A kind of super-weather-resistant powder coating for electrostatic spraying and preparation method thereof

A technology of electrostatic spraying and powder coating, which is applied in powder coatings, conductive coatings, polyester coatings, etc., and can solve problems such as complex dispersion processes, restrictions on the development of powder coatings for electrostatic spraying, and poor substrate bonding

Active Publication Date: 2020-06-26
TIANCHANG JINLING ELECTRONICS
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the prior art, in order to disperse carbon nanotubes in the polymer film-forming matrix, not only a complicated dispersion process is required, but also there are a series of problems such as poor bonding with the matrix, which greatly limits the development of powder coatings for electrostatic spraying.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of super-weather-resistant powder coating for electrostatic spraying and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A powder coating for super weather-resistant electrostatic spraying, comprising the following raw materials in parts by weight: 50 parts of polyester resin, 35 parts of alkyd resin, 3 parts of polyester-coated carbon nanotubes, 6 parts of nano-titanium dioxide, and 1 part of nano-zinc oxide , 3 parts of aluminum nitride, 0.5 parts of phosphotungstic acid, 2 parts of quartz, 5 parts of bauxite, 6 parts of vinyltriethoxysilane, 5 parts of titanium dioxide, 2 parts of benzoin, polyether modified organosiloxane 0.5 parts of solution, 1 part of polyacrylate polymer, 1 part of propylene glycol methyl ether acetate, 10 parts of β-hydroxyalkylamide;

[0021] Wherein, the polyol monomer adopted in the synthetic method of the polyester resin is neopentyl glycol, and the polyacid monomer adopted is terephthalic acid; the vegetable oleic acid monomer adopted in the synthetic method of the alkyd resin It is soybean oil fatty acid, the polyol monomer used is pentaerythritol, and the ...

Embodiment 2

[0024] A powder coating for super weather-resistant electrostatic spraying, comprising the following raw materials in parts by weight: 80 parts of polyester resin, 15 parts of alkyd resin, 15 parts of polyester-coated carbon nanotubes, 2 parts of nano-titanium dioxide, and 5 parts of nano-zinc oxide , 1 part of aluminum nitride, 2 parts of phosphotungstic acid, 0.5 part of quartz, 15 parts of bauxite, 2 parts of vinyltriethoxysilane, 10 parts of titanium dioxide, 1 part of benzoin, alkyl modified organosiloxane 2 parts of solution, 0.1 part of polymer silicone, 5 parts of propylene glycol methyl ether acetate, 4 parts of β-hydroxyalkylamide;

[0025] Wherein, the polyol monomer adopted in the synthetic method of the polyester resin is ethylene glycol and trimethylolpropane, and the polybasic acid monomer adopted is isophthalic acid; The vegetable oleic acid monomer is linolenic acid, the polyol monomers used are pentylene glycol and trimethanol propane, and the polyacid monome...

Embodiment 3

[0028] A powder coating for super weather-resistant electrostatic spraying, comprising the following raw materials in parts by weight: 60 parts of polyester resin, 30 parts of alkyd resin, 5 parts of polyester-coated carbon nanotubes, 5 parts of nano-titanium dioxide, and 3 parts of nano-zinc oxide , 2 parts of aluminum nitride, 0.8 parts of phosphotungstic acid, 1.6 parts of quartz, 8 parts of bauxite, 5 parts of vinyltriethoxysilane, 7 parts of titanium dioxide, 1.8 parts of benzoin, 0.8 parts of acrylate copolymer solution, 0.7 parts of fluorine-modified acrylate polymer, 3 parts of propylene glycol methyl ether acetate, and 8 parts of β-hydroxyalkylamide;

[0029] Wherein, the polyhydric alcohol monomer adopted in the synthetic method of polyester resin is trimethylolethane and glycerin, the polybasic acid monomer adopted is adipic acid; In the synthetic method of described alkyd resin, adopt The vegetable oleic acid monomer is dehydrated ricinoleic acid, the polyol monome...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a super-weather-resistance powder coating for electrostatic spraying and a preparation method thereof. The powder coating comprises the following raw materials of, by weight, 50-80 parts of polyester resin, 15-35 parts of alkyd resin, 3-15 parts of polyester-coated carbon nanotubes, 2-6 parts of nano-titanium dioxide, 1-5 parts of nano-zinc oxide, 1-3 parts of aluminum nitride, 0.5-2 parts of phosphotungstic acid, 0.5-2 parts of quartz, 5-15 parts of bauxite, 2-6 parts of vinyltriethoxysilane, 5-10 parts of titanium dioxide, 1-2 parts of benzoin, 0.5-2 parts of leveling agents, 0.1-1 part of auxiliary agent, 1-5 parts of propylene glycol methyl ether acetate, 4-10 parts of beta-hydroxyalkylamide. According to the provided super-weather-resistance powder coating for electrostatic spraying and the preparation method thereof, on the premise that a good electrostatic spraying effect of the powder coating is ensured, the weather resistance of the coating is greatly improved.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a super weather-resistant powder coating for electrostatic spraying and a preparation method thereof. Background technique [0002] Electrostatic spraying uses the principle of high-voltage electrostatic corona electric field. The metal diversion cup on the spray gun head is connected to a high-voltage negative charge, and the workpiece to be coated is grounded to form a positive electrode. A strong electrostatic field is formed between the spray gun and the workpiece. When the carrier gas (compressed air) sends the powder coating from the powder supply barrel to the diversion cup of the spray gun through the powder delivery pipe, dense charges are generated around it, and the powder is negatively charged. Under the action of electrostatic force and compressed air, The powder is evenly adsorbed on the workpiece, and after heating, the powder is melted and solidified (or plasti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/02C09D167/08C09D5/03C09D5/24C09D7/61C09D7/62C09D7/63
CPCC08K2201/011C08L2201/04C08L2205/02C08L2205/03C08L2205/035C09D5/033C09D5/24C09D167/02C08L67/08C08K13/06C08K9/10C08K7/24C08K2003/2241C08K3/36C08K2003/2296
Inventor 茆文斌
Owner TIANCHANG JINLING ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap