Manufacturing process and application process of wall surface decoration coating material

A technology for wall decoration and manufacturing process, which is applied to the manufacturing process of wall decoration paint and its application technology field, can solve the problems of increasing decoration cost, labor cost, complicated construction, etc., and achieves strong coverage and color retention. Strong, convenient construction and smooth effect

Inactive Publication Date: 2016-01-27
安庆余
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the current existing paint products, after a long time of use, it is easy to have insufficient phenomena such as cracking, blooming, and alkali. Therefore, people usually decorate the wall with various ceramic tile products, such as imitation porcelain Jade porcelain, crystal porcelain, etc., which increase the cost of decoration, and at the same time, the construction is complicated, which also increases labor costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A preferred embodiment of the manufacturing process of a kind of wall decoration coating of the present invention, comprises the following steps:

[0014] (a) Mix 3.3kg of water, 50g of cellulose HPMC, 125g of styrene-acrylic emulsion, and 10ml of whitening liquid to prepare mixed solution A for later use;

[0015] (b) Mix 550g of water and 150g of cornstarch to make a mixed solution P, mix 260g of water and 30g of caustic soda to make a mixed solution Q, mix the mixed solution P and mixed solution Q together to get a mixed solution B standby;

[0016] (c) Mix 2.3kg of ash calcium, 6kg of heavy calcium and 125g of bentonite together to prepare mixed powder C for later use;

[0017] (d) After mixing the mixed solution A, mixed solution B and mixed powder C evenly together, the coating matrix can be obtained.

[0018] During actual construction, the application technology of above-mentioned embodiment, comprises the following steps:

[0019] (i) Prepare the paint matri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a manufacturing process and an application process of a wall surface decoration coating material. The manufacturing process comprises: mixing 3.3 kg of water, 50 g of cellulose HPMC, 125 g of a styrene-acrylic emulsion and 10 ml of a whitening liquid to prepare a mixed liquid A for spare; mixing 550 g of water and 150 g of corn starch to prepare a mixed liquid P, mixing 260 g of water and 30 g of caustic soda to prepare a mixed liquid Q, and mixing the mixed liquid P and the mixed liquid Q to prepare a mixed liquid B for spare; mixing 2.3 kg of ash calcium, 6 kg of calcium carbonate and 125 g of bentonite to prepare mixed powder C for spare; and uniformly mixing the mixed liquid A, the mixed liquid B and the mixed powder C so as to obtain the coating material matrix. According to the present invention, the manufacturing process is simple, the cost is stable and reliable, the effect of the ceramic tile can be achieved through the coating material coating, the wall surface decoration cost is effectively reduced, water washing thousands of times can be achieved, the pressing calendaring is easy and rapid, and the coating material is the ideal wall surface decoration coating material.

Description

technical field [0001] The invention relates to the technical field of wall coatings, in particular to a manufacturing process and application process of wall decorative coatings. Background technique [0002] In the known technical field, wall coatings are used to decorate and protect building walls, so that the building walls are beautiful and tidy, and can also protect the building walls and prolong their service life. In the current existing paint products, after a long time of use, it is easy to have insufficient phenomena such as cracking, blooming, and alkali. Therefore, people usually decorate the wall with various ceramic tile products, such as imitation porcelain Jade porcelain, crystal porcelain, etc., which increase the cost of decoration, and at the same time, the construction is complicated, which also increases labor costs. Contents of the invention [0003] The technical problem to be solved by the present invention is: to overcome the above problems, to p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/02C04B14/28
Inventor 安庆余
Owner 安庆余
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products