Graphene-modified antibacterial anticorrosive paint

A technology for graphene modification and anti-corrosion coatings, which is applied in anti-corrosion coatings, anti-fouling/underwater coatings, epoxy resin coatings, etc. It can solve the problems of poor antibacterial effect, large coating thickness, poor solvent resistance, etc. Corroded by bacteria, low cost, good wear resistance

Active Publication Date: 2019-05-21
ZHEJIANG SCI-TECH UNIV
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of antibacterial anticorrosion material with good wear resistance, water resistance and other defects in order to solve the defects of existing antibacterial and anticorrosion materials containing heavy metals, and the coating thickness is large, low hardness, poor solvent resistance, poor heat resistance or poor antibacterial effect. Graphene-modified antibacterial anticorrosion coatings with antibacterial properties, salt spray resistance, good flexibility, high adhesion and long-term excellent antibacterial anticorrosion properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene-modified antibacterial anticorrosive paint
  • Graphene-modified antibacterial anticorrosive paint
  • Graphene-modified antibacterial anticorrosive paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A graphene-modified antibacterial anticorrosion coating, the raw materials of the antibacterial anticorrosion coating include by weight: 30 parts of epoxy resin, 15 parts of modified diatomite, 0.5 part of graphene material, and 0.5 part of nano-silver particles , 8 parts of fillers, 1.5 parts of additives, 13 parts of nano-silver copper-loaded POSS-based resin and 16 parts of water.

[0033] The filler includes 1 part of nano tourmaline powder, 1 part of nano titanium dioxide, 2 parts of mica powder, 2 parts of heavy calcium and 2 parts of alginate powder; the particle size of heavy calcium and alginate powder is 200 mesh.

[0034] The preparation method of described nano-silver copper loaded POSS-based resin is as follows:

[0035] (1) Preparation of POSS pre-polymerization solution: Take 60 parts of ammonia water according to the weight and dissolve them in 110 parts of isopropanol, stir evenly and raise the temperature to 85°C, add γ-acryloyloxypropyl trimethyl 10 ...

Embodiment 2

[0038] A graphene-modified antibacterial and anti-corrosion coating, the raw materials of the anti-bacterial anti-corrosion coating include by weight: 42 parts of epoxy resin, 21 parts of modified diatomite, 7 parts of graphene materials, and 0.7 parts of nano-silver particles , 15 parts of fillers, 5 parts of additives, 14 parts of nano-silver copper-loaded POSS base resin and 20 parts of water.

[0039] The filler includes 2 parts of nano tourmaline powder, 2 parts of nano titanium dioxide, 1 part of mica powder, 5 parts of heavy calcium and 5 parts of alginate powder; the particle size of heavy calcium and alginate powder is 300 mesh.

[0040] The preparation method of described nano-silver copper loaded POSS-based resin is as follows:

[0041] (1) Preparation of POSS pre-polymerization solution: Take 70 parts of ammonia water according to the weight and dissolve them in 110 parts of isopropanol, stir evenly and raise the temperature to 88°C, add γ-acryloyloxypropyl trimeth...

Embodiment 3

[0045] A graphene-modified antibacterial anticorrosion coating, the raw materials of the antibacterial anticorrosion coating include by weight: 50 parts of epoxy resin, 35 parts of modified diatomite, 10 parts of graphene materials, and 1 part of nano-silver particles , 20 parts of fillers, 6 parts of additives, 15 parts of nano-silver copper loaded POSS base resin and 25 parts of water.

[0046] The filler includes 2 parts of nano tourmaline powder, 2 parts of nano titanium dioxide, 1 part of mica powder, 5 parts of heavy calcium and 10 parts of alginate powder; the particle size of the heavy calcium and alginate powder is 250 mesh.

[0047] The preparation method of described nano-silver copper loaded POSS-based resin is as follows:

[0048] (1) Preparation of POSS pre-polymerization liquid: Take 85 parts of ammonia water according to the weight and dissolve them in 110 parts of isopropanol, stir evenly and raise the temperature to 95°C, add γ-acryloyloxypropyl trimethyl 25...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of antibacterial anticorrosive products, especially to a graphene-modified antibacterial anticorrosive paint. Raw materials of the antibacterial anticorrosive paintcomprise, by weight, 30-50 parts of epoxy resin, 15-35 parts of modified diatomite, 0.5-10 parts of a graphene material, 0.5-1 part of nano-silver particles, 8-20 parts of a filler, 1.5-6 parts of anauxiliary agent, 13-15 parts of nano-silver cooper-supported POSS-based resin and 16-25 parts of water. The prepared graphene-modified antibacterial anticorrosive paint can solve practical problems inthe fields of ship, marine equipment, granary, etc. which have antibacterial and anticorrosive requirements. The product has good economic benefit, and energy materials are saved. The product has excellent adhesion and good wear resistance in the aspects of steel structures, metal plates, etc., and can be resistant to high and low temperature, high salinity and bacterial corrosion to achieve theantibacterial and anticorrosive effect.

Description

technical field [0001] The invention relates to the field of antibacterial and anticorrosion coating products, in particular to a graphene-modified antibacterial and anticorrosion coating. Background technique [0002] The annual economic loss caused by corrosion in the world accounts for about 4% to 5% of GDP, of which marine corrosion accounts for 1 / 3, which hinders the development of marine economy. On average, large ships need to be docked for antibacterial and anticorrosive coating every 5 years It consumes a lot of anti-corrosion and antibacterial materials, which also delays the normal operation of ships, as do other marine facilities; there are also granaries closely related to our lives, most of which have special metal plates, pipes, It is composed of materials such as concrete structure, and has strict requirements for antibacterial and anti-corrosion. [0003] At present, many antibacterial and anticorrosive materials with excellent performance on the market con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/14C09D5/10C09D7/61
Inventor 陈智锋江克平杨洁
Owner ZHEJIANG SCI-TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap