Water-borne hydrographics transfer printing pigment and preparation method thereof
A technology of water transfer printing and water-based linking material, which is applied in the direction of art paints, etc., can solve the problems of cumbersome methods, difficult to clean, and pollute the environment, and achieve the effect of strong playability, easy transfer, and low cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] Prepare 5 parts of water-based vehicle, 4 parts of alkane ammonium salts of copolymers containing acidic groups, 5 parts of antifreeze, 0.2 parts of defoamers, 0.3 parts of antibacterial preservatives, 3 parts of water-based colorants, 0.05 parts of leveling agents and 82.45 parts of water, wherein parts are parts by weight. Among them, the water-based vehicle is water-based polyurethane-polyacrylic acid copolymer emulsion, the antifreeze is a mixture of propylene glycol and sorbitol, the weight ratio of the two is 1:1, the defoamer is polysiloxane, and the antibacterial preservative is phenoxyethanol , The leveling agent is acrylate modified polydimethylsiloxane.
[0023] According to the above formula quantity, add the water-based polyurethane-polyacrylic acid copolymer emulsion into the water, stir at a speed of 800r / min, and add the alkane ammonium salt of the acid group-containing copolymer and the acrylate-modified polydimethylsilane successively while stirring. ...
Embodiment 2
[0026] Prepare 13 parts of water-based linking material, 6 parts of alkane ammonium salts of copolymers containing acidic groups, 7 parts of antifreeze, 0.3 parts of defoamers, 0.5 parts of antibacterial preservatives, 5 parts of water-based colorants, 0.1 parts of leveling agents and 66.10 parts of water, wherein parts are parts by weight. Among them, the water-based vehicle is water-based polyurethane-polyacrylic acid copolymer emulsion, the antifreeze is a mixture of propylene glycol and sorbitol, the weight ratio of the two is 1:1, the defoamer is polysiloxane, and the antibacterial preservative is phenoxyethanol , The leveling agent is acrylate modified polydimethylsiloxane.
[0027] According to the above formula quantity, add the water-based polyurethane-polyacrylic acid copolymer emulsion into the water, stir at a speed of 800r / min, and add the alkane ammonium salt of the acid group-containing copolymer and the acrylate-modified polydimethylsilane successively while st...
Embodiment 3
[0030] Prepare 20 parts of water-based vehicle, 9 parts of alkanyl ammonium salts of copolymers containing acidic groups, 8 parts of antifreeze, 0.5 parts of defoamers, 0.8 parts of antibacterial preservatives, 10 parts of water-based colorants, 0.2 parts of leveling agents and 51.5 parts of water, wherein parts are parts by weight. Among them, the water-soluble linking material is water-based polyurethane-polyacrylic acid copolymer emulsion, the antifreeze agent is a mixture of propylene glycol and sorbitol, the weight ratio of the two is 1:1, the defoamer is polysiloxane, and the antibacterial preservative is phenoxy Alcohol, leveling agent is acrylate modified polydimethylsiloxane.
[0031] According to the above formula quantity, add the water-based polyurethane-polyacrylic acid copolymer emulsion into the water, stir at a speed of 800r / min, and add the alkane ammonium salt of the acid group-containing copolymer and the acrylate-modified polydimethylsilane successively whi...
PUM
Property | Measurement | Unit |
---|---|---|
Density | aaaaa | aaaaa |
Density | aaaaa | aaaaa |
Density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com