Carbon dioxide arc welding wire with small diameter of 1.6 mm and high alloy content
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A carbon dioxide and gas protection technology, applied in welding medium, welding equipment, metal processing equipment, etc., can solve the problems of single formula, prone to spatter, reduce welding repair effect, etc., to achieve the effect of high alloy content and wide range of applications
Inactive Publication Date: 2015-12-30
SHANGHAI SMILE SPECIAL ALLOY MATERIALS
View PDF7 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the disadvantage of flux-cored wire is that spatter is prone to occur during welding, which reduces the welding repair effect; at the same time, the single formula of traditional flux-cored wire cannot be used in extreme environments and high-strength contact occasions
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
example 1
[0011] A carbon dioxide gas shielded welding wire for blast furnaces in steel mills;
[0012] It consists of a 1.6mm wire sheath and a flux core which includes the following components: 4% C, 1.5% Si, 1.0% Mn, 22% Cr, 1.5% Ni, 3.5% Mo, 2% Co, 3.5% Nb, 1.5% V, 1.5% W, 3.5% Ti; the rest is B.
[0015] A carbon dioxide gas shielded welding wire used in cement mill grinding;
[0016] It includes a 1.6mm welding wire sheath and a flux core, which includes the following components: 5% C, 1.5% Si, 1.0% Mn, 22% Cr, 7% V, 7% Ti, and the rest is b.
[0019] A carbon dioxide gas shielded welding wire for oil drilling valves;
[0020] It includes a 1.6mm welding wire sheath and a flux core, which includes the following components: 1.0% C, 1.2% Si, 17% Mn, 12% Cr, 7% Ni, 5% Co, and the rest is b.
[0021] It has the advantages of corrosion resistance, high pressure resistance and high strength.
[0022] The present invention adopts the above formula, which contains various alloy elements and high alloy content, and is especially suitable for occasions requiring high temperature resistance, corrosion resistance, wear resistance and impact resistance, so that the flux cored wire can be used more widely.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention relates to a carbon dioxidearc welding wire with the small diameter of 1.6 mm and the high alloy content. The welding wire comprises 1.6-mm welding wire skin and a flux core. The welding wire is characterized in that the flux core is prepared from 1.5%-6% of C, 0.5%-2% of Si, 0.5%-20% of Mn, 10%-25% of Cr, 0%-8% of Ni, 0%-5% of Mo, 0%-7% of Co, 0%-5% of Nb, 0%-10% of V, 0%-2% of W, 0%-10% of Ti and the balance B. According to the carbon dioxidearc welding wire with the small diameter of 1.6 mm and the high alloy content, by means of the formula, multiple alloy elements are contained, the alloy content is high, the welding wire is especially suitable for the occasions needing the high temperature resistance, corrosion resistance, abrasion resistance and impact resistance, and the usage occasion of the flux core welding wire is wider.
Description
technical field [0001] The invention relates to the field of welding wire, in particular to a 1.6mm fine-diametercarbon dioxide gas shielded welding wire with high alloy content. Background technique [0002] Flux-cored welding wire containing alloys can be used in the surface repair of mechanical equipment to enhance the service life of mechanical equipment, and can also be coated on the surface of mechanical equipment to increase the single service life of mechanical equipment and reduce maintenance flat rate. However, the disadvantage of flux-cored wire is that spatter is prone to occur during welding, which reduces the welding repair effect; at the same time, the single formula of traditional flux-cored wire cannot be used in extreme environments and high-strength contact occasions. Contents of the invention [0003] The purpose of the present invention is to provide a weld with high deposition rate, no spatter, good shape and excellent weld seam quality. No preheati...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More