A kind of polymetallic complex dye sensitizer containing 8-hydroxyquinoline derivative and cu(ii) and its preparation method

A technology of dye sensitizers and metal complexes, applied in organic dyes, photosensitive devices, photovoltaic power generation, etc., can solve problems such as unsatisfactory effects, improve light absorption performance and carrier transport capacity, and expand conjugated π system, cost reduction and the effect of original resource constraints

Active Publication Date: 2018-12-14
XIANGTAN UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the main research is to use organic substances such as benzothiadiazole as the auxiliary electron acceptor A', but due to the influence of its electron-absorbing ability, coordination balance with the donor D and its stability, the effect is not very satisfactory.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polymetallic complex dye sensitizer containing 8-hydroxyquinoline derivative and cu(ii) and its preparation method
  • A kind of polymetallic complex dye sensitizer containing 8-hydroxyquinoline derivative and cu(ii) and its preparation method
  • A kind of polymetallic complex dye sensitizer containing 8-hydroxyquinoline derivative and cu(ii) and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A polymetallic complex PCZ-QCu containing 8-hydroxyquinoline derivatives and Cu(II).

[0026] A polymetallic complex PCZ-QCu with carbazole derivative as donor (D), 8-hydroxyquinoline derivative and Cu(II) complex as auxiliary electron acceptor A', and polymerization degree n of 11 , and its molecular structure is:

[0027]

[0028] The preparation method of above-mentioned polymetallic complex PCZ-QCu:

[0029] A: Preparation of 2,5-dibromo-3-[2-(8-hydroxyquinoline)-vinyl]thiophene: After weighing 5-formyl-8-p-toluenesulfonyloxyquinoline (3.15g , 10mmol) and 2,5-dibromo-3-bromomethyltriphenylphosphothiophene (5.97g, 10mmol), it was added respectively in the three-necked round bottom flask of 250ml, then poured into 100ml of absolute ethanol ( CH 3 CH 2 OH), stirred to dissolve, and then in N 2 Under protection, slowly add sodium ethylate solution (Na: 0.80g, 30ml absolute ethanol) dropwise to it through the constant pressure dropping funnel under ice bath, afte...

Embodiment 2

[0034] A polymetallic complex PIDT-QCu containing 8-hydroxyquinoline derivatives and Cu(II).

[0035] A kind of polymetallic with indaprodithiophene derivative (IDT) as donor D, 8-hydroxyquinoline derivative and Cu(II) complex as auxiliary electron acceptor A', and degree of polymerization n is 7 Complex PIDT-QCu, its molecular structure formula is:

[0036]

[0037] Synthesis of the above polymeric metal complex PIDT-QCu:

[0038] A: Consistent with the synthesis method of step A in Example 1;

[0039] B: consistent with the synthesis method of step B in Example 1;

[0040] C: Similar to step D in Example 1, except that the carbazole derivative (0.175g, 0.4mmol) is replaced by an indabrodithiophene (IDT) derivative (0.426g, 0.4mmol) to obtain a solid A kind of polymetallic complex PIDT-QCu 0.30g containing 8-hydroxyquinoline derivatives and Cu(II), the yield is 51%; FTIR (KBr, cm -1 ):3421(-OH), 2921, 2851(C-H), 2207(C≡N), 1650(C=O), 1591(C=C), 1540(C=N), 1093(C=N-Cu ...

Embodiment 3

[0042] The thermogravimetric curves (TGA) of polymetallic complex dyes PCZ-QCu and PIDT-QCu were measured respectively. Method: Q50 Thermogravimetric Analyzer, N 2 The test was carried out at a heating rate of 25°C / min under protection, and the test results were as follows: Figure 4 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a novel D-A'-PI-A polymer metal complex sensitizer (as shown in a formula I) taking 8-hydroxyquinoline derivative Cu (II) as an auxiliary electron acceptor, a preparation method of the sensitizer and application of the sensitizer to dye-sensitized solar cells. The sensitizer takes derivates of IDT (indacenodithiophene) or CZ (carbazole) as electron donors (D), 8-hydroxyquinoline derivative Cu (II) complexes serve as A' and pi bridges respectively, cyanoacrylate serves as an electron acceptor (A) and an anchor group, and Yamamoto polymerization is performed to obtain sensitizers PIDT-QCu and PCZ-QCu. The D-A'-PI-A sensitizer taking high-electrophilicity 8-hydroxyquinoline derivative Cu (II) complexes as the auxiliary electron acceptor A' is synthesized successfully. According to photovoltaic performance tests, the sensitizer is excellent in photovoltaic performance and thermal stability and has a promising application prospect.

Description

technical field [0001] The invention relates to a kind of D-A'-π-A type polymerized metal complex dye sensitizer with 8-hydroxyquinoline derivative and Cu(II) as auxiliary electron acceptor A' and its preparation method and application, which belongs to new Materials in the field of optoelectronic materials. Background technique [0002] Dye-sensitized solar cells are and O'Regan researched and invented in 1991. Its photovoltaic principle is as follows: under light, the thin film TiO is adsorbed on the FTO glass plate of the battery 2 The dye sensitizer molecules on the particle surface absorb light and change from the ground state to the excited state, because the excited state of the dye and the TiO 2 Energy level difference in conduction band, excited state electrons injected into TiO 2 conduction band, electrons pass through sensitized TiO 2 After the film is transferred to the FTO glass electrode, the electrons are transferred to the counter (positive) electrode o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G61/12C09B69/10H01G9/20
CPCY02E10/542
Inventor 钟超凡刘晔陈天祺廖艳龙祝春晓陈旭
Owner XIANGTAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More