A polymer waterproof material

A technology of polymer waterproofing and polymer colloid, which is applied in the direction of layered products, synthetic resin layered products, chemical instruments and methods, etc., can solve the problems of insufficient waterproof performance and low peel strength, and achieve excellent weather resistance and composition Effects that are uncomplicated and inexpensive to produce

Active Publication Date: 2018-03-23
上海远盛建筑防水材料厂 +1
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The inventor of the present application provides a polymer waterproof material, which has excellent peeling performance and waterproof performance, overcomes the defects of low peeling strength and insufficient waterproof performance of traditional asphalt-based waterproof materials, and is environmentally friendly and economical at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A polymer waterproof material
  • A polymer waterproof material
  • A polymer waterproof material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Example 1 , Preparation of polymer colloid

[0033] Put 30 parts of hot melt adhesive and 3 parts of naphthenic oil into the oxidation kettle according to the weight ratio, heat to 130 ° C, after the hot melt adhesive and naphthenic oil melt, stir evenly, then put 15 parts of white cement and 51.5 parts of quartz sand and 0.5 part of green pigment, the system was heated to 140° C., and stirred evenly to prepare polymer colloid.

Embodiment 2

[0034] Example 2 , Preparation of polymer colloid

[0035] Put 20 parts of hot melt adhesive and 6 parts of naphthenic oil into the oxidation kettle according to the weight ratio, heat to 110°C, after the hot melt adhesive and naphthenic oil melt, stir evenly, then add 11 parts of white cement and 62 parts of quartz sand and 1 part of green pigment, heat the system to 120°C, stir evenly, and prepare polymer colloid.

Embodiment 3

[0036] Example 3 , Preparation of polymer colloid

[0037] Put 48 parts of hot melt adhesive and 1.7 parts of naphthenic oil into the oxidation kettle according to the weight ratio, heat to 150 ° C, after the hot melt adhesive and naphthenic oil melt, stir evenly, then put 20 parts of white cement and 30 parts of quartz sand and 0.3 parts of green pigment, the system was heated to 160° C., stirred evenly, and the polymer colloid was prepared.

[0038] The specific formula of embodiment 1-3 polymer colloid is as shown in table 1:

[0039] Table 1 polymer colloid formula

[0040]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a polymer waterproof material, which comprises polymer colloid. The polymer colloid is obtained by mixing the following ingredients (by weight): 20-48 parts of hot melt adhesive, 1.7-5 parts of naphthenic oil, 10-20 parts of white cement, 30-60 parts of quartz sand and 0.3-1 part of green pigment. The polymer waterproof material also comprises a fetal membrane and an isolating membrane. The polymer colloid is uniformly dip-coated between the fetal membrane and the isolating membrane. The polymer waterproof material has excellent weatherability, peel strength and waterproofness, and can provide a skin-type waterproof barrier for building materials. Environmentally-friendly non-asphaltic base raw materials are adopted, and the ingredients are not complex. The preparation technology is simple, and production cost is low. The polymer waterproof material has economical and environmental-protection characteristics and has a wide prospect for large-scale industrial application.

Description

technical field [0001] The invention belongs to the field of waterproof materials, in particular, it relates to a polymer waterproof material. Background technique [0002] At present, my country's waterproof materials are still dominated by asphalt-based waterproof materials, accounting for 65% of all waterproof materials, polymer waterproof membranes account for about 15%, and other waterproof materials account for about 20%. Among them, polymer waterproof membrane is a typical new building waterproof material. Because of its excellent performance, in line with the purpose of building material innovation, and the rise of light steel structure buildings, it has developed very rapidly in recent years. [0003] In the prior art, on the one hand, the traditional asphalt-based waterproof materials have low peel strength and insufficient waterproof performance. With the prolongation of use time, their waterproof performance weakens; on the other hand, the use of asphalt-based ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04B32B27/06C04B111/27
CPCB32B27/06B32B2323/043C04B28/04C04B2111/27C04B2103/0045C04B24/00C04B14/06C04B14/307
Inventor 张文乐
Owner 上海远盛建筑防水材料厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com