Reinforced and scratch-resistant polypropylene material and preparation method thereof

A polypropylene material and polypropylene technology are applied in the field of scratch-resistant polypropylene materials and their preparation and enhancement, which can solve the problems of heavy odor, affecting indoor environment VOC, odor, etc., achieving simple preparation method, easy guarantee of material performance, Simple to use effects

Active Publication Date: 2016-11-23
HEFEI GENIUS NEW MATERIALS
View PDF10 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional anti-scratch agents are mainly erucamide substances and high polysiloxane substances. These two types of substances have their own disadvantages such as heavy odor. When polypropylene composite materials are used in automotive interior parts, there will be impact Indoor environment VOC, odor and other issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] 80 kg of polypropylene, 0.5 kg of phenolic heat stabilizer 1010, 0.5 kg of lubricant EBS, 20 kg of one-dimensional β-SiAlON, 0.2 kg of titanate coupling agent NDZ109, and 0.2 kg of white oil 36# at an aspect ratio of The 40:1 twin-screw extruder was melted, mixed and dispersed, and all the raw materials were blended and extruded to obtain the polypropylene compound of this example. The processing temperature during preparation was 200°C.

Embodiment 2

[0035] 85 kg of polypropylene, 0.5 kg of phenolic heat stabilizer 1010, 0.5 kg of lubricant zinc stearate, 0.3 kg of lubricant calcium stearate, 15 kg of one-dimensional β-SiAlON, 0.4 kg of silane coupling agent KH-550 , 0.3 kg of white oil 32# was melted, mixed and dispersed in a twin-screw extruder with a length-to-diameter ratio of 56:1. After all the raw materials were blended, extruded and granulated, the polypropylene compound of this embodiment was obtained. The processing temperature during preparation was 220°C.

Embodiment 3

[0037] 90 kilograms of polypropylene, 0.1 kilogram of phenolic heat stabilizer 1010 and 0.1 kilogram of heat stabilizer 168, 0.2 kilogram of silane coupling agent KH-570, 0.2 kilogram of white oil 15#, 10 kilograms of one-dimensional β-SiAlON in aspect ratio Melt, mix and disperse in a twin-screw extruder at a ratio of 35:1, and after all raw materials are blended, extruded and granulated, the polypropylene compound of this example is obtained. The processing temperature during preparation was 170°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention relates to a reinforced and scratch-resistant polypropylene material and a preparation method thereof, wherein the material is prepared from 70-95 parts of polypropylene, 30-5 parts of SiAlON, 0.1-0.5 part of a coupling agent, 0.1-1 part of a thermal stabilizer, 0-1 part of a lubricant, and 0-0.5 part of white oil, and the weight sum of the polypropylene and the SiAlON is 100 parts. According to the present invention, the one-dimensional beta-SiAlON adopted as the scratch-resistant agent is added to the polypropylene material so as to concurrently provide advantages of material scratch resistance enhancing and material strength increasing and overcome the disadvantage of the material scratch resistance reducing of the traditional reinforcing filling material; and the obtained reinforced and scratch-resistant polypropylene material is used in vehicle interior decoration materials, and does not have disadvantages of scratch-resistant agent precipitation, odor, appearance and the like compared to the traditional scratch-resistant agent adding material.

Description

technical field [0001] The invention relates to the technical field of polypropylene, in particular to a reinforced and scratch-resistant polypropylene material and a preparation method thereof. technical background [0002] Polypropylene material is widely used in interior and exterior parts of automobiles due to its advantages of low price and light weight. However, the scratch resistance of the polypropylene material itself is poor, especially the scratch resistance of the polypropylene material filled with talcum powder is even worse, and the material yields under the action of pressing force and sliding force or transverse (lateral) force, Ductile / brittle failure occurs resulting in scratches. In scratches, the uneven surface produces uneven light scattering and "scratch whitening", which limits the use of polypropylene materials in parts where scratch resistance is required. [0003] In order to solve this problem, a scratch-resistant agent is usually added to the po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L91/06C08K13/02C08K3/34C08K5/10C08K5/20C08K5/098
Inventor 杨桂生计娉婷
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap