A kind of laminating adhesive and preparation method thereof

A technology of adhesives and additives, applied in the direction of adhesives, polymer adhesive additives, adhesive additives, etc., can solve the problems of poor ink layer affinity, environmental pollution, poor fluidity, etc., and achieve improved adhesion, Cost reduction and ease of use

Active Publication Date: 2018-02-27
CHINA PETROLEUM & CHEM CORP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, most SBS laminating adhesives are solvent-based. Although the adhesion is good, a large amount of organic solvents will directly volatilize into the air during operation, causing environmental pollution and poisoning to the human body.
People find that SBS glue still has some shortcomings in use: (1) the peel strength of the laminated paper decreases rapidly; (2) the viscosity is high, the fluidity is poor, and the coating is difficult; (3) the affinity for the ink layer Poor performance, when the laminated paper is peeled off, the ink is difficult to remove, and the phenomenon of "light film" is easy to appear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of laminating adhesive and preparation method thereof
  • A kind of laminating adhesive and preparation method thereof
  • A kind of laminating adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Compound the modified SBS in Table 1 according to the laminating adhesive formula in Table 2, add modified SBS, tackifying resin and organic solvent into the container, and after fully dissolving, add emulsifier and deionized water to Cut emulsifier for emulsification to obtain water-emulsion laminating adhesive. The properties of the obtained water-emulsion laminating adhesive are shown in Table 3 below.

[0038] Table 1 Characteristic parameters of modified SBS

[0039] Sample serial number

corresponding sample

1#

S / B=3 / 7, Mn=89,000

2#

S / B=3 / 7, Mn=108,000

3#

S / B=3 / 7, Mn=127,000

4#

S / B=2 / 8, Mn=82,000

5#

S / B=2 / 8, Mn=104,000

6#

S / B=4 / 6, Mn=83,000

7#

S / B=4 / 6, Mn=105,000

[0040] Table 2 Formula composition of modified SBS water-emulsion laminating adhesive

[0041] components

parts by weight

Modified SBS

2 copies

Terpene resin

5 copies

Rosin r...

Embodiment 2

[0046] Except that modified SBS adopts 5# of Table 1 and emulsifier adopts anionic and nonionic emulsifier combination (SDBS+OP-10), others are the same as Example 1. The obtained laminating adhesive emulsion is a white uniform emulsion with a pH of 6.7, a viscosity of 265 at 25° C., a peel strength of 25, and the coating film has no foaming and a smooth plate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a laminating adhesive and a preparation method thereof. The laminating adhesive includes a matrix resin, a tackifying resin, an auxiliary agent and a solvent, wherein the matrix resin is a SBS three-block block with an amino group at one end and a carboxyl group at the other end. Copolymer, the laminating adhesive has the characteristics of good fluidity, strong cohesive force, and good ink affinity, which overcomes the poor affinity of the existing SBS adhesive to the ink layer, and the ink is difficult to remove when the laminating paper is peeled off. In the past, the defect of "light film" phenomenon is easy to appear, and the laminating adhesive is environmentally friendly, low in cost, and meets the requirements of industrial production and application.

Description

technical field [0001] The invention relates to a laminating adhesive and a preparation method thereof, belonging to the field of composite polymer materials. Background technique [0002] Lamination is a combination of plastic film coated with adhesive and paper printed matter after heating and pressure to form a paper-plastic product. It is one of the common post-press processing technologies for paper printed matter. The printed matter after lamination has a smoother and brighter surface due to the addition of a thin and transparent plastic film on the surface, which not only improves the gloss and fastness of the printed matter, but also prolongs the service life of the printed matter. Antifouling, abrasion resistance, folding resistance, chemical corrosion resistance and other protective effects. At present, common paper-plastic laminated packaging products include cartons, cartons, handbags, fertilizer bags, seed bags, self-adhesive labels, etc. According to differen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J153/02C09J11/08
Inventor 梁红文许安军刘先珍李望明蒋文英黄丽芳
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com