A kind of positive lead paste for agm start-stop battery and preparation method thereof

A positive electrode paste and storage battery technology, which is applied in the field of positive electrode paste for AGM start-stop batteries and its preparation, can solve problems such as fluctuations in fuel economy, achieve enhanced adhesion effects, excellent adhesion performance, and simple and easy-to-control processes Effect

Active Publication Date: 2016-06-29
CAMEL GRP XIANGYANG BATTERY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to different working conditions, the fuel economy of idling start and stop fluctuates, but it can basically achieve 5%-10% fuel saving ability, which has a significant effect on reducing emissions and protecting the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of positive lead paste for agm start-stop battery and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A positive lead paste for AGM start-stop batteries, comprising the following components in parts by weight: 700kg of lead powder, 1kg of polyester fiber, 0.1kg of glass fiber, 8kg of 4BS seed crystals, 120kg of red lead, 60kg of sulfuric acid and 90kg of pure water;

[0036] Among them, the size range of polyester fiber and glass fiber is 1mm-2mm;

[0037] The density of sulfuric acid is 1.35-1.45g / cm 3 , the iron content in sulfuric acid is not more than 1ppm;

[0038] The iron content in the lead powder is not more than 10ppm;

[0039] Described lead powder is the lead powder containing PbO, and the content that PbO accounts for lead powder is 70wt%;

[0040] According to the proportioning of above-mentioned positive electrode lead paste, make following preparation:

[0041] 1) Add red lead, polyester fiber, glass fiber and 4BS seeds:

[0042] Weigh an appropriate weight of red lead, polyester fiber, glass fiber and 4BS seed crystals, add to the paste equipment an...

Embodiment 2

[0053] A positive lead paste for an AGM start-stop battery, comprising the following components in parts by weight: 800kg of lead powder, 0.4kg of polyester fiber, 1kg of glass fiber, 3.5kg of 4BS seed crystal, 85kg of red lead, 65kg of sulfuric acid and 82kg of pure water;

[0054] Among them, the size range of polyester fiber and glass fiber is 2mm-4mm;

[0055] The density of sulfuric acid is 1.35-1.45g / cm 3 , the iron content in sulfuric acid is not more than 1ppm;

[0056] The iron content in the lead powder is not more than 10ppm;

[0057] Described lead powder is the lead powder containing PbO, and the content that PbO accounts for lead powder is 73wt%;

[0058] According to the proportioning of above-mentioned positive electrode lead paste, make following preparation:

[0059] 1) Add red lead, polyester fiber, glass fiber and 4BS seeds:

[0060] Weigh an appropriate weight of red lead, polyester fiber, glass fiber and 4BS seed crystals, add to the paste equipment and...

Embodiment 3

[0071] A positive lead paste for an AGM start-stop battery, comprising the following components in parts by weight: 900kg of lead powder, 0.1kg of polyester fiber, 1kg of glass fiber, 50kg of red lead, 80kg of sulfuric acid and 70kg of pure water;

[0072] Among them, the size range of polyester fiber and glass fiber is 4mm-6mm;

[0073] The density of sulfuric acid is 1.35-1.45g / cm 3 , the iron content in sulfuric acid is not more than 1ppm;

[0074] The iron content in the lead powder is not more than 10ppm;

[0075] Described lead powder is the lead powder containing PbO, and the content that PbO accounts for lead powder is 76wt%;

[0076] According to the proportioning of above-mentioned positive electrode lead paste, make following preparation:

[0077] 1) Add red lead, polyester fiber, glass fiber and 4BS seeds:

[0078] Weigh an appropriate weight of red lead, polyester fiber, glass fiber and 4BS seed crystals, add to the paste equipment and mix and stir evenly to o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of lead accumulators, and specifically discloses a positive lead paste for AGM start-stop accumulators and a preparation method thereof. The positive lead paste contains the following ingredients in parts by weight: 70-90 parts by weight of lead powder, 0.01-0.1 polyester fiber, 0.01-0.1 glass fiber, 0-0.8 4BS seed crystal, 5-12 red lead, 6-8 sulfuric acid and Pure water 7-9. The positive electrode paste can greatly improve the cycle life of the AGM start-stop battery, especially the 50% DOD cycle life, and slow down the muddy failure of the positive electrode paste during the use of the start-stop battery.

Description

technical field [0001] The invention belongs to the technical field of lead storage batteries, and in particular relates to a positive lead paste for AGM start-stop storage batteries and a preparation method thereof. Background technique [0002] With the attention of various countries on climate change and the gradual improvement of people's awareness of environmental protection, the voice of reducing vehicle exhaust emissions is also getting higher and higher. Pollutants emitted by motor vehicles mainly include hydrocarbons (HC), nitrogen oxides (NOx), carbon monoxide (CO), particulates (PM) and other harmful substances, which will have a direct impact on global climate change, environmental pollution, and human health. Reducing vehicle exhaust emissions has basically become the common understanding of the world's major economies. [0003] The micro-hybrid idling start-stop car has obvious practical significance in terms of saving fuel, reducing greenhouse gas, and toxic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/57H01M4/14H01M4/16H01M4/62
CPCH01M4/14H01M4/16H01M4/57H01M4/62Y02E60/10
Inventor 刘小峰孟刚徐建刚王天成陈顺宏夏诗忠
Owner CAMEL GRP XIANGYANG BATTERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com