High-throughout preparing device and preparing method for metal solidification samples

A metal solidification and preparation device technology, which is applied in the control of molten metal pouring from ladles, metal processing equipment, casting equipment, etc., can solve the problem of huge material gene pool, achieve simple and effective control of experimental variables, and accelerate the establishment of Effect

Active Publication Date: 2016-08-17
SHANGHAI UNIV
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the process of establishing the material gene bank, because there are many materials, the material gene bank that needs to be established is very large.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-throughout preparing device and preparing method for metal solidification samples
  • High-throughout preparing device and preparing method for metal solidification samples

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The preferred embodiments of the present invention are given below in conjunction with the accompanying drawings to describe the technical solution of the present invention in detail.

[0023] Such as figure 1 As shown, the high-throughput preparation device for metal solidification samples of the present invention includes a crucible 1, a resistance furnace 2, a stopper 3, a temperature measuring element 4, a slit-shaped nozzle 5, an array cooling platform 6, a mobile system 7, and a microcomputer control system , the crucible 1, the stopper rod 3 and the temperature measuring element 4 are all located in the resistance furnace 2, and the metal sample is smelted under temperature control; A thin layer of fluid flows out; the array cooling platform 6 is located directly below the slit-shaped nozzle 5, the array cooling platform 6 is connected to the mobile system 7 located at its bottom, and the microcomputer control system controls the resistance furnace 2, stopper rod...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-throughout preparing device and preparing method for metal solidification samples. The device comprises a crucible, a resistance furnace, a stopper, a temperature measurement element, a narrow seam type nozzle, an array cooling table, a moving system and a microcomputer control system, wherein the crucible, the stopper and the temperature measurement element are all positioned in the resistance furnace so as to carry out temperature-controlled smelting on metal samples; the bottom of the crucible is connected with the narrow seam type nozzle, and molten metal flows out of the narrow seam type nozzle and forms a thin layer of fluid; the array cooling table is positioned under the narrow seam type nozzle and is connected with the moving system positioned at the bottom of the array cooling table; and the microcomputer control system controls the resistance furnace, the stopper, the temperature measurement element and the moving system. The high-throughout preparing device and preparing method can be used for rapidly screening optimal technical parameters and solidification structures and are favorable to the rapid building of material gene banks.

Description

technical field [0001] The invention relates to a metal preparation device and method, in particular to a high-throughput preparation device and method for metal solidification samples. Background technique [0002] Material genetic engineering is a hotspot in current research. The database of materials, that is, the material gene library, is established by combining simulation and experiment methods, and materials can be quickly designed on this basis, which greatly shortens the research and development cycle and application cycle of materials. In the process of establishing the material gene bank, because there are many materials, the material gene bank to be established is very large. How to quickly and accurately establish is the key problem that needs to be solved at present. High-throughput methods provide a very efficient solution for the rapid establishment of gene banks for research materials. On the basis of setting a certain range for numerical calculation, hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22D37/00
CPCB22D37/00
Inventor 张云虎张亚博宋长江徐智帅仲红刚翟启杰
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap