Guided tissue regeneration composite membrane material and preparation method thereof

A technology of tissue regeneration and composite membrane, applied in medical science, surgery, etc., to achieve the effect of promoting periodontal ligament cell adhesion, promoting periosteum cell adhesion, and good biocompatibility

Active Publication Date: 2016-11-16
SHANGHAI NINTH PEOPLES HOSPITAL AFFILIATED TO SHANGHAI JIAO TONG UNIV SCHOOL OF MEDICINE
View PDF6 Cites 43 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Due to the defects of a single material and preparation technology, it is difficult to meet the requirements of the ideal GTR. Therefore, using appropriate preparation technology,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Guided tissue regeneration composite membrane material and preparation method thereof
  • Guided tissue regeneration composite membrane material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0033] Example one

[0034] In this embodiment, the present invention provides a method for preparing a double-layer guided tissue regeneration composite membrane material, which includes the following steps:

[0035] Prepare the loose layer of macromolecule polymer and phosphate inorganic substance in the bottom layer. The steps for preparing the macromolecular polymer / phosphate inorganic porous layer are described in detail below:

[0036] Step 1. Use template induction and self-assembly methods to synthesize phosphate inorganic compounds. The non-ionic block copolymer is used as a structure-directing agent and dissolved in deionized water, stirred with magnetic force until the solution is clear; adjust the pH value of the solution system to pH=1 with 37% concentrated hydrochloric acid, and stir for 2h until the solution becomes a white emulsion. Then add ethyl orthosilicate, calcium nitrate and triethyl phosphate into the solution reaction system, and then put them into the auto...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a guided tissue regeneration composite membrane material. The guided tissue regeneration composite membrane material is characterized by being in a double-layer membrane structure, wherein the double-layer membrane structure comprises a loose layer on the bottom layer and a compact layer on the upper layer. According to a second aspect, the invention provides a preparation method of the guided tissue regeneration composite membrane material. According to the guided tissue regeneration composite membrane material and the preparation method, the biological membrane material having the customized specification, having the tissue integration activity, and being capable of promoting the growth of the osteoblasts can be printed by adopting a three-dimensional printer, a material with the capacity of promoting the periodontal ligament cell adhesion and the periosteum cell adhesion is prepared by combining with the electrospinning technology, and a medicine having the antimicrobial activity is combined, therefore, the guided tissue regeneration composite membrane material has good biocompatibility, good bone repair function and good bacteria resisting function, and can be used for the periodontal guided tissue regeneration treatment and periosteum defect repair.

Description

technical field [0001] The invention relates to the field of medical biomaterials, in particular to a guided tissue regeneration composite membrane material and a preparation method thereof. Background technique [0002] In the late 1970s and early 1980s, Nyman, Lindhe, Karring, Gottlow and other scholars proposed a series of guided tissue regeneration (Guided Tissue Regeneration, hereinafter referred to as GTR) for the treatment of periodontal disease, the core of which is to use tissue to guide the regeneration membrane, namely Through the role of space barrier, the gingival epithelium and connective tissue are prevented from attaching to the root surface quickly during the healing process, so that the periodontal ligament cells with regenerative ability preferentially occupy the root surface and form new attachments, so as to achieve periodontal support tissue regeneration . Therefore, the guiding membrane is one of the crucial factors for GTR therapy. With the developm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L31/12A61L31/16A61L31/14
CPCA61L31/026A61L31/042A61L31/044A61L31/048A61L31/06A61L31/148A61L31/16A61L2300/404A61L2300/412A61L2300/414
Inventor 汤亭亭陆尔奕杨盛兵茅传圆
Owner SHANGHAI NINTH PEOPLES HOSPITAL AFFILIATED TO SHANGHAI JIAO TONG UNIV SCHOOL OF MEDICINE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap