A kind of processing method of silver jewelry

A processing method and technology of silver jewelry, applied in clothing, jewelry, applications, etc., can solve the problems of silver jewelry processing technology confusion, poor gloss of silver jewelry, unsightly welding, etc., and achieve beautiful silver jewelry, smooth surface, and high wear resistance Effect

Active Publication Date: 2019-04-09
GUIZHOU YIHUAZHUANG DEV CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the improvement of living standards, people buy more and more silver ornaments, and the requirements for the appearance and quality of silver ornaments are constantly improved. Due to the higher demand, the processing technology of silver ornaments in the prior art is relatively chaotic, resulting in processed silver ornaments. Defects such as poor gloss of jewelry and unsightly welding have caused many defective products to be re-melted, causing unnecessary losses to the manufacturer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for processing silver jewelry includes the following steps:

[0021] (1) Rolling: The silver block is fed into the tablet press to be rolled into a silver wire with a width of 1 cm and a thickness of 0.5 cm;

[0022] (2) Modification: Put the silver wire into the modification solution and soak for 25 minutes at a temperature of 60°C;

[0023] (3) High temperature: Send the soaked silver wire into a 150℃ high temperature furnace for 10 minutes, and place it in a ventilated place to cool to 40℃;

[0024] (4) The production of chaotic wire: the high-temperature treated silver wire is twisted on a flat object with a wooden pressing tool into a silver filigree, and the twisted silver filigree is wound on an iron rod with a diameter of 3 cm, and placed in an oven for 120 minutes , Then naturally cool to room temperature, remove the silver filigree from the iron rod, pinch the spiral silver filigree by hand, and then use a hammer to slightly beat both sides to get the silver ...

Embodiment 2

[0033] A method for processing silver jewelry includes the following steps:

[0034] (1) Rolling: The silver block is fed into the tablet press and rolled into a silver wire with a width of 1.5 cm and a thickness of 1 cm;

[0035] (2) Modification: Put the silver wire into the modification solution and soak for 35 minutes at a temperature of 70°C;

[0036] (3) High temperature: send the soaked silver wire into a 220 ℃ high temperature furnace for 20 minutes, and place it in a ventilated place to cool to 60 ℃;

[0037] (4) Production of chaotic wire: use a wooden pressing tool to twist the high-temperature treated silver wire on a flat object into a silver filigree, wind the twisted silver filigree on an iron rod with a diameter of 5 cm, and put it in an oven for 180 minutes , Then naturally cool to room temperature, remove the silver filigree from the iron rod, pinch the spiral silver filigree by hand, and then use a hammer to slightly beat both sides to get the silver filigree;

[003...

Embodiment 3

[0046] A method for processing silver jewelry includes the following steps:

[0047] (1) Rolling: the silver block is fed into the tablet press to be rolled into a silver wire with a width of 1.2 cm and a thickness of 0.8 cm;

[0048] (2) Modification: Put the silver wire into the modification solution and soak for 30 minutes at a temperature of 68°C;

[0049] (3) High temperature: send the soaked silver wire into a 180℃ high temperature furnace for 15 minutes, and place it in a ventilated place to cool to 48℃;

[0050] (4) The production of chaotic wire: the high-temperature treated silver wire is twisted on a flat object with a wooden pressing tool to form a silver filigree, and the twisted silver filigree is wound on an iron rod with a diameter of 3 to 5 cm and placed in an oven Treat it for 150 minutes, then cool it naturally to room temperature, remove the silver filigree from the iron rod, squeeze the spiral silver filigree by hand, and then use a hammer to slightly beat on both...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of silver ornament processing, in particular to a processing method of a silver ornament. The method comprises the following six steps to finish the silver ornament processing: rolling, modifying, processing under high temperature, manufacturing entangled threads, welding the silver threads subjected to modifying and high-temperature processing are high in tensile strength, wearing resistance, toughness and glossiness, so that the silver threads can be effectively prevented from breaking and deforming during the entangled thread manufacturing process; moreover, the plasticity of the silver threads in processing can be improved. The silver ornament processed through the abovementioned scheme is nice in appearance, smooth in surface, glossy, high in wearing resistance, and hard to damage.

Description

Technical field [0001] The invention belongs to the technical field of silver jewelry processing, in particular to a silver jewelry processing method. Background technique [0002] With the improvement of living standards, people’s purchase of silver jewelry is increasing, and the requirements for the appearance and quality of silver jewelry are continuously improved. Due to the higher demand, the processing technology of silver jewelry in the prior art is relatively chaotic, resulting in the processed silver Defects such as poor gloss of jewelry and unsightly welding have caused many defective products to be reheated, causing unnecessary losses to the manufacturer. Summary of the invention [0003] In order to solve the above technical problems, the present invention provides a method for processing silver jewelry. [0004] Specifically, it is achieved through the following technical solutions: [0005] A method for processing silver jewelry includes the following steps: [0006] (1...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A44C27/00B23P15/00
CPCA44C27/00B23P15/00
Inventor 李开琼李开元张喜
Owner GUIZHOU YIHUAZHUANG DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com