Hard water softening agent and its preparation method and application

A technology of hard water softener and diatomite, which is applied in the direction of complex/solubilizer treatment, etc., can solve the problems of unsafety and high investment cost, and achieve the effect of good physical adsorption performance

Inactive Publication Date: 2017-12-01
科比环保科技(天津自贸试验区)有限公司
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, hard water softening methods include ion exchange method, membrane separation method, drug addition method, etc., but some methods have high investment costs and some methods are not safe.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hard water softening agent and its preparation method and application
  • Hard water softening agent and its preparation method and application
  • Hard water softening agent and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Preparation of hard water softener: Take 1.5g of diatomite, 0.2g of sodium carbonate, 0.1g of sodium hydroxide, 1g of activated carbon, then add 7.2g of deionized water, mix well, dry and shape, and obtain purification softener 1;

[0014] Preparation of filter column: first put a layer of filter paper in the adsorption column, then add a layer of 5mm filter paper pulp layer, then put 2g of diatomaceous earth, 5g of purification softener 1, and 2g of activated carbon in turn, and then add a layer of 5mm of filter paper pulp, then put a layer of filter paper, and finally drain to obtain the filter column 1.

Embodiment 2

[0016] Preparation of hard water softener: Take 1.5g of diatomaceous earth, 0.5g of sodium carbonate, 0.2g of sodium hydroxide, 2g of activated carbon, then add 5.8g of deionized water, mix well, dry and shape, and obtain purification softener 2;

[0017] Preparation of filter column: first put a layer of filter paper in the adsorption column, then add a layer of 5mm filter paper slurry layer, then put 1g of diatomaceous earth, 8g of purification softener 2, and 1g of activated carbon in turn, and then add a layer of 5mm of filter paper pulp, then put a layer of filter paper, and finally drain to obtain the filter column 2.

Embodiment 3

[0019] Preparation of hard water softener: Take 2.5g of diatomaceous earth, 0.2g of sodium carbonate, 0.1g of sodium hydroxide, 1g of activated carbon, then add 6.2g of deionized water, mix well, dry and shape, and obtain purification softener 3;

[0020] Preparation of filter column: first put a layer of filter paper in the adsorption column, then add a layer of 5mm filter paper pulp layer, then put 4g of diatomaceous earth, 10g of purification softener 3, and 1g of activated carbon in turn, and then add a layer of 5mm of filter paper pulp, then put a layer of filter paper, and finally drain to obtain the filter column 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention specifically relates to a hard water softening agent and its preparation method and application, belonging to the field of tap water treatment. The hard water softening agent comprises the following components by weight: 15-25% of diatomite, 1-5% of sodium carbonate, 1-2% of sodium hydroxide and 10-20% of activated carbon, with the balance being deionized water. The hard water softening agent provided by the invention purifies and softens tap water in one step and is convenient and quick; through addition of the activated carbon, residual chlorine in tap water can be effectively filtered out; in particular, the diatomite is added into the purifying softening agent, so the softening agent is allowed to have good physical adsorption properties due to the great specific surface of the diatomite; after calcium and magnesium ions in tap water form precipitates with sodium carbonate and sodium hydroxide in the purifying softening agent, the precipitates can be adsorbed by the diatomite; and the design of a filter column makes the calcium and magnesium ions in tap water to be fully precipitated, so residual chlorine can be effectively filtered out.

Description

technical field [0001] The invention belongs to the field of tap water treatment, and in particular relates to a hard water softener and a preparation method and application thereof. Background technique [0002] Hard water refers to water containing a large amount of calcium ions and magnesium ions, which brings many hazards to life and production. For example, scale is generated when hard water is heated, and scum produced by contact with soap affects the cleaning effect. Drinking water with high hardness affects health and brings losses to industrial production. When hard water passes through the pipeline, scale tends to stick to the pipe wall for a long time. It is easy to damage the equipment. The content of calcium and magnesium ions in tap water is generally high, and the residual chlorine in tap water is also very harmful to human health. At present, hard water softening methods include ion exchange method, membrane separation method, dosing method, etc., but some ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C02F5/08
CPCC02F5/08
Inventor 陶正勇
Owner 科比环保科技(天津自贸试验区)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap