Electron beam cured high-wear-resistant scratch-resistant white coating and preparation method and construction method thereof

A technology of electron beam curing and high wear resistance, applied in the field of coatings, it can solve the problems of poor coating adhesion, insufficient curing, residual photoinitiator, etc., and achieve excellent hiding power, good wear resistance, and excellent scratch resistance. Effect

Active Publication Date: 2019-06-18
中山易必固电子束科技有限公司
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The white paint in the prior art mostly adopts ultraviolet light curing method. If the concentration of color paste in the paint is relatively high, especially when the coating is thick, it is difficult for ultraviolet light to penetrate the bottom, resulting in insufficient curing, and It will also lead to poor adhesion between coatings; and in the case of low concentration of color paste, UV curing is used, although it can be cured relatively completely, but the covering power is not enough
And to achieve good hiding power, the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electron beam cured high-wear-resistant scratch-resistant white coating and preparation method and construction method thereof
  • Electron beam cured high-wear-resistant scratch-resistant white coating and preparation method and construction method thereof
  • Electron beam cured high-wear-resistant scratch-resistant white coating and preparation method and construction method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0040] Example 1.

[0041] An electron beam cured white paint with high abrasion resistance and scratch resistance of this embodiment includes the following components by weight: 600.0g white paste, hexafunctional urethane acrylate UX-5400W 150.0g, trimethylolpropane triacrylic acid Ester 174.0g, dipentaerythritol hexaacrylate 50.0g, dispersant BYK163 5.0g, polyether modified dimethylsiloxane BYKUV351020.0g, defoamer BYK055 1.0g.

[0042] Among them, the white paste includes the following raw materials in terms of mass percentage: 60% titanium dioxide, 6342 15% modified polyester acrylate, 15% trimethylolpropane triacrylate, 6% hexanediol diacrylate, dispersant BYK163 4%.

[0043] Among them, the titanium dioxide is rutile titanium dioxide; in this embodiment, the crystal grain size of rutile titanium dioxide is 0.3 μm and the specific gravity is 4.0 g / cm 3 .

[0044] The above-mentioned preparation method of electron beam curing high abrasion and scratch resistance white paint inclu...

Example Embodiment

[0048] Example 2.

[0049] An electron beam cured white paint with high abrasion resistance and scratch resistance of this embodiment includes the following components by weight: white paste 620.0g, hexafunctional urethane acrylate UX-5400W 160.0g, trimethylolpropane triacrylic acid 154.0g of ester, 40.0g of dipentaerythritol hexaacrylate, 5.0g of dispersant BYK163, polyether modified dimethylsiloxane BYKUV351020.0g, and defoamer BYK055 1.0g.

[0050] Among them, the white paste includes the following raw materials in terms of mass percentage: 50% titanium dioxide, 6342 20% modified polyester acrylate, 20% trimethylolpropane triacrylate, 8% hexanediol diacrylate, dispersant BYK163 2%.

[0051] Among them, the titanium dioxide is rutile titanium dioxide; in this embodiment, the crystal size of rutile titanium dioxide is 0.2 μm, and the specific gravity is 3.0 g / cm 3 .

[0052] The above-mentioned preparation method of electron beam curing high abrasion and scratch resistance white pai...

Example Embodiment

[0056] Example 3.

[0057] An electron beam cured white paint with high abrasion resistance and scratch resistance of this embodiment includes the following components by weight: 650.0 g of white paste, hexafunctional urethane acrylate UX-5400W 130.0 g, trimethylolpropane triacrylic acid 149.0g of ester, 45.0g of dipentaerythritol hexaacrylate, 5.0g of dispersant BYK163, polyether modified dimethylsiloxane BYKUV351020.0g, and defoamer BYK055 1.0g.

[0058] Among them, the white paste includes the following raw materials in terms of mass percentage: 70% titanium dioxide, 6342 10% modified polyester acrylate, 10% trimethylolpropane triacrylate, 5% hexanediol diacrylate, dispersant BYK163 5%.

[0059] Among them, the titanium dioxide is rutile titanium dioxide; in this embodiment, the crystal grain size of rutile titanium dioxide is 0.4 μm and the specific gravity is 5.0 g / cm 3 .

[0060] The above-mentioned preparation method of electron beam curing high abrasion and scratch resistance...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of coatings, in particular to an electron beam cured high-wear-resistant scratch-resistant white coating and a preparation method and a construction methodthereof. The electron beam cured high-wear-resistant scratch-resistant white coating comprises white slurry, urethane acrylate with six functional groups, trimethylolpropane triacrylate, dipentaerythritol hexaacrylate, a dispersing agent, polyether modified dimethyl siloxane and a defoaming agent. The preparation method of the electron beam cured high-wear-resistant scratch-resistant white coating comprises the following steps: first step, preparing white slurry; and second step, preparing the white coating. The electron beam cured high-wear-resistant scratch-resistant white coating has the characteristics of being high in color paste concentration, excellent in hiding power, capable of avoiding the fact that a white primer coats for many times and is combined to a white finish paint or varnish to achieve a good hiding power effect, capable of enabling a cured white coating layer to be better in yellowing property, high in hardness, wear-resistant, scratch-resistant, good in yellowingproperty, good in adhesive force, good in leveling property and the like.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an electron beam-cured white coating with high wear resistance and scratch resistance, as well as a preparation method and a construction method thereof. Background technique [0002] The white paint in the prior art mostly adopts ultraviolet light curing method. If the concentration of color paste in the paint is relatively high, especially when the coating is thick, it is difficult for ultraviolet light to penetrate the bottom, resulting in insufficient curing, and It will also lead to poor adhesion between coatings; and in the case of low concentration of color paste, UV curing is used. Although it can be cured relatively completely, the hiding power is not enough. And to achieve good hiding power, the existing technology is to use multiple coatings of white primer combined with white topcoat (the proportion of titanium dioxide in the topcoat is low) or varnish to achieve goo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/14C09D7/61C09D7/65B05D3/06B05D7/24
Inventor 梁立喜陈立任杰李林梁铭通陈卓成
Owner 中山易必固电子束科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap