Novel waterproof wood material adhesive and preparation method thereof

A technology of wood adhesives and adhesives, applied in the preparation of animal glue or gelatin, adhesives, lignin adhesives, etc., can solve problems such as high cost, poor bonding strength, and poor waterproofness, and achieve Low cost, good water resistance, and enhanced adhesion

Inactive Publication Date: 2016-06-08
上海齐驭实业有限公司
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The products made by the above method either have poor bonding strength, poor water resistance, or high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The present invention is a urea-formaldehyde resin adhesive, which is produced by adding 0.3% liquid sodium carboxymethylcellulose or carboxymethyl cellulose to the E2 grade urea-formaldehyde resin adhesive with a solid content of 65% produced by Beijing Taier Chemical Co., Ltd. Obtained after the cellulose is stirred evenly.

Embodiment 2

[0023] The present invention is a urea-formaldehyde resin adhesive, which is prepared by adding 0.5% of liquid sodium carboxymethylcellulose or carboxymethyl to the E2 grade urea-formaldehyde resin adhesive produced by Beijing Taier Chemical Co., Ltd. with a solid content of 65%. Obtained after the cellulose is stirred evenly.

Embodiment 3

[0025] The present invention is a urea-formaldehyde resin adhesive, which is produced by adding 0.8% liquid sodium carboxymethylcellulose or carboxymethyl cellulose to the E2 grade urea-formaldehyde resin adhesive with a solid content of 65% produced by Beijing Taier Chemical Co., Ltd. Obtained after the cellulose is stirred evenly.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel waterproof wood material adhesive and a preparation method thereof. Sodium carboxymethylcellulose or carboxymethylcellulose or carboxymethyl starch accounting for 0.3-0.8% is added to the adhesive. The adhesive is urea resin adhesive, waterborne polyurethane adhesive, acrylic ester adhesive, epoxy resin adhesive, isocyanate adhesive, phenolic resin adhesive, soy-based adhesive, starch adhesive, lignin adhesive, tannin adhesive and the like. Liquid sodium carboxymethylcellulose and carboxymethylcellulose can be directly added to the adhesive; powdery sodium carboxymethylcellulose, carboxymethylcellulose and carboxymethyl starch are added together with the last batch of solid raw materials in the production process. The waterproof wood material adhesive is high in bonding strength, good in waterproofing performance and low in cost; when the adhesive is used for manufacturing fiberboards or plywood, the water absorption expansion coefficient of panels is kept between 0.5 mm and 0.8 mm, the waterproofing performance is improved, the bonding strength is improved, and the adhesive is particularly suitable for manufacturing fiberboards.

Description

technical field [0001] The invention belongs to the technical field of adhesives, and relates to a novel waterproof wood adhesive, in particular to a novel waterproof wood adhesive with good water resistance and low cost. Background technique [0002] Urea-formaldehyde resin adhesive is the most used type of adhesive, especially in the manufacture of various wood-based panels in the wood processing industry, urea-formaldehyde resin and its modified products account for about 90% of the total amount of adhesive. However, it is easy to decompose when encountering strong acid and strong alkali, poor weather resistance, poor initial viscosity, large shrinkage, high brittleness, water resistance, and easy aging. The wood-based panels produced by urea-formaldehyde resin have the problem of formaldehyde release in the process of manufacture and use. , so it must be modified. In other words, although the early urea-formaldehyde resin adhesive products were of good quality, they wer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J161/28C09J175/04C09J133/08C09J161/06C09J163/00C09J179/04C09J189/00C09J103/00C09J197/00C09J191/00
CPCC09J103/00C09J133/08C09J161/06C09J161/28C09J163/00C09J175/04C09J179/04C09J189/00C09J191/00C09J197/005C08L1/286C08L3/08
Inventor 宋振刚
Owner 上海齐驭实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com