Method for preparing degradable aggregate with fertilizer efficiency

A technology of aggregate and fertilizer efficiency, applied in the field of preparation of degradable aggregate, can solve problems such as poor growth and development of plants, damage to concrete structure, huge plant root system, etc., and achieve the effect of preventing damage to concrete structure, promoting decay and decomposition, and simple process

Inactive Publication Date: 2017-05-31
UNIV OF JINAN
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, plant-growing ecological concrete has not been widely used at present. The fundamental reason is that there are still the following problems: there is no nutrient component required for plant growth in concrete, resulting in poor growth and development of plants or even death; due to the inverse ratio between the strength and porosity of concrete, In order to ensure the strength of concrete, the porosity is generally less than 38%, resulting in the phenomenon that the plant root system is too large and destroys the concrete structure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for preparing degradable aggregate with fertilizer effect, comprising the steps of:

[0021] (1) Crush the corn kernels and screen the particles with a particle size of 0.5-3mm, soak them in warm water at 65°C for 2 days, remove them, and drain them.

[0022] (2) After stirring 50% by weight of drained corn kernels, 1% phosphoric acid, 1% yeast, 40% saturated water-absorbing resin and 8% starch for 30 seconds, granulate into balls with a particle size between 9- 10mm, get the aggregate core;

[0023] (3) After mixing 80% starch, 6% dextrin, 4% gum arabic, and 10% water by weight for 80 seconds, spray it on the surface of the aggregate core in a mist state to form a coating. The thickness of the soluble coating is 50% of the diameter, degradable aggregates were obtained after drying at 65°C.

[0024] The specific surface area of ​​the above-mentioned water-absorbent resin is 280m 2 , the water absorption rate is 60; the specific surface area of ​​dextrin is 2...

Embodiment 2

[0028] A method for preparing degradable aggregate with fertilizer effect, comprising the steps of:

[0029] (1) Crush the corn kernels and screen the particles with a particle size of 0.5-3mm, soak them in warm water at 35°C for 5 days, remove them, and drain them.

[0030] (2) After stirring 85% by weight of drained corn kernels, 3% phosphoric acid, 3% yeast, 7% saturated water-absorbing resin and 2% starch for 90 seconds, granulate into balls with a particle size between 5- 8mm, get the aggregate core;

[0031] (3) After mixing 90% starch, 2% dextrin, 2% gum arabic, and 6% water by weight for 30 seconds, spray it on the surface of the aggregate core in a mist state to form a coating. The thickness of the soluble coating is 20% of the diameter. The degradable aggregate was obtained after drying at 45°C.

[0032] The specific surface area of ​​the above-mentioned water-absorbent resin is 340m 2 , the water absorption rate is 95; the specific surface area of ​​dextrin is 3...

Embodiment 3

[0036] A method for preparing degradable aggregate with fertilizer effect, comprising the steps of:

[0037] (1) Crush the corn kernels and screen the particles with a particle size of 0.5-3mm, soak them in warm water at 45°C for 4 days, remove them, and drain them.

[0038] (2) 65% by weight of drained corn kernels, 2% phosphoric acid, 2% yeast, 23% saturated water-absorbing resin and 8% starch were stirred for 60 seconds, and then granulated into balls with a particle size between 7- 9mm, get the aggregate core;

[0039] (3) After mixing 85% starch, 4% dextrin, 5% gum arabic, and 6% water by weight for 50 seconds, spray it on the surface of the aggregate core in a mist state to form a coating. The thickness of the soluble coating is 40% of the diameter. The degradable aggregate was obtained after drying at 50°C.

[0040] The specific surface area of ​​the above-mentioned water-absorbent resin is 300m 2 , the water absorption rate is 75; the specific surface area of ​​the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing degradable aggregate with fertilizer efficiency and belongs to the technical field of energy-saving environment-friendly building materials. The method comprises the following steps: mixing crushed corn kernel particles with phosphoric acid, saccharomycetes, a water-saturated water-absorbent resin and starch, granulating into balls so as to obtain an aggregate core; and spraying a soluble envelope on the surface of the aggregate core in a mist state so as to form an envelope, drying, thereby obtaining the degradable aggregate with the fertilizer efficiency. The preparation method is simple, readily available in raw materials and low in cost, the prepared aggregate can provide the nutrition components needed for the growth of plants when used for vegetation ecological concrete and has low crush index and moisture absorption rate, and the strength requirement of the concrete aggregate is guaranteed. In addition, the aggregate can be naturally degraded within a certain period, does not cause any pollution to the environment, and provides more space for the growth of plant roots.

Description

technical field [0001] The invention relates to a method for preparing degradable aggregate with fertilizer effect, and belongs to the technical field of energy-saving and environment-friendly building materials. Background technique [0002] Ecological concrete is a concrete material that can adapt to the growth of animals and plants, and has a positive effect on regulating ecological balance, beautifying the environment and realizing the coordination between human beings and nature. The research and development time of this kind of concrete is not long. The emergence of ecological concrete marks that humans have adopted a more active and proactive attitude in the process of dealing with the relationship between concrete materials and the environment. Concrete is not only used as a building material to construct structures or buildings needed by human beings, but also a material that integrates with nature and has a positive protective effect on the natural environment and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B20/10C05G3/00C04B28/00C04B38/00C04B16/00
CPCC04B20/1048C04B28/00C04B38/00C04B2103/0072C05F11/00C05G3/00C05G5/30C04B20/0016C04B16/00C04B22/165C04B24/38C04B24/24C04B2103/0001C04B14/02C04B22/002C04B2103/0068C05F11/08
Inventor 宫晨琛马法豪吴波芦令超
Owner UNIV OF JINAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap