, which is twice that of ordinary stainless steel, so it can save materials and reduce equipment manufacturing costs. At present, in the forging process of existing duplex stainless steel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D8/00
Inventor 许亮刘智李湘军刘其源程文虎韩长信
Owner WUXI PAIKE HEAVY CASTING & FORGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com