Manufacturing method for novel recombinant wood

A manufacturing method and technology for reconstituting wood, applied in the field of wood processing, can solve the problems of long time, poor permeability and the like

Active Publication Date: 2018-07-31
LIANYUNGANG NANFANG WOOD IND CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most air-drying wood glues are poorly penetrating and require external pressure to achieve the impregnation effect, or take longer to reach the specified amount of impregnation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1: take the recombined wood manufacturing method of the disentangling poplar wood beam after the blue change as constituent unit, and its steps are as follows:

[0018] Step 1) unit treatment: dilute the poplar wood bundles after the blue change to a mixed solution of 0.1mol / L NaoH and sodium pyrophosphate with a pH value of 9.0, and then adjust the pH value so that the pH value reaches 7.5;

[0019] Step 2) drying: drying the conditioned poplar wood beams to a moisture content of 10%,

[0020] Step 3) dipping and drying: the dried wood bundles are dipped with low molecular weight phenolic resin, the viscosity is 15mpa s, the molecular weight is 350, the dipping time is 1min, and the amount of dipping of wood bundles is the absolute dry weight 30% of 30%, after dipping and drying, the drying temperature is 45°C, and the moisture content after drying is 10-12%;

[0021] Step 4) Plate making: The hot-pressing process adopted is that the hot-pressing temperatur...

Embodiment 2

[0023] Embodiment 2: take the Chinese fir branch material after the blue change as raw material, then through rolling, the wood beam that loosens into is the recombined wood manufacturing method of constitutive unit, and its steps are as follows:

[0024] Step 1) unit treatment: dilute the fir wood beams after the blue change to a mixed solution of 0.1mol / L NaoH and sodium pyrophosphate with a pH value of 10.0 to adjust the pH value so that the pH value reaches 8.5;

[0025] Step 2) drying: drying the conditioned poplar wood bundles to a moisture content of 10%;

[0026] Step 3) dipping and drying: the dried wood bundles are dipped with low molecular weight phenolic resin, the viscosity is 17mpa s, the molecular weight is 300, the dipping time is 3min, and the amount of dipping of wood bundles is the absolute dry weight 35% of 35%, after dipping and drying, the drying temperature is 50°C, and the moisture content after drying is 8-12%;

[0027] Step 4) Plate making: using a s...

Embodiment 3

[0028] Embodiment 3: the recombined wood manufacturing method taking the toon wood beam after the blue change as a constituent unit, its steps are as follows:

[0029] Step 1) unit treatment: the thawed toon wood beams after the blue stain are diluted with deionized water to a mixed solution of 0.1mol / L NaoH and sodium pyrophosphate with a pH value of 11.0, and the pH value is adjusted to make its pH reach 9.0 ;

[0030] Step 2) drying: drying the conditioned poplar wood beams to a moisture content of 12%,

[0031] Step 3) dipping and drying: the dried wood bundles are dipped with low molecular weight phenolic resin, the viscosity is 20mpa s, the molecular weight is 450, the dipping time is 5min, and the dipping amount is the absolute dry weight of the wood bundles 40% of 40%, after dipping and drying, the drying temperature is 55°C, and the moisture content after drying is 8-12%;

[0032] Step 4) Plate making: using a segmented hot-pressing process, the hot-pressing tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing method for novel recombinant wood. The process steps are as follows, 1), rubber wood, cotton wood, cedar wood, ailanthus altissima and other small-diameter-grade logs easy to blue stain, brush wood, a rotary-cutting veneer processing residue and the like are used as raw materials, and undergo rolling and defibering to form wood bunches which is loose in thetransverse direction and do not crack in longitudinal direction to serve as constituent units; 2), the 0.1mol / L of the NaoH and the sodium pyrophosphate mixed solution which is diluted to reach the PHvalue of 9.0-11.0 through the deionized water is used for quenching and tempering the wood bunches; and 3), the quenched and tempered wood bunches undergo drying, glue dipping, hot pressing and otherprocesses to prepare the recombinant wood. The method has the advantages of being high in raw material utilization rate, good in impregnating effect and the like, the prepared recombinant wood has excellent mechanical properties and better dimensional stability; and in addition, the method further has the advantages of being high in production efficiency and low in energy consumption.

Description

technical field [0001] The invention relates to a manufacturing method of a novel recombined wood, which belongs to the technical field of wood processing. Background technique [0002] Tree species such as poplar, fir, and rubber wood toon are prone to blue stain, which will lead to a decrease in the appearance quality of the wood, affecting the price of the wood and the appearance of the wood after secondary processing. However, the blue stain has no obvious effect on the strength of the wood, and the wood has the advantages of better permeability and hygroscopicity after the blue stain. Recombined wood is a recombined structural material that is made of wood bundles or veneers, mainly by spraying or dipping glue. The permeability of wood raw materials has a significant impact on the impregnation process and the properties of recombined wood. Most air-drying wood glues are poorly penetrating and require externally applied pressure to achieve impregnation, or take longer ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K5/00B27K5/04B27N1/02B27N3/10
CPCB27K5/00B27K5/04B27N1/02B27N3/10
Inventor 关明杰张媛
Owner LIANYUNGANG NANFANG WOOD IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com