A method for preparing nano zno-go/waterborne polyurethane superamphiphobic coating by spraying method

A water-based polyurethane, spraying technology, applied in the field of materials, can solve the problems of loss of superhydrophobicity, damage, etc., and achieve the effects of low reaction equipment requirements, strong adhesion, and low production costs

Active Publication Date: 2022-03-25
NANCHANG HANGKONG UNIVERSITY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the fine rough structure and low surface energy substances on the superhydrophobic surface are easily damaged by mechanical effects such as impact and friction during processing and use, thus losing superhydrophobic properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing nano zno-go/waterborne polyurethane superamphiphobic coating by spraying method
  • A method for preparing nano zno-go/waterborne polyurethane superamphiphobic coating by spraying method
  • A method for preparing nano zno-go/waterborne polyurethane superamphiphobic coating by spraying method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Weigh 1.6 g of ZnO (30 nm grade) and disperse it in 40 mL of absolute ethanol, and add 0.2 mL of perfluorooctyltrichlorosilane and 10 drops of H 2 O, and magnetically stirred for 30 min to obtain solution A; weigh 0.1 g of GO and disperse it in 25 mL of absolute ethanol, and ultrasonically treat it for 30 min to form a uniformly dispersed suspension B; mix solution A and suspension B to obtain solution C, heating in a water bath at 60 °C, magnetic stirring for 6 h; washing with deionized water and absolute ethanol for 2-3 times, and suction filtration to obtain nano-ZnO-GO composites, vacuum drying at 80 °C for 12 h, and grinding for later use. Weigh an appropriate amount of water-based polyurethane A and B components in a ratio of 5:1, stir evenly, and cure at room temperature for 30 minutes, then spray on the surface of the treated aluminum substrate, spray two layers, and construct a water-based polyurethane coating; the prepared The nano-ZnO-GO composite was added t...

Embodiment 2

[0037] Weigh 1.6 g of ZnO (30 nm grade) and disperse it in 40 mL of absolute ethanol, and add 0.2 mL of perfluorooctyltrichlorosilane and 10 drops of H 2 O, and magnetically stirred for 30 min to obtain solution A; weigh 0.1 g of GO and disperse it in 25 mL of absolute ethanol, and ultrasonically treat it for 30 min to form a uniformly dispersed suspension B; mix solution A and suspension B to obtain solution C, heating in a water bath at 60 °C, magnetic stirring for 6 h; washing with deionized water and absolute ethanol for 2-3 times, and suction filtration to obtain nano-ZnO-GO composites, vacuum drying at 80 °C for 12 h, and grinding for later use. Weigh an appropriate amount of water-based polyurethane A and B components in a ratio of 5:1, stir evenly, and cure at room temperature for 30 minutes, then spray on the surface of the treated aluminum substrate, spray two layers, and construct a water-based polyurethane coating; the prepared The nano-ZnO-GO composite was added t...

Embodiment 3

[0039] Weigh 1.6 g of ZnO (30 nm grade) and disperse it in 40 mL of absolute ethanol, and add 0.2 mL of perfluorooctyltrichlorosilane and 10 drops of H 2O, and magnetically stirred for 30 min to obtain solution A; weigh 0.1 g of GO and disperse it in 25 mL of absolute ethanol, and ultrasonically treat it for 30 min to form a uniformly dispersed suspension B; mix solution A and suspension B to obtain solution C, heating in a water bath at 60 °C, magnetic stirring for 6 h; washing with deionized water and absolute ethanol for 2-3 times, and suction filtration to obtain nano-ZnO-GO composites, vacuum drying at 80 °C for 12 h, and grinding for later use. Weigh an appropriate amount of water-based polyurethane A and B components in a ratio of 5:1, stir evenly, and cure at room temperature for 30 minutes, then spray on the surface of the treated aluminum substrate, spray two layers, and construct a water-based polyurethane coating; the prepared The nano-ZnO-GO composite was added to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
contact angleaaaaaaaaaa
angleaaaaaaaaaa
contact angleaaaaaaaaaa
Login to view more

Abstract

A method for preparing nano-ZnO-GO / waterborne polyurethane super-amphiphobic coating by spraying method, adopting the method of ultrasonic hydrothermal compounding, first modifying nano-zinc oxide by perfluorooctyl trichlorosilane, and then applying the modified nano- ZnO and GO were loaded to obtain a nano-ZnO-GO composite. A water-based polyurethane layer was prepared on the surface of the substrate, and then a low-surface-energy nano-ZnO-GO composite layer was constructed on the surface of the water-based polyurethane layer. After the coating was cured, its surface morphology and static contact angle. The invention reduces the surface energy of nano-zinc oxide, improves the hydrophobicity and oleophobicity of the surface of the nano-ZnO-GO composite layer after fluorination treatment, achieves a super-amphiphobic effect, and improves the stability of the coating. The invention has the advantages of low production cost, simple preparation method, low requirements on reaction equipment, mild reaction conditions, no environmental pollution and large-scale production.

Description

technical field [0001] The invention belongs to the technical field of materials, and relates to a preparation method of a nanometer ZnO-GO / waterborne polyurethane superamphiphobic coating. Background technique [0002] In recent years, scholars at home and abroad have been inspired by the "lotus leaf effect", and superhydrophobic surfaces have aroused extensive interest of researchers. The main research idea is to introduce inorganic nano-rough structures on the surface of metal substrates and modify low surface energy substances. The preparation methods mainly include sol-gel method, hydrothermal method, layer-by-layer self-assembly method, chemical vapor deposition method, spray coating method and surface grafting. Copolymerization etc. [0003] Generally speaking, the current research mainly focuses on the following areas: (1) The study of plants and animals with superhydrophobic surfaces in nature provides inspiration for the development of materials with new surface s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B05D5/08B05D7/00B05D7/14C09D1/00
CPCC09D1/00B05D5/08B05D7/14B05D7/58B05D2503/00B05D2420/01B05D2420/02
Inventor 谢婵唐陈云李长全欧军飞薛名山王法军李文
Owner NANCHANG HANGKONG UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap