Method for preparing black tungsten carbide composite coating through physical vapor deposition method

A technology of physical vapor deposition and composite coating, which is applied in the field of PVD black technology, can solve the problems of poor process stability, poor corrosion resistance, non-abrasion resistance, etc., and achieve extended daily use, good oxidation resistance, and strong corrosion resistance. Effect

Active Publication Date: 2018-09-28
精研(东莞)科技发展有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] It should be further pointed out that for the traditional PVD black process, it has the de

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0032] The present invention will be described below with reference to specific embodiments.

[0033] A method for preparing a black tungsten carbide composite coating by physical vapor deposition, comprising the following process steps, specifically:

[0034] a. Degreasing and cleaning:

[0035] a1. Place the product to be processed in a general-purpose degreasing cleaning solution for immersion cleaning;

[0036] a2. Put the product after soaking and cleaning in the general degreasing cleaning agent in alcohol for ultrasonic cleaning, and the ultrasonic cleaning time is 3-8 minutes;

[0037] a3. Put the product after ultrasonic cleaning in ultrapure water for slow pulling and dehydration treatment, and the ultrapure water is 100 ℃ hot water;

[0038] a4. Put the product after the ultrapure water slow-drawing and dehydration treatment in an oven for baking treatment. The oven uses circulating air at 110-180°C for baking. The baking treatment time is 30-50 minutes; wait for ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing a black tungsten carbide composite coating through a physical vapor deposition method. The method comprises the following steps of oil removal and cleaning, bottom layer preparation, transition buffering layer preparation, hardening wear-resistant film layer preparation, color layer preparation and cooling and discharging, wherein the oil removal andcleaning step comprises the following steps of carrying out soaking and cleaning in a common oil removal and cleaning agent solution, carrying out ultrasonic cleaning in alcohol, carrying out slowly pulling and dehydrating in ultrapure water with the temperature of 100 DEG C and carrying out baking. According to the step design of the process, the black tungsten carbide composite coating preparedthrough the method for preparing the black tungsten carbide composite coating through the physical vapor deposition method has the advantages of being high in corrosion resistance and good in anti-oxidation property, and capable of well meeting the daily use of products and prolonging the service lift of the products.

Description

technical field [0001] The invention relates to the technical field of PVD black technology, in particular to a method for preparing a black tungsten carbide composite coating by a physical vapor deposition method. Background technique [0002] At present, with the rapid development of various electronic products and fierce competition, consumers not only require high-quality and durable products, but also have a particularly strong demand for high-end fashion, colorful and eye-catching appearance. [0003] It should be further pointed out that for the traditional PVD black process, it has the defects of low hardness, poor corrosion resistance, non-abrasion resistance, and poor process stability. Therefore, it is necessary to improve the existing PVD black process. Contents of the invention [0004] The object of the present invention is to provide a method for preparing a black tungsten carbide composite coating by physical vapor deposition in view of the deficiencies in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C14/06C23C14/14C23C14/16C23C14/32C23C14/02
CPCC23C14/0015C23C14/0021C23C14/021C23C14/0635C23C14/14C23C14/16C23C14/325
Inventor 施正彪李煜
Owner 精研(东莞)科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap