Multi-colored peacock feather grain decoration ceramic tile and preparation method

A technology of peacock feathers and ceramic tiles, which is applied in the field of decorative tiles, can solve the problems of no glaze texture changes, etc., and achieve the effect of increasing detail changes, enhancing three-dimensionality and fidelity, and presenting realistic surface colors

Inactive Publication Date: 2017-02-22
SHAANXI UNIV OF SCI & TECH
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But this kind of brick is only innovated from the color of the surface, and there is no certain glaze texture change.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multi-colored peacock feather grain decoration ceramic tile and preparation method
  • Multi-colored peacock feather grain decoration ceramic tile and preparation method
  • Multi-colored peacock feather grain decoration ceramic tile and preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The preparation of the textured ceramic green body specifically includes: using a mold to press the ceramic green body, and trimming the surface of the ceramic green body to obtain a textured ceramic green body.

[0026] The mold is a mold with concave and convex grain lines similar to peacock feathers.

[0027] The preparation method of the blue glaze slurry is as follows: firstly, by mass parts, 55-70 parts of feldspar, 20-30 parts of quartz, 5-10 parts of calcite, 1-5 parts of talc and 2-5 parts of cobalt blue material Mix evenly to get the mixture, then add sodium tripolyphosphate and CMC to the mixture, mix evenly, finely grind to 250 mesh, prepare the specific gravity of the glaze slurry to be 1.6-1.7g / cm 3 , to get blue glaze slurry.

[0028] The additions of sodium tripolyphosphate and CMC are respectively 0.4% and 1% of the mixture quality.

[0029] Apply the blue glaze slurry evenly on the textured ceramic body, put it into the kiln and raise the temperature...

Embodiment 1

[0035] A method for preparing a color-changing peacock feather pattern decorative tile, the specific method is as follows:

[0036] 1) Preparation of textured ceramic body:

[0037] see figure 1 , using a ceramic mold 1 with concave-convex texture lines 2 similar to peacock feathers to press the ceramic body, and trimming the surface of the ceramic body to obtain a textured ceramic body 3;

[0038] 2) Preparation of blue glaze slurry:

[0039] By mass percentage, mix 55% feldspar, 30% quartz, 10% calcite, 3% talc, and 2% cobalt blue material evenly to obtain a mixture, and then add the quality of the mixture to the mixture 0.4% sodium tripolyphosphate and 1% CMC are mixed evenly, finely ground to 250 mesh, and the specific gravity of the prepared glaze slurry is 1.6-1.7g / cm 3 , to get blue glaze;

[0040] 3) see figure 2 , apply the blue glaze slurry evenly on the textured ceramic body 3, enter the kiln and raise the temperature to 1150°C under a reducing atmosphere, kee...

Embodiment 2

[0045] A method for preparing a color-changing peacock feather pattern decorative tile, the specific method is as follows:

[0046] 1) Preparation of textured ceramic body:

[0047] see figure 1 , using a ceramic mold 1 with concave-convex texture lines 2 similar to peacock feathers to press a ceramic body, and trimming the surface of the ceramic body to obtain a textured ceramic body 3;

[0048] 2) Preparation of blue glaze slurry:

[0049] Mix 60% feldspar, 20% quartz, 10% calcite, 5% talc, and 5% cobalt blue material to obtain a mixture by mass percentage, and then add 0.4% of the mass of the mixture to the mixture Sodium tripolyphosphate and 1% CMC are mixed evenly, finely ground to 250 mesh, and the specific gravity of the prepared glaze slurry is 1.6-1.7g / cm 3 , to get blue glaze;

[0050] 3) see figure 2 , apply the blue glaze slurry evenly on the textured ceramic body 3, enter the kiln and raise the temperature to 1200°C under a reducing atmosphere, keep it warm fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a multi-colored peacock feather grain decoration ceramic tile and a preparation method. The preparation method comprises the steps that firstly, a ceramic body with grains is prepared, blue glaze slip is uniformly applied to the ceramic body with the grains, the ceramic body is put into a kiln, heating, calcination and heat preservation are performed at the reducing atmosphere, natural cooling is performed to obtain a blue glaze ceramic tile with a blue glaze layer, a semi-finished peacock grain ceramic tile is obtained after the surface of the blue glaze ceramic tile is polished, then the semi-finished peacock grain ceramic tile is uniformly sprayed with a layer of a nano silicon oxide photonic crystal film, and then thermal treatment is performed to prepare the multi-colored peacock feather grain decoration ceramic tile. The decoration ceramic tile obtained through the preparation method is the peacock grain ceramic tile showing different colors at different angles, multi-color changes can be generated on the basis of stamping-back grains, the multi-colored peacock feather grain decoration effect is achieved, the produced ceramic tile can form more natural peacock feather third dimension and clear vivid grains, has the advantage of being more vivid in surface color, and can be widely applied in the fields of architectural decoration and ceramic decoration.

Description

technical field [0001] The invention relates to a decorative ceramic tile used in the fields of architectural decorative ceramics, interior decorative ceramics, etc., in particular to a color-changing peacock feather pattern decorative ceramic tile and a preparation method thereof. Background technique [0002] As ceramic products have entered thousands of households, there are many types of ceramic tiles on the market, and the surface texture and color of the products tend to be diversified. In recent years, the more popular ones are: leather tiles, wood tiles, cloth tiles, etc. The uniqueness is becoming more and more obvious. In order to cater to the individual needs of different consumers, more unique craftsmanship is needed in the research and development of ceramic tiles to meet market demand. Most of the colored bionic textured bricks on the market are printed with patterns on the flat body surface and fired. The texture is single and lacks three-dimensionality, and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/89C03C8/14C03C1/06B24B7/19B28B11/04B28B11/10
CPCC04B41/52B24B7/19B28B11/041B28B11/044B28B11/048B28B11/10C03C1/06C03C8/14C04B41/89C04B2235/963C04B41/5022C04B41/5035
Inventor 王毅郭燕妮王伟伟杨晓燕
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More