Organic silicon polymer composite emulsion and preparation method thereof
A composite emulsion and silicone technology, applied in the field of materials, can solve the problems of restricting the development and utilization of large-scale and large-diameter materials, affecting the service life and wide application, and being easy to be damaged by water absorption. Strong acid-base ability and good wet viscosity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
Specific Example 1
[0025] A silicone polymer composite emulsion, comprising the following components in parts by weight: 5 parts of ethylene vinyl acetate, 90 parts of silicone, and 1 part of a catalyst; the silicone is phenethyl methyl polysiloxane One or more of alkane, phenethyl methyl hydrogen-containing polysiloxane, substituted phenethyl methyl polysiloxane or substituted phenethyl methyl hydrogen-containing polysiloxane.
[0026] A preparation method of the said organosilicon polymer composite emulsion includes the following steps:
[0027] ① Prepare a certain mass fraction of ethylene vinyl acetate into a suspension emulsion, and mix the suspension with deionized water at a mass ratio of 3:1;
[0028] ② Adjust the laboratory temperature to room temperature 25℃;
[0029] ③. Slowly add 3‰ silicone material and catalyst to the ethylene vinyl acetate suspension emulsion, and disperse it in a high-speed disperser at a speed of 1800 revolutions per minute for 20 minutes, so that th...
Example Embodiment
Specific Example 2
[0032] An organosilicon polymer composite emulsion, comprising the following components in parts by weight: 500 parts of ethylene vinyl acetate, 110 parts of silicone, and 5 parts of catalyst; the silicone is phenethyl methyl polysiloxane One or more of alkane, phenethyl methyl hydrogen-containing polysiloxane, substituted phenethyl methyl polysiloxane or substituted phenethyl methyl hydrogen-containing polysiloxane.
[0033] A preparation method of the said organosilicon polymer composite emulsion includes the following steps:
[0034] ① Prepare a certain mass fraction of ethylene vinyl acetate into a suspension emulsion, and mix the suspension with deionized water at a mass ratio of 3:1;
[0035] ② Adjust the laboratory temperature to room temperature 25℃;
[0036] ③. Slowly add 5‰ organosilicon material and catalyst into the ethylene vinyl acetate suspension emulsion, and disperse it in a high-speed disperser at a speed of 2000 revolutions per minute for 25 minu...
Example Embodiment
Specific Example 3
[0039] A silicone polymer composite emulsion, comprising the following components in parts by weight: 450 parts of ethylene vinyl acetate, 108 parts of silicone, and 3 parts of catalyst; the silicone is phenethyl methyl polysiloxane One or more of alkane, phenethyl methyl hydrogen-containing polysiloxane, substituted phenethyl methyl polysiloxane or substituted phenethyl methyl hydrogen-containing polysiloxane.
[0040] A preparation method of the said organosilicon polymer composite emulsion includes the following steps:
[0041] ① Prepare a certain mass fraction of ethylene vinyl acetate into a suspension emulsion, and mix the suspension with deionized water at a mass ratio of 3:1;
[0042] ② Adjust the laboratory temperature to room temperature 25℃;
[0043] ③. Slowly add 4‰ silicone material and catalyst to the ethylene vinyl acetate suspension emulsion, and disperse it in a high-speed disperser at a speed of 1900 revolutions per minute for 23 minutes to comple...
PUM
Property | Measurement | Unit |
---|---|---|
Glass transition temperature | aaaaa | aaaaa |
Glass transition temperature | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap