An economical non-quenched and tempered micro-alloyed plastic mold steel plate and its manufacturing method

A plastic mold and microalloying technology, which is applied in the field of economical non-quenched and tempered microalloyed plastic mold steel plate and its manufacturing, can solve the problems of uneven microstructure and section hardness, high alloy cost and manufacturing cost, and reduce component segregation , reduce the cost of the alloy, and improve the effect of grain refinement

Active Publication Date: 2016-12-07
NANJING IRON & STEEL CO LTD +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to overcome the two major disadvantages of non-quenched and tempered plastic mold steel plate alloy cost and manufacturing cost, and uneven microstructure and section hardness, and provide an economical non-quenched and tempered micro-alloyed pre-hardened plastic Die steel plate and manufacturing method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An economical non-quenched and tempered micro-alloyed plastic mold steel plate and its manufacturing method
  • An economical non-quenched and tempered micro-alloyed plastic mold steel plate and its manufacturing method
  • An economical non-quenched and tempered micro-alloyed plastic mold steel plate and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] An economical method for manufacturing non-quenched and tempered micro-alloyed plastic mold steel plates, using converter smelting, LF+RH refining and pouring continuous casting slabs, the heating temperature of the slabs for pouring continuous casting slabs is 1200-1230°C, and the steel plates are subjected to controlled rolling The finish rolling temperature is 900-950°C, the final rolling temperature is 870-920°C, the steel plate is cooled after rolling, and tempered at 550-600°C after rolling; after tempering, the yield strength of the finished steel plate of plastic mold steel reaches 800 MPa or more , the section hardness is 310-340 HB, which meets the performance requirements of P20 pre-hardened steel plate. The specific steps and requirements are as follows:

[0030]1) Converter smelting, LF+RH refining, and continuous casting to obtain continuous casting slabs; the chemical composition of continuous casting slabs meets carbon: 0.32-0.40%, silicon: 0.20-0.50%, m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
hardnessaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an economical non-quenched and non-tempered micro-alloyed plastic die steel plate and a making method thereof. The economical non-quenched and non-tempered micro-alloyed plastic die steel plate comprises 0.32-0.40wt% of C, 0.20-0.50wt% of Si, 1.00-1.50wt% of Mn, 1.20-1.70wt% of Cr, 0.20wt% or less of Mo, 0.0025wt% or less of B, 0.03wt% or less of Ti, 0.03wt% or less of Nb, and the balance Fe. The making method comprises the following steps: carrying out converter smelting, LF+RH refining and continuous slab casting; heating the obtained slab at 1200-1230DEG C, carrying out precision rolling at 900-950DEG C, and carrying out finishing rolling at 870-920DEG C; carrying out controlled cooling after the steel plate rolling; and tempering the steel plate obtained after the controlled rolling and controlled cooling at 550-600DEG C to obtain the finished pre-hardened plastic die steel plate having a bainite structure. The yield strength, the normal temperature impact toughness and the cross section hardness of the steel plate are above 800MPa, above 20J and 310-350HB respectively. The making method is suitable for the production of pre-hardened plastic die steel plates with the specification of below 120mm from 320mm continuous casting blanks.

Description

technical field [0001] The invention relates to a plastic mold steel plate and a manufacturing method thereof, in particular to an economical non-tempered microalloyed plastic mold steel plate and a manufacturing method thereof. Background technique [0002] With the rapid development of my country's plastics industry, the market demand for plastic mold steel is increasing. In order to improve the service life of the mold, the processing accuracy of the mold and the quality of plastic products, the market has higher and higher requirements for the quality of mold steel. The traditional plastic mold steel means that the hot-processed steel plate is firstly quenched and tempered to reach the hardness range required by the plastic mold steel, and then mechanically processed, so as to avoid mold deformation and cracks caused by heat treatment. Although plastic mold steel has the above advantages, it also has the characteristics of high quenching crack sensitivity, high productio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/18C22C38/32C22C38/28C22C38/26C21D8/02
Inventor 张逖斯松华王新袁晓敏高飞李智慧
Owner NANJING IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com