A kind of warm mixed sulfur asphalt and preparation method thereof

A sulfur and asphalt technology, applied in building thermal insulation materials, buildings, building components, etc., can solve the problems of poor thermal stability and anti-aging performance of asphalt, environmental pollution, etc., to improve anti-aging performance, shorten reaction time, reduce The effect of preparation temperature

Active Publication Date: 2019-06-11
CHINA PETROLEUM & CHEM CORP +1
View PDF16 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0022] In order to solve the problems in the prior art that the use temperature of sulfur asphalt is relatively high, which may easily cause environmental pollution or that the use temperature can be lowered after adding a warm mix agent, but the thermal stability and anti-aging performance of the asphalt are not good. The present invention provides a warm Mixing sulfur asphalt, adding a self-made warm mixing agent, can significantly reduce the production and use temperature of sulfur asphalt, reduce the air pollution caused by sulfur asphalt in production and use, and at the same time improve the thermal stability of asphalt and improve anti-aging performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of warm mixed sulfur asphalt and preparation method thereof
  • A kind of warm mixed sulfur asphalt and preparation method thereof
  • A kind of warm mixed sulfur asphalt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] (1) Preparation of warm mix agent

[0059]Using Ni metal as a catalyst, the CO obtained after gasification of coal, and H 2 The synthesis reaction is carried out to obtain mixed alkanes in which alkanes with carbon numbers of 30 to 60 account for 90%.

[0060] ①Weigh 1000g of the above-mentioned mixed alkanes, about 1.2mol, put them in a closed container, heat to 480°C, add 3g of catalyst anhydrous CuCl 2 , keep introducing 0.89 mol of chlorine at this temperature, and feed nitrogen to keep the pressure of the reaction vessel at 3MPa, and react for 30min to obtain the intermediate;

[0061] ②Weigh 7000g of the fourth-line extraction oil with 70% aromatics content, and add 441g of complex [Cu(NH 3 ) 4 〕SO 4 , placed in another container and heated to 350°C, and kept stirring at this temperature for 180min to obtain aromatic hydrocarbon complex components;

[0062] ③Introduce the aromatic hydrocarbon complexing component into the above-mentioned intermediate, keep th...

Embodiment 2

[0066] (1) Preparation of warm mix agent

[0067] Using Co metal as a catalyst, the CO obtained after gasification of coal, and H 2 The synthesis reaction is carried out to obtain mixed alkanes in which alkanes with carbon numbers of 30 to 130 account for 90%.

[0068] ① Weigh 3500g of the above-mentioned mixed alkanes, about 4.5mol, put them in a closed container, heat to 400°C, add 31.5g of catalyst anhydrous MnCl 2 , keep introducing 1.16mol of chlorine at this temperature, and feed nitrogen to keep the pressure of the reaction vessel at 5MPa, and react for 60min to obtain the intermediate;

[0069] ②Weigh 1000g of catalytic cracking oil slurry with an aromatics content of 63%, and add 19g of complex K to it 4 [Fe(CN) 6 ], placed in another container and heated to 270°C, and kept stirring at this temperature for 120 minutes to obtain aromatic hydrocarbon complex components;

[0070] ③Introduce the aromatic hydrocarbon complexing component into the above-mentioned interm...

Embodiment 3

[0074] (1) Preparation of warm mix agent

[0075] Using Fe metal as a catalyst, CO obtained from gasification of coal, and H 2 The synthesis reaction is carried out to obtain mixed alkanes in which alkanes with carbon numbers of 70 to 90 account for 90%.

[0076] ①Weigh 1000g of the above-mentioned mixed alkanes, about 0.8mol, put them in a closed container, heat to 440°C, add 6g of catalyst anhydrous NiCl 2 , keep the temperature and introduce 0.31mol of fluorine, and feed nitrogen to keep the pressure of the reaction vessel at 4MPa, and react for 45min to obtain the intermediate;

[0077] ②Weigh 3500g of phenolic refined oil with aromatics content of 78%, and add 164g of complex [Ni(CO) 4 ], placed in another container and heated to 310°C, stirred at a constant temperature for 160min at this temperature to obtain the aromatic complex component;

[0078] ③Introduce the aromatic hydrocarbon complexing component into the above-mentioned intermediate, keep the temperature at ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention provides warm-mixing sulfur asphalt. The warm-mixing sulfur asphalt is prepared from the following components in parts by mass: 0.5 to 7 parts of warm-mixing agent, 33 to 79.5 parts of matrix asphalt and 20 to 60 parts of sulfur. The warm-mixing agent is prepared by adopting the following method: firstly, reacting polymer paraffin with a halide element at a certain temperature and pressure under the action of a catalyst to obtain an intermediate; uniformly mixing aromatic hydrocarbon oil with a complex to obtain an aromatic hydrocarbon complexing component; secondly, reacting the aromatic hydrocarbon complexing component with the intermediate at a certain temperature to obtain the warm-mixing agent for the warm-mixing sulfur asphalt provided by the invention. According to the warm-mixing agent used by the warm-mixing sulfur asphalt provided by the invention, a warm-mixing effect on asphalt can be realized, the high-and-low temperature performance of the asphalt is considered, the thermal stability of the asphalt can be improved, and the aging resistant property is improved; the warm-mixing asphalt is prepared from the warm-mixing agent and the asphalt, so that the melting temperature of the asphalt and the viscosity of the asphalt at the temperature are reduced; particularly when the sulfur asphalt is prepared, the preparation temperature of the sulfur asphalt can be reduced, and the occurrence quantity of the harmful gases is reduced.

Description

technical field [0001] The invention relates to a warm-mix asphalt, in particular to a warm-mix sulfur asphalt and a preparation method thereof, belonging to the fields of petroleum industry and basic material chemistry. Background technique [0002] The asphalt mixture used in road engineering in the past is generally divided into two types according to the mixing construction temperature: cold mix asphalt mixture CMA (Cold Mix Asphalt) and hot mix asphalt mixture HMA (Hot Mix Asphalt). Cold-mix asphalt mixture is generally mixed and paved with emulsified asphalt or liquid asphalt and aggregate at room temperature, without heating the aggregate and binder, which can save a lot of energy. However, the initial strength of cold-mix asphalt mixture is low, and it is difficult to meet the requirements of important projects such as expressways and heavy-duty traffic roads. Hot mix asphalt mixture is widely used and has good road performance. However, in the production process o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L91/00C08K3/06
CPCY02A30/30
Inventor 陈保莲范思远张静宁爱民李志军程国香
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com