A kind of preparation method taking polymethyl methacrylate as matrix coumarin film

A technology of polymethyl methacrylate and methyl coumarin, which is applied in the direction of chemical instruments and methods, luminescent materials, etc., can solve the problems of changing luminescence wavelength, poor film uniformity, and influence of research results, etc., and achieve high light transparency , good film-forming performance and simple preparation method

Inactive Publication Date: 2017-09-01
CHONGQING UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although there are related introductions on the preparation of thin films, the existing thin films generally suffer from poor uniformity of film formation, and the luminous wavelength will be changed to varying degrees after forming, so the research on luminous properties based on such thin films will have an impact on the research results

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method taking polymethyl methacrylate as matrix coumarin film
  • A kind of preparation method taking polymethyl methacrylate as matrix coumarin film
  • A kind of preparation method taking polymethyl methacrylate as matrix coumarin film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) Dissolving 7-hydroxy-4-methylcoumarin

[0025] The specific process of dissolution is: add 0.0181 g of 7-hydroxy-4-methylcoumarin into a clean and dry volumetric flask, then add 100 ml of absolute ethanol solvent, and keep stirring until it is completely dissolved, and the molar concentration is 1.0x10 -3 mol / L 7-hydroxy-4-methylcoumarin absolute ethanol solution.

[0026] (2) Dissolving polymethyl methacrylate

[0027] The specific process of dissolution is: add 0.4987 g of polymethyl methacrylate into a clean and dry test tube, then add 10 ml of tetrahydrofuran, and keep stirring at 60 degrees Celsius until it is completely dissolved to obtain polymethyl methacrylate with a mass concentration of 5%. methyl acrylate tetrahydrofuran solution.

[0028] (3) Mix 7-hydroxy-4-methylcoumarin / polymethyl methacrylate solution

[0029] The specific process of mixing is: use a micro-sampler to measure 25 ul of the 7-hydroxy-4-methylcoumarin absolute ethanol solution obtai...

Embodiment 2

[0035] (1) Dissolving 7-hydroxy-4-methylcoumarin

[0036] The specific process of dissolution is: add 0.0437 g 7-hydroxy-4-methylcoumarin into a clean and dry volumetric flask, then add 250 ml of dichloromethane solvent, and keep stirring until it is completely dissolved, and the molar concentration is 1.0x10 -3 mol / L solution of 7-hydroxy-4-methylcoumarin in dichloromethane.

[0037] (2) Dissolving polymethyl methacrylate

[0038] The specific process of dissolution is: add 1.0013 g of polymethyl methacrylate into a clean and dry test tube, then add 20 ml of tetrahydrofuran, and keep stirring at 50 degrees Celsius until it is completely dissolved to obtain polymethyl methacrylate with a mass concentration of 5%. methyl acrylate tetrahydrofuran solution.

[0039] (3) Mixing 7-hydroxy-4-methylcoumarin / polymethyl methacrylate solution

[0040] The specific process of mixing is: use a micro-sampler to measure 10 ul of the 7-hydroxy-4-methylcoumarin dichloromethane solution ob...

Embodiment 3

[0044] (1) Dissolving 7-hydroxy-4-methylcoumarin

[0045] The specific process of dissolution is: add 0.0171 g of 7-hydroxy-4-methylcoumarin into a clean and dry beaker, then add 100 ml of tetrahydrofuran solvent, and keep stirring until it is completely dissolved to obtain a molar concentration of 1.0×10 -3 mol / L solution of 7-hydroxy-4-methylcoumarin in tetrahydrofuran.

[0046] (2) Dissolving polymethyl methacrylate

[0047] The specific process of dissolution is: add 0.5002 g of polymethyl methacrylate into a clean and dry test tube, then add 10 ml of chloroform, and keep stirring at 60 degrees Celsius until it is completely dissolved to obtain polymethyl methacrylate with a mass concentration of 5%. chloroform methyl acrylate solution.

[0048] (3) Mix 7-hydroxy-4-methylcoumarin / polymethyl methacrylate solution

[0049] The specific process of mixing is: use a micro-injector to measure 50 ul of 7-hydroxy-4-methylcoumarin tetrahydrofuran solution obtained in step (1) an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a coumarin film with polymethyl methacrylate as the matrix. 1) preparing 7-hydroxy-4-methyl coumarin solution and polymethyl methacrylate solution respectively; 2. ) Prepare a mixed solution of 7‑hydroxy‑4‑methylcoumarin / polymethyl methacrylate; 3) Use a measuring tool to directly drop or spin coat the mixed solution obtained in step 2) on a clean and dry glass or quartz sheet , and in the atmosphere or in a vacuum environment, dry at 25-80 degrees Celsius to obtain a concentration of 1.0x10-5 mol / g~1.0x10-4 mol / g of 7-hydroxy-4-methylcoumarin / polyformazine Methyl acrylate film. The preparation method forms a uniform film, has little change to the luminous wavelength, and is more conducive to the research on the luminous performance of the material. The preparation method is simple, the conditions are mild, easy to operate and control, and is suitable for actual production.

Description

technical field [0001] The invention relates to the research on coumarin light-emitting technology, in particular to a method for preparing a coumarin film with polymethyl methacrylate as a matrix, and belongs to the field of organic photoelectric technology. Background technique [0002] Organic light-emitting materials have received continuous and focused attention and research in the fields of display and lighting due to their wide source of materials, low price, excellent optoelectronic properties, and outstanding characteristics such as flexibility and large-area preparation. To achieve full color display and white lighting, blue light is essential. Compared with green and red light materials, the research on blue light materials has been in a relatively backward state, which is one of the important factors restricting the commercial application of organic electroluminescence. [0003] Coumarin is a general term for compounds whose parent ring structure is benzoa-pyron...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J5/18C08L33/12C08K5/1545C09K11/06
Inventor 黄杰
Owner CHONGQING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com